Steel sheet for hot stamping use, method of production of same, and method of production of high strength part

Patent metadata

Field	Value
Publication number	US-10344360-B2
Application number	US-201114003881-A
Country	US
Kind code	B2
Filing date	Mar 9, 2011
Priority date	Mar 9, 2011
Publication date	Jul 9, 2019
Grant date	Jul 9, 2019

Abstract

Specifically, it provides steel sheet for hot stamping use which is comprised of chemical ingredients which contain, by mass %, C: 0.05 to 0.40%, Si: 0.02% or less, Mn: 0.1 to 3%, S: 0.02% or less, P: 0.03% or less, Al: 0.005% or less, Ti: 0.01% or less, N: 0.01% or less, one or both of Cr and Mo in a total of 0.005 to 1%, and O: 0.003 to 0.03% and which have a balance of Fe and unavoidable impurities and which contains average diameter 0.1 to 15 μm Fe—Mn-based composite oxide particles dispersed in the steel sheet or furthermore has crushed voids around the composite oxide particles, a method of production of the same, and a method of production of a hot stamped high strength part.

First claim

The invention claimed is:

1. A steel sheet for hot stamping use which is comprised of chemical ingredients which contain, by mass %,
C: 0.05 to 0.40%,
Si: 0.001 to 0.02%,
Mn: 0.1 to 3%,
Al: 0.0002 to 0.005%,
Ti: 0.0005 to 0.01%,
O: 0.003 to 0.03%,
N: 0.006% or less,
one or more of Cr and Mo in a total of 0.005 to 2%, and
a balance of Fe and unavoidable impurities,
provided that said steel sheet contains no W,
wherein the steel sheet contains average diameter 0.1 to 15 μm Fe—Mn-based composite oxide particles dispersed in the steel sheet.

2. The steel sheet for hot stamping use as set forth in claim 1 which further contains, by mass %, the ingredients which are included in one or more groups among the three groups of (a) to (c):
(a) B: 0.0005 to 0.01%;
(b) one or more of Nb, V, and Co in a total of 0.005 to 1%; and
(c) one or more of Ni and Cu in a total of 0.005 to 2%.

3. The steel sheet for hot stamping use as set forth in claim 1 or 2 , wherein there are voids around said composite oxide particles.

4. The steel sheet for hot stamping use as set forth in claim 1 or 2 , wherein the voids around said composite oxide particles have average sizes of 10 to 100% of the average size of said composite oxide particles.

5. The steel sheet for hot stamping use as set forth in claim 1 or 2 , wherein the steel sheet is plated by any of aluminum plating, zinc-aluminum plating, and zinc plating.

Assignees

• Kusumi Kazuhisa
• Ogawa Yuji
• Abe Masayuki
• Murakami Hidekuni
• Takeda Kengo
• Maki Jun
• Nippon Steel & Sumitomo Metal Corp

Inventors

• Kusumi Kazuhisa
• Ogawa Yuji
• Abe Masayuki
• Murakami Hidekuni
• Takeda Kengo
• Maki Jun

Classifications

• C21D8/00

  Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment (hardening articles or materials formed by forging or rolling with no further heating beyond that required for the formation C21D1/02) · CPC title

• C22C38/22

  with molybdenum or tungsten · CPC title

• C21D8/0236

  Cold rolling · CPC title

• C22C38/04

  containing manganese · CPC title

• B21B1/22

  for rolling {plates, strips,} bands or sheets of indefinite length (B21B1/42 takes precedence) · CPC title