Method for preparing a particulate cathode material

Patent metadata

Field	Value
Publication number	US-10329154-B2
Application number	US-201414567220-A
Country	US
Kind code	B2
Filing date	Dec 11, 2014
Priority date	Dec 7, 2006
Publication date	Jun 25, 2019
Grant date	Jun 25, 2019

Abstract

A method for preparing an electrode material, said material comprising complex oxide particles having a non-powdery conductive carbon deposit on at least part of their surface, said method comprising: grinding into nanometer size complex oxide particles or particles of complex oxide precursors, wherein the grinding is performed in a bead mill on particles dispersed in a carrier solvent, adding an organic carbon precursor to the oxide particles or oxide precursor particles before, during or after said grinding, and pyrolysing the mixture thus obtained, selecting the size of the particles to grind, the size of the beads used to grind, and the size of the resulting particles such that: 0.004<MS(SP)/MS(B)<0.12 and 0.0025<MS(FP)/MS(SP)<0.25, wherein MS(SP) represents the mean size diameter of the particles before grinding, MS(FP) represents the mean size diameter of the particles after grinding, and MS(B) is the mean size diameter of the beads.

First claim

The invention claimed is:

1. A method for improving the electrochemical performance of previously synthesized lithium metal phosphate particles, said method comprising:
grinding said previously synthesized lithium metal phosphate particles into a particle size of from 5 nm to less than 1 micron, wherein the grinding is performed in a bead mill on particles dispersed in a carrier solvent, and such that:
0.004<MS(SP)/MS(B)<0.12,
0.0025<MS(FP)/MS(SP)<0.25

wherein MS(SP) represents the mean size diameter of the particles before grinding, MS(FP) represents the mean size diameter of the particles after grinding, and MS(B) is the mean size diameter of the beads;
adding an organic carbon precursor to the particles before, during or after said grinding; and
performing a pyrolysis on the organic carbon precursor and ground particles to obtain a non-powdery conductive carbon deposit on at least part of the surface of the particles,

wherein said organic carbon precursor is a monomer, said method comprising a further step performed after said grinding and before said pyrolysis, said further step being polymerizing or cross-linking the organic carbon precursor.

2. The method of claim 1 , wherein the carrier solvent is water or isopropanol.

3. The method of claim 1 , said method comprising a further step performed before said pyrolysis, said further step being aggregating the organic carbon precursor and the ground particles.

4. The method of claim 3 , wherein said aggregating is performed by flocculating, by spray drying, or by charge effect.

5. The method of claim 1 , wherein the mean size diameter of the beads is from 100 μm to 500 μm.

6. The method of claim 1 , said method comprising a further step performed before said grinding, said further step being adding an organic stabilizing agent to said previously synthesized lithium metal phosphate particles.

7. The method of claim 6 , wherein the organic stabilizing agent is selected from the group consisting of organic electrostatic or electrosteric stabilizers, surfactants, dispersant agents, self-adsorbing agents, and encapsulating agents.

8. The method of claim 6 , wherein the organic stabilizing agent is a conductive carbon precursor.

9. The method of claim 1 , wherein the particles before said grinding have a size of from 1 μm to 50 μm.

10. The method of claim 1 , wherein the previously synthesized lithium metal phosphate particles have an olivine structure, and wherein:
lithium is optionally partly replaced with not more than 10 atomic % Na or K;
the metal is Fe II or Mn II and is optionally partly replaced with not more than 50 atomic % of at least one metal selected from the group consisting of Mn, Fe, Ni and Co, and optionally replaced with not more than 10 atomic % of at least one aliovalent or isovalent metal different from Fe, Mn, Ni or Co; and
phosphate is optionally partly replaced with not more than 10 mol % of at least one group selected from SO and SiO 4.

11. The method of claim 10 , wherein the aliovalent or isovalent metal different from Fe, Mn, Ni or Co is at least one metal selected from the group consisting Mg, Mo, Nb, Al, Ta, Ge, La, Y, Yb, Sm, Ce, Hf, Cr, Zr, Bi, Zn, Ca and W.

12. The method of claim 1 , wherein the previously synthesized lithium metal phosphate particles have the formula LiFe 1-x Mn x PO 4 , wherein 0 ≤×≤0.5, or LiMnPO 4 .

Assignees

• Johnson Matthey Plc

Inventors

• Liang Guoxian
• Charest Patrick
• Gauthier Michel
• Guerfi Abdelbast
• Michot Christophe
• Zaghib Karim

Classifications

• B82Y30/00

  Nanotechnology for materials or surface science, e.g. nanocomposites · CPC title

• C01P2002/32

  spinel-type (AB2O4) · CPC title

• H01M4/625

  Carbon or graphite · CPC title

• H01M4/136 Primary

  Electrodes based on inorganic compounds other than oxides or hydroxides, e.g. sulfides, selenides, tellurides, halogenides or LiCoFy · CPC title

• C01P2004/04

  obtained by TEM, STEM, STM or AFM · CPC title