Foam compositions and uses thereof

Patent metadata

Field	Value
Publication number	US-10344150-B2
Application number	US-201715833276-A
Country	US
Kind code	B2
Filing date	Dec 6, 2017
Priority date	Mar 15, 2016
Publication date	Jul 9, 2019
Grant date	Jul 9, 2019

Abstract

Components for articles of footwear and athletic equipment are provided including a foam. A variety of foams and foam components and compositions for forming the foams are provided. In some aspects, the foams and components including the foams can have exceptionally high energy return while also having improved durability and softness. In particular, midsoles including the foams are provided for use in an article of footwear. Methods of making the compositions and foams are provided, as well as methods of making an article of footwear including one of the foam components. In some aspects, the foams and foam components can be made by injection molding or injection molding followed by compression molding.

First claim

I claim:

1. An article of footwear comprising a component, wherein the component is made by a process comprising crosslinking and foaming a first composition, wherein the first composition comprises:
a partially hydrogenated thermoplastic elastomeric block copolymer, the partially hydrogenated thermoplastic elastomeric block copolymer comprising:
one or more A blocks comprising aromatic repeat units,
one or more B blocks comprising aliphatic repeat units, and
one or more first ethylenically unsaturated groups present on one or both of the aromatic repeat units and the aliphatic repeat units;

an olefinic block copolymer, wherein the olefinic block copolymer is a copolymer of a first alpha-olefin and a second alpha-olefin different from the first alpha-olefin, and wherein the olefinic block copolymer comprising one or more second ethylenically unsaturated groups;
an alpha-olefin linking polymer, wherein the alpha-olefin linking polymer comprises one or more aliphatic sidechains; and
an ethylene-vinyl acetate copolymer;
wherein a sum of a ratio I, II, III, IV, V and VI is from about 5.0 to about 16.0;
wherein the ratio I is a ratio of a total parts by weight of the olefinic block copolymer present in the composition to a total parts by weight of the partially hydrogenated thermoplastic elastomeric block copolymer present in the composition;
wherein the ratio II is a ratio of a total parts by weight of the alpha-olefin linking polymers present in the composition to a total parts by weight of the partially hydrogenated thermoplastic elastomeric block copolymer present in the composition;
wherein the ratio III is ratio of a total parts by weight of the ethylene-vinyl acetate copolymers present in the composition to a total parts by weight of the partially hydrogenated thermoplastic elastomeric block copolymer present in the composition;
wherein the ratio IV is a ratio of the total parts by weight of the alpha-olefin linking polymers present in the composition to a total parts by weight of the olefinic block copolymer present in the composition,
wherein the ratio V is a ratio of the total parts by weight of the one or more ethylene-vinyl acetate copolymers present in the composition to a total parts by weight of the olefinic block copolymer present in the composition, and
wherein the ratio VI is a ratio of the total parts by weight of the ethylene-vinyl acetate copolymer to a total parts by weight of the alpha-olefin linking polymer.

2. The article of footwear according to claim 1 , wherein the sum of ratio I, II, III, IV, V, and VI is from about 14.00 to about 16.00.

3. The article of footwear according to claim 1 , wherein the component is a midsole.

4. The article of footwear according to claim 1 , wherein the first composition comprises about 5 parts by weight to about 20 parts by weight of the partially hydrogenated thermoplastic elastomeric block copolymer based upon an entire weight of the resin components,
wherein the entire weight of the resin components, based upon a total parts by weight of the polymers in the first composition, is about 40 parts by weight to about 86 parts by weight.

5. The article of footwear according to claim 1 , wherein the first composition comprises about 5 parts by weight to about 20 parts by weight of the olefinic block copolymer by weight based upon an entire weight of the resin components,
wherein the entire weight of the resin components, based upon a total parts by weight of the polymers in the first composition, is about 40 parts by weight to about 86 parts by weight.

6. The article of footwear according to claim 1 , wherein the first composition comprises about 15 parts by weight to about 35 parts by weight of the alpha-olefin linking polymer based upon an entire weight of the resin components,
wherein the entire weight of the resin components, based upon a total parts by weight of the polymers in the first composition, is about 40 parts by weight to about 86 parts by weight.

7. The article of footwear according to claim 1 , wherein the first composition further comprises one or both of a free-radical initiator and a chemical blowing agent.

8. The article of footwear according to claim 7 , wherein the first composition comprises the free-radical initiator, and
wherein the free-radical initiator is selected from the group consisting of dicumyl peroxide; n-butyl-4,4-di(t-butylperoxy) valerate; 1,1-di(t-butylperoxy)3,3,5-trimethylcyclohexane; 2,5-dimethyl-2,5-di(t-butylperoxy) hexane; di-t-butyl peroxide; di-t-amyl peroxide; t-butyl peroxide; t-butyl cumyl peroxide; 2,5-dimethyl-2,5-di(tbutylperoxy)hexyne-3; di(2-t-butyl-peroxyisopropyl)benzene; dilauroyl peroxide; dibenzoyl peroxide; t-butyl hydroperoxide; and a combination thereof.

9. The article of footwear according to claim 7 , wherein the first composition comprises a chemical blowing agent, and
wherein the chemical blowing agent is selected from the group consisting of a carbonate, bicarbonate, carboxylic acid, azo compound, isocyanate, persulfate, peroxide, and a combination thereof.

10. The article of footwear according to claim 1 , wherein the component has an energy return of about 60% to about 85%.

11. The article of footwear according to claim 1 , wherein the ratio I is from about 0.65 to about 7.00.

12. The article of footwear according to claim 1 , wherein the olefinic block copolymer does not comprise a cycloalkyl olefin.

13. The article of footwear according to claim 1 , wherein the first composition comprises a first alpha-olefin linking polymer and a second alpha-olefin linking polymer,
wherein the first alpha-olefin linking polymer and the second alpha-olefin linking polymer are copolymers of ethylene and 1-butene, each having a different ratio of ethylene to 1-butene monomer content in the copolymer.

14. The article of footwear according to claim 1 , wherein the ethylene-vinyl acetate copolymer having a vinyl acetate content of about 10% to about 45% by weight based upon the weight of the ethylene-vinyl acetate copolymer.

15. The article of footwear according to claim 1 , wherein the ratio IV is from about 1.00 to 10.00, and
wherein the ratio V is from about 2.00 to 10.00.

16. The article of footwear according to claim 15 , wherein the ratio V is from about 2.50 to 4.50.

17. The article of footwear according to claim 1 , wherein the first composition comprises about 10 parts by weight to about 50 parts by weight of the alpha-olefin linking polymer based upon an entire weight of the resin components,
wherein the entire weight of the resin components, based upon a total parts by weight of the polymers in the first composition, is about 40 parts by weight to about 86 parts by weight.

18. The article of footwear according to claim 1 , wherein the first composition comprises about 30 parts by weight to about 60 parts by weight of the ethylene-vinyl acetate copolymer based upon an entire weight of the resin components,
wherein the entire weight of the resin components, based upon a total parts by weight of the polymers in the first composition, is about 40 parts by weight to about 86 parts by weight.

19. The article of footwear according to claim 1 , wherein the component has an energy return of about 70% to about 85%.

Assignees

• Nike Inc

Inventors

• Baghdadi Hossein A

Classifications

• C08J9/06

  by a chemical blowing agent · CPC title

• C08J2331/04

  Homopolymers or copolymers of vinyl acetate · CPC title

• C08J9/0061 Primary

  characterized by the use of several polymeric components · CPC title

• A43B13/188

  Differential cushioning regions · CPC title

• C08J2323/08

  Copolymers of ethene (C08J2323/16 takes precedence) · CPC title