Fused porogen process for acoustic septa fabrication

Patent metadata

Field	Value
Publication number	US-10336433-B2
Application number	US-201514641537-A
Country	US
Kind code	B2
Filing date	Mar 9, 2015
Priority date	Mar 9, 2015
Publication date	Jul 2, 2019
Grant date	Jul 2, 2019

Abstract

An example method for manufacturing a multicellular structure for acoustic damping is described that includes applying a porogen material to a solid support, inserting a multicellular frame into the solid support and through the porogen material so as to fill cells of the multicellular frame with the porogen material, fusing the porogen material, removing the multicellular frame from the solid support, and the multicellular frame contains a suspended fused porogen network attached to walls of the cells of the multicellular frame. The method also includes applying a solution to the suspended fused porogen network in the cells of the multicellular frame to percolate the suspended fused porogen network, curing the solution, and removing the suspended fused porogen network from the multicellular frame resulting in porous septum membranes of the cured solution in cells of the multicellular frame.

First claim

What is claimed is:

1. A method for forming porous membranes within a multicellular frame for manufacturing a multicellular structure for acoustic damping in an aircraft, the method comprising:
templating the multicellular frame with a fused porogen network so as to create a multicellular frame-porogen assembly;
applying a polymer into the fused porogen network of the multicellular frame-porogen assembly; and
removing the fused porogen network from the multicellular frame-porogen assembly resulting in polymeric septum membranes within the multicellular frame, and wherein the polymeric septum membranes are porous membranes having a thickness of about 1.0 mm to about 5.0 mm and wherein the porous membranes comprise a substantially continuous matrix having pores with a size less than about 15% of the thickness of the polymeric septum membranes.

2. The method of claim 1 , wherein applying the polymer into the fused porogen network of the multicellular frame-porogen assembly comprises:
applying a solution of a polymer precursor material and solvent to the fused porogen network in cells of the multicellular frame to percolate the fused porogen network; and
curing the polymer precursor solution.

3. The method of claim 1 , wherein templating the multicellular frame with the fused porogen network comprises:
applying a porogen material to a solid support;
inserting the multicellular frame into the solid support and through the porogen material so as to fill cells of the multicellular frame with the porogen material;
fusing the porogen material; and
removing the multicellular frame-porogen assembly from the solid support, wherein the multicellular frame-porogen assembly contains a suspended fused porogen network attached to walls of the cells of the multicellular frame.

4. The method of claim 3 , wherein the porogen material is selected from a type of material consisting of a salt, a sugar, an organic solid, and a polymer particle.

5. The method of claim 3 , wherein the porogen material is selected from a type of material consisting of a cubic particle, a spherical particle, an amorphous particle, a rod particle, a whisker-like particle, a leachable particle, and a non-removable polymer particle.

6. The method of claim 3 , wherein the solid support includes a convex surface, and the method comprises:
removing the multicellular frame from the solid support resulting in a suspended convex fused porogen network; and
fabricating convex porous septum membranes.

7. The method of claim 3 , wherein fusing the porogen comprises:
applying a humidity atmosphere for a given amount of time; and
applying a thermal atmosphere for a given amount of time to form the suspended fused porogen network that attaches to the walls of the cells of the multicellular frame.

8. The method of claim 3 , wherein fusing the porogen material comprises a combination of a chemical and a thermal treatment.

9. The method of claim 1 , wherein applying the polymer into the fused porogen network comprises:
immersing the multicellular frame-porogen assembly into a polymer resin solution to coat the fused porogen network with the polymer resin solution.

10. The method of claim 9 , wherein the solution is selected from the group consisting of a polymer resin not diluted with a solvent, and a polymer resin diluted with a solvent.

11. The method of claim 9 , further comprising
applying a thermal atmosphere for a given amount of time to set a microstructure of the solution and to cure the solution.

12. The method of claim 11 , wherein the microstructure of the solution is configured to create one or more of pressure barriers, flow restrictors, and resonant cavities for controlling transmission of acoustic noise.

13. The method of claim 1 , wherein removing the suspended fused porogen network from the multicellular frame-porogen assembly comprises:
placing the multicellular frame into a water bath; and
drying the porous septum membranes in the cells of the multicellular frame.

14. The method of claim 1 , wherein the polymeric septum membranes are first polymeric septum membranes within the multicellular frame, and the method further comprises:
templating the multicellular frame with a second fused porogen network;
applying a second polymer into the second fused porogen network; and
removing the second fused porogen network resulting in second polymeric septum membranes within the multicellular frame.

15. A method for manufacturing a multicellular structure for acoustic damping in an aircraft, the method comprising:
applying a porogen material to a solid support;
inserting a multicellular frame into the solid support and through the porogen material so as to fill cells of the multicellular frame with the porogen material;
fusing the porogen material;
removing the multicellular frame from the solid support, wherein the multicellular frame contains a suspended fused porogen network attached to walls of the cells of the multicellular frame;
applying a solution to the suspended fused porogen network in the cells of the multicellular frame to percolate the suspended fused porogen network;
curing the solution; and
removing the suspended fused porogen network from the multicellular frame resulting in porous septum membranes of the cured solution in cells of the multicellular frame, and wherein the porous septum membranes having a thickness of about 1.0 mm to about 5.0 mm and wherein the porous septum membranes comprise a substantially continuous matrix having pores with a size less than about 15% of the thickness of the porous septum membranes.

16. The method of claim 15 , wherein the multicellular frame includes a honeycomb frame comprised of one of aluminum, titanium, carbon composite, aramid, or fiberglass.

Assignees

• Boeing Co

Inventors

• Stache Erin E
• Herrera Eric
• Cumberland Larken E
• Alam Shahriar
• Roper Christopher S
• Mcknight Geoffrey

Classifications

• G10K11/168

  Plural layers of different materials, e.g. sandwiches · CPC title

• E04C2/365

  by honeycomb structures · CPC title

• B64C1/40 Primary

  Sound or heat insulation {, e.g. using insulation blankets} · CPC title

• G10K11/172

  using resonance effects · CPC title

• B32B3/12

  characterised by a layer of regularly- arranged cells, e.g. a honeycomb structure · CPC title