Ballistic and stab resistant composite

Patent metadata

Field	Value
Publication number	US-10323908-B2
Application number	US-201615091982-A
Country	US
Kind code	B2
Filing date	Apr 6, 2016
Priority date	May 8, 2015
Publication date	Jun 18, 2019
Grant date	Jun 18, 2019

Abstract

A flexible composite suitable for use in a knife, pick, bullet and fragment-resistant article comprising
(i) a first zone comprising fabric but no resin, the first first zone comprising from 10 to 90 percent of the total thickness of the composite, (ii) a third zone comprising an elastomeric or thermoplastic resin but no fabric, the third zone comprising from 0 to 50 percent of the total thickness of the composite and (iii) a second zone, located between the first and third zones, comprising fabric and an elastomeric or thermoplastic resin, the second zone comprising from 10 to 90 percent of the total thickness of the composite.

First claim

The invention claimed is:

1. A composite suitable for use in a knife, pick, bullet and fragment-resistant article comprising a polymeric fibrous fabric core section free of resin (first zone) and, located on at least one side of the core section, a polymeric fibrous fabric section impregnated with an elastomeric or thermoplastic resin (second zone)
wherein:
(i) the resin comprises from 5 to 79 percent of the volume fraction of the composite,
(ii) the resin fills up to 100 percent of a fiber-free volume of the second zone,
(iii) the first zone comprises from 10 to 90 percent of the total thickness of the composite,
(iv) the fibers of the first or second zones have a tenacity of at least 20 g/denier and a tensile modulus of at least 444 g/dtex, and
(v) the resin has an elongation to break of between 20 to 1200 percent.

2. The composite of claim 1 wherein the fabric of the first or second zones is woven, nonwoven, braided or knit.

3. The composite of claim 1 wherein the polymer of the fibers of the fabric of the first or second zones is aromatic polyamide, aromatic co-polyamide or polyethylene.

4. The composite of claim 1 wherein the thermoplastic resin is polyvinyl, polyolefin, polyamide, polyester, polyurethane, polyacrylonitrile or polysulfone.

5. The composite of claim 1 wherein the elastomer is rubber or silicone.

6. The composite of claim 2 wherein the nonwoven fabric is unidirectional, biaxial, multiaxial.

7. A composite suitable for use in a knife, pick, bullet and fragment-resistant article comprising
(i) a first zone comprising fabric but no resin, the first first zone comprising from 10 to 90 percent of the total thickness of the composite,
(ii) a third zone comprising an elastomeric or thermoplastic resin but no fabric, the third zone comprising from 0 to 50 percent of the total thickness of the composite and
(iii) a second zone comprising fabric and an elastomeric or thermoplastic resin, the second zone comprising from 10 to 90 percent of the total thickness of the composite wherein
(a) the fabric of the first and second zones is formed from polymeric yarns having a yarn tenacity of at least 20 g/denier and a yarn modulus of at least 444 g/dtex,
(b) the elastomeric or thermoplastic resin of the second or third zones has an elongation to break of between 20 to 1200 percent,
(c) the resin comprises from 5 to 79 percent of the volume fraction of the second zone, and
(d) the resin fills between 80 to 100 percent of a fiber-free volume of the second zone.

8. The composite of claim 7 wherein the fabric is woven, nonwoven or knit.

9. The composite of claim 7 wherein the polymer of the yarns of the fabric is aromatic polyamide, aromatic co-polyamide or polyethylene.

10. The composite of claim 7 wherein the thermoplastic resin is polyvinyl, polyolefin, polyamide, polyester, polyurethane, polyacrylonitrile or polysulfone.

11. The composite of claim 7 wherein the elastomer is rubber or silicone.

12. The composite of claim 8 wherein the nonwoven fabric is unidirectional, biaxial, multiaxial.

13. A protective article comprising at least one composite of claim 1 or claim 7 that is knife, pick, bullet and fragment-resistant.

14. The protective article of claim 13 wherein the article meets the requirements of NIJ 0101.04 level IIIA Revision A dated June 2001, of NIJ 0115.00 dated September 200 and of HOSDB publication No 39/07/C protection level KR1/SP1 E1 standards dated 2007.

15. The protective article of claim 13 wherein the article, when tested according to Test Method A, exhibits a flexural force no greater than 4000 N.

16. The composite of claim 7 , wherein the second zone is located between the first and third zones when the third zone comprises greater than 0 percent of the total thickness of the composite.

17. The composite of claim 7 , wherein the first zone is located between the second and third zones when the third zone comprises greater than 0 percent of the total thickness of the composite.

18. The composite of claim 7 , wherein the second zone covers the entire surface area of at least one side of the first zone.

19. The composite of claim 7 , wherein the third zone covers the entire surface area of at least one side of the first zone or the second zone.

Assignees

• Du Pont

Inventors

• Rozant Olivier
• Bader Yves
• Boogh Louis
• Pont Nicolas

Classifications

• C08J2300/26

  Elastomers · CPC title

• B32B27/12

  next to a fibrous or filamentary layer · CPC title

• B32B2262/0253

  Polyolefin fibres · CPC title

• B29C70/28

  Shaping operations therefor · CPC title

• B32B27/30

  comprising vinyl {(co)polymers; comprising acrylic (co)polymers} · CPC title