Resin composition and multilayered structure using same

Patent metadata

Field	Value
Publication number	US-10329411-B2
Application number	US-201113637448-A
Country	US
Kind code	B2
Filing date	Mar 25, 2011
Priority date	Mar 26, 2010
Publication date	Jun 25, 2019
Grant date	Jun 25, 2019

Abstract

A resin composition, containing: (A) polyolefin; (B) a saponified ethylene-vinyl acetate copolymer having an ethylene content of from 20 to 65 mol % and a degree of saponification of vinyl acetate units of 96% or more; (C) a saponified ethylene-vinyl acetate copolymer having an ethylene content of from 68 to 98 mol % and a degree of saponification of vinyl acetate units of 20% or more; (D) a random copolymer consisting of ethylene and vinyl acetate; (E) a pigment comprising titanium oxide particles comprising a surface coated with a compound of a metal other than titanium or a silicon compound; and (I) a lubricant; wherein a mass ratio (AB) is from 3 to 99.5, a mass ratio (B/C) is from 1 to 100, a mass ratio of (D/C) is from 0.1 to 15, a mass ratio (E/C) is from 0.04 to 50, and a content of (C) is from 0.01 to 2.4 parts, particularly 0.33 to 1.5 parts, by mass based on 100 parts by mass of (A) and (B). A molded product, in particular a multilayered structure, obtained by melt molding the resin composition has good dispersibility of the pigment, and improved uneven coloration.

First claim

The invention claimed is:

1. A resin composition, comprising:
(A) a polyolefin;
(B) a saponified ethylene-vinyl acetate copolymer comprising an ethylene content of from 20 to 65 mol % and having a degree of saponification of vinyl acetate units of 96% or more;
(C) a saponified ethylene-vinyl acetate copolymer comprising an ethylene content of from 68 to 98 mol % and having a degree of saponification of vinyl acetate units of 20% or more;
(D) a random copolymer consisting of ethylene and vinyl acetate;
(E) a pigment; and
(I) a lubricant,

wherein:
a mass ratio of the polyolefin (A) and the saponified ethylene-vinyl acetate copolymer (B), (A/B), is from 3 to 99.5;
a mass ratio of the saponified ethylene-vinyl acetate copolymer (B) and the saponified ethylene-vinyl acetate copolymer (C), (B/C), is from 2 to 18;
a mass ratio of the random copolymer consisting of ethylene and vinyl acetate (D) and the saponified ethylene-vinyl acetate copolymer (C), (D/C), is from 0.1 to 15;
a mass ratio of the pigment (E) and the saponified ethylene-vinyl acetate copolymer (C), (E/C), is from 0.1 to 1.2;
a content of the saponified ethylene-vinyl acetate copolymer (C) is from 0.33 to 1.5 parts by mass, based on 100 parts by mass of a total amount of the polyolefin (A) and the saponified ethylene-vinyl acetate copolymer (B);
a content of the lubricant (1) is from 0,00001 to 1 parts by mass, based on 100 parts by mass of the total amount of (A) and (B);
the pigment (E) comprises titanium oxide particles comprising a surface coated with a compound of a metal other than titanium or a silicon compound; and
the titanium oxide particles have an average particle diameter of from 0.01 to 0.4 μm.

2. The resin composition of claim 1 , further comprising:
(H) a conjugated polyene compound,
wherein a content of the conjugated polyene compound (H) is from 0.000001 to 1 parts by mass, based on 100 parts by mass of the total amount of (A) and (B).

3. The resin composition of claim 1 ,
wherein the content of the lubricant (I) is from 0.00005 to 11.5 parts by mass, based on 100 parts by mass of the total amount of (A) and (B).

4. The resin composition of claim 1 , further comprising:
a metal salt (F) of fatty acid,
wherein a mass ratio of the metal salt (F) of fatty acid and the pigment (E), (F/E), is from 0.1 to 3.

5. The resin composition of claim 1 , wherein the pigment (E) comprises titanium oxide particles comprising a surface coated with at least one of an oxide, sulfide, nitride, carbide, boride, chloride, carbonate, hydroxide, sulfate, nitrate, phosphate, or carboxy late of aluminum, silicon, zirconium, zinc, magnesium, or calcium.

6. The resin composition of claim 5 , wherein the titanium oxide particles are coated with alumina (Al 2 O 3 ), silica (SiO 2 ), or both.

7. The resin composition of claim 6 , wherein the titanium oxide particles are coated with both alumina (Al 2 O 3 ) and silica (SiO 2 ).

8. The resin composition of claim 7 , wherein the pigment (E) comprises titanium oxide particles coated with a mixture of alumina (Al 2 O 3 ) and silica (SiO 2 ).

9. The resin composition of claim 1 , wherein the titanium oxide particles have an average particle diameter of from 0.1 to 0.3 μm.

10. The resin composition of claim 1 , wherein the titanium oxide particles have an average particle diameter of from 0.15 to 0.25 μm.

Assignees

• Igarashi Takeyuki
• Haneda Yasuhiko
• Kitamura Masahiro
• Tai Shinji
• Kuraray Co

Inventors

• Igarashi Takeyuki
• Haneda Yasuhiko
• Kitamura Masahiro
• Tai Shinji

Classifications

• C08K2003/2241

  Titanium dioxide · CPC title

• B32B27/06

  as the main or only constituent of a layer, {which is} next to another layer of {the same or of} a {different material (next to a layer of a particular substance B32B9/045; next to a bituminous or tarry layer B32B11/046; next to a water setting substance layer B32B13/12; next to a metal layer B32B15/08; next to a glass layer B32B17/10; next to a layer formed of natural mineral fibres or particles B32B19/045; next to a wood layer B32B21/08; next to a cellulosic plastic layer B32B23/08; next to a natural or synthetic rubber layer B32B25/08)} · CPC title

• B32B2439/80

  Medical packaging · CPC title

• B32B2439/70

  Food packaging · CPC title

• C08L23/0861

  Saponified copolymers, e.g. ethylene vinyl alcohol copolymers · CPC title