Abstract

Processes for forming cosmetically appealing edges on laminated fabric structures are described. The methods involve a laser cutting process that includes in-process melting of polymer material within the laminated fabric so as to coat fibers of the laminated fabric. The resultant cut laminated fabric has a cosmetic edge that has no exposed fibers. The laser cutting and melting can be performed in a single laser cutting operation, making it well suited for integration into manufacturing product lines.

First claim

What is claimed is:

1. A method of forming a cosmetic edge on a laminated fabric, the laminated fabric including a polymer layer and an attached fabric layer, the fabric layer including fibers, the method comprising:
cutting an edge of the laminated fabric by directing a laser beam at the polymer layer and the attached fabric layer, wherein during the cutting:
the laser beam melts a portion of the polymer layer forming a pool of melted polymer material, wherein the pool of melted polymer material coats the fibers along the edge so as to prevent exposure of the fibers along the edge.

2. The method of claim 1 , wherein cutting the edge comprises using a pulsed laser beam that impinges the laminated fabric a plurality of times.

3. The method of claim 1 , wherein cutting the edge comprises scanning the laser beam over the laminated fabric a plurality of times.

4. The method of claim 1 , wherein cutting the edge and melting the portion of the polymer layer occurs using a single laser operation.

5. The method of claim 1 , wherein the laminated fabric includes a plurality of polymer layers and wherein the fabric layer is positioned between at least two of the plurality of polymer layers.

6. The method of claim 1 , wherein the polymer layer includes at least one of polyurethane, epoxy, acrylic, polyester and a polyimide.

7. The method of claim 1 , wherein the fibers include at least one of polymer-based fibers, carbon fibers and glass fibers.

8. The method of claim 1 , wherein the cut edge is a beveled edge.

9. A method of cutting a laminated fabric, the laminated fabric including a polymer layer and a fabric layer, the fabric layer having fibers, the method comprising:
impinging a laser beam on the laminated fabric such that the laser beam cuts the laminated fabric, wherein the laser beam locally heats the polymer layer forming a pool of melted material that completely coats a cut edge of the fabric layer; and
repeating the impinging until the laser beam cuts through a width of the laminated fabric such that a final cut edge of the laminated fabric has a coating that completely covers the fabric layer and the fibers along the final cut edge.

10. The method of claim 9 , wherein repeating the impinging comprises using a pulsed laser beam that impinges the laminated fabric a plurality of times.

11. The method of claim 9 , wherein repeating the impinging comprises scanning the laser beam over the laminated fabric a plurality of times.

12. The method of claim 9 , wherein repeating the impinging comprises stepwise cutting the laminated fabric and melting the polymer layer in a single laser operation.

13. The method of claim 9 , wherein the pool of melted material cools and at least partially hardens prior to repeating the impinging.

Assignees

• Apple Inc

Inventors

• Lancaster-Larocque Simon Regis Louis
• Nielson Bradley J
• Kononiuk Jacob S

Classifications

• D06M23/18

  for the chemical treatment of borders of fabrics or knittings; for the thermal or chemical fixation of cuttings, seams or fibre ends · CPC title

• B32B27/36

  comprising polyesters · CPC title

• B32B27/308

  comprising acrylic (co)polymers · CPC title

• B32B7/12

  using interposed adhesives or interposed materials with bonding properties · CPC title

• B32B2260/021

  Fibrous or filamentary layer · CPC title