Preparation method of calcium carbonate with high purity from inorganic materials containing alkali metals or alkali earth metals

Patent metadata

Field	Value
Publication number	US-10322941-B2
Application number	US-201715435801-A
Country	US
Kind code	B2
Filing date	Feb 17, 2017
Priority date	Feb 19, 2016
Publication date	Jun 18, 2019
Grant date	Jun 18, 2019

Abstract

The present invention relates to a method and a process of preparing precipitated calcium carbonate of high purity by extracting calcium ion contained in an alkali ion-containing inorganic material such as mineral, steelmaking slag and waste concrete with the use of an acidic aqueous solution, separating other metal ions from the extracted solution, preparing an alkaline earth metal hydroxide using an alkaline aqueous solution and then contacting the same with carbon dioxide.

First claim

What is claimed is:

1. A method for preparing calcium carbonate from an alkali ion-comprising inorganic material, which comprises:
(1) a step of preparing hydrochloric acid solution, and a sodium hydroxide aqueous solution or a mixture of a sodium hydroxide aqueous solution and a potassium hydroxide aqueous solution;
(2) a step of producing a dissolving solution by extracting metal ions comprising a calcium ion from an alkali ion-comprising inorganic material using the hydrochloric acid solution;
(3) a step of removing an impurity from the dissolving solution by reacting the dissolving solution with the sodium hydroxide aqueous solution or the mixture of the sodium hydroxide aqueous solution and the potassium hydroxide aqueous solution such that the impurity is transformed into a metal hydroxide and the metal hydroxide is removed;
(4) a step of producing a slurry comprising calcium hydroxide by reacting an impurity-removed dissolving solution with the sodium hydroxide aqueous solution or the mixture of the sodium hydroxide aqueous solution and the potassium hydroxide aqueous solution; and
(5) a step of transforming the calcium hydroxide into a high-purity calcium carbonate by providing carbon dioxide to the slurry and separating the high-purity calcium carbonate.

2. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 1 , wherein, in the step (1), the hydrochloric acid solution, and the sodium hydroxide aqueous solution or the mixture of the sodium hydroxide aqueous solution and the potassium hydroxide aqueous solution are prepared by purifying a waste acid and a waste alkali.

3. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 1 , wherein in the step (1), the hydrochloric acid solution, and the sodium hydroxide aqueous solution or the mixture of the sodium hydroxide aqueous solution and the potassium hydroxide aqueous solution are prepared by providing a sodium chloride aqueous solution or a mixture of a sodium chloride aqueous solution and a potassium chloride aqueous solution to an electrolysis system.

4. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 3 , which further comprises a step (6) of recycling the mixture of the sodium chloride aqueous solution and the potassium chloride aqueous solution remaining after the step (5) to the step (1).

5. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 1 , wherein the inorganic material is one or more selected from a group consisting of waste concrete, slag, fly ash, feldspar (CaAl 2 Si 2 O 8 ), forsterite (Mg 2 SiO 4 ), glauconite, ilmenite (FeTiO 3 ), listwanite (carbonated serpentinite), magnetite, olivine ((Mg,Fe) 2 SiO 4 ), opoka, serpentine, serpentinite, talc (Mg 3 Si 4 Si 10 (OH) 2 ) and wollastonite (CaSiO 3 ).

6. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 1 , wherein the step (2) is performed under a condition of a hydrochloric acid concentration of 0.1-5.0 M, a solid-to-liquid ratio 10-500 g/L, and a reaction temperature of 10-200° C.

7. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 1 , wherein, in the step (2), a hydrochloric acid consumption yield based on the alkali ion is 70-100%.

8. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 1 , wherein a concentration of the sodium hydroxide aqueous solution or the mixture of the sodium hydroxide aqueous solution and the potassium hydroxide aqueous solution added in the step (3) is 0.1-5.0 mol/L.

9. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 1 , wherein, in the step (3), the impurity is removed by adding the sodium hydroxide aqueous solution or the mixture of the sodium hydroxide aqueous solution and the potassium hydroxide aqueous solution such that a pH of the dissolving solution is in a range from about pH 7 to about pH 13.

10. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 9 , wherein the impurity is magnesium chloride, iron chloride, aluminum chloride or a combination thereof.

11. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 9 , wherein, in the step (3), the impurity is precipitated by reacting with the sodium hydroxide aqueous solution or the mixture of the sodium hydroxide aqueous solution and the potassium hydroxide aqueous solution and a precipitated impurity is removed by centrifugation or filtration.

12. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 1 , wherein a concentration of the sodium hydroxide aqueous solution or the mixture of the sodium hydroxide aqueous solution and the potassium hydroxide aqueous solution added in the step (4) is 0.1-5.0 mol/L.

13. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 1 , wherein, in the step (4), a volume ratio of the impurity-removed dissolving solution and the sodium hydroxide aqueous solution or the mixture of the sodium hydroxide aqueous solution and the potassium hydroxide aqueous solution is 2:1 to 1:5.

14. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 1 , wherein the step (5) is performed under a condition of a reaction temperature of 5-150° C. and a pressure of 1-20 atm.

15. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 4 , wherein, in the step (6), cation remaining in the mixture of the sodium chloride aqueous solution and the potassium chloride aqueous solution after the step (5) is removed by a flocculant and then the mixture of the sodium chloride aqueous solution and the potassium chloride aqueous solution, from which the cation is removed, is recycled to the step (1).

16. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 15 , wherein the flocculant is an anionic polymer flocculant.

17. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 4 , wherein, in the step (6), a sodium chloride aqueous solution is additionally provided to the mixture of the sodium chloride aqueous solution and the potassium chloride aqueous solution when the mixture of the sodium chloride aqueous solution and the potassium chloride aqueous solution is recycled to the step (1).

18. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 17 , wherein the additionally provided sodium chloride aqueous solution is provided to the mixture of the sodium chloride aqueous solution and the potassium chloride aqueous solution after its impurity is removed through the step (3) and the step (4).

19. The method for preparing calcium carbonate from an alkali ion-comprising inorganic material according to claim 3 , wherein the electrolysis system of the step (1) produces the sodium hydroxide aqueous solution or the mixture of the sodium hydroxide aqueous solution and the potassium hydroxide aqueous solution at an anode and produces the hydrochloric acid solution at a cathode.

Assignees

• Korea Inst Sci & Tech

Inventors

• Jung Kwang Deog
• Ha Heung Yong
• Oh Jun Woo
• Jo Ho Yong

Classifications

• C21B15/00

  Other processes for the manufacture of iron from iron compounds (by electrolysis C25C1/06) · CPC title

• C22B7/007

  by acid leaching · CPC title

• C01P2006/80

  Compositional purity · CPC title

• Y02P10/234

  Cross-Sectional Technologies · mapped topic

• C01P2004/62

  Submicrometer sized, i.e. from 0.1-1 micrometer · CPC title