Method for producing a tube of glass

Patent metadata

Field	Value
Publication number	US-10315947-B2
Application number	US-201715647881-A
Country	US
Kind code	B2
Filing date	Jul 12, 2017
Priority date	Dec 19, 2014
Publication date	Jun 11, 2019
Grant date	Jun 11, 2019

Abstract

A method for forming a hollow cylinder, in a single step, into a quartz glass tube with a large outer diameter and high dimensional stability is provided. To produce the tube, the cylinder, while rotating, is softened in portions in a heating zone which is moved at a relative feed rate Va and the softened portion is radially expanded by a centrifugal force and/or internal overpressure applied in the hollow cylinder bore so as to form a deformation zone. The radial expansion of the softened portion is carried out at a location-dependent radial expansion rate Vr, the profile of which along the deformation zone has a maximum value Vr,max which is smaller than 20 cm/min. The temperature in a rear heating portion of the heating zone, assigned to the end of the deformation zone, is lower than in a front heating portion assigned to the beginning of the deformation zone.

First claim

We claim:

1. A method for producing a tube ( 22 ) of glass by forming a hollow cylinder ( 2 ) from glass with a first outer diameter D 1 , the method comprising
while the hollow cylinder is rotating about a rotation axis ( 6 ), softening the hollow cylinder in portions in a heating zone ( 20 ) which is moved at a relative feed rate Va to form a softened portion and radially expanding the softened portion under an action of a centrifugal force and/or of an internal overpressure applied in a bore ( 7 ) of the hollow cylinder ( 2 ) so as to form a deformation zone ( 30 ), the tube ( 22 ) being shaped continuously to a second outer diameter D 2 which is greater than the first outer diameter D 1 ,
wherein the radial expansion of the softened portion is carried out at a location-dependent radial expansion rate Vr, a profile of which along the deformation zone ( 30 ) has a maximum value Vr, max, Vr, max being smaller than 20 cm/min,
wherein the radial expansion of the softened portion is such that the tube ( 22 ) is produced at the second outer diameter D 2 which is greater by at least 70 mm than the first outer diameter D 1 in a single forming step, and
wherein the heating zone is subdivided into a front heating portion assigned to a beginning of the deformation zone and a rear heating portion assigned to an end of the deformation zone, with a higher temperature being generated on a surface of the deformation zone by the front heating portion than by the rear heating portion, such that a temperature towards the end of the deformation zone is lower than a temperature at the beginning of the deformation zone.

2. The method according to claim 1 , wherein the tube ( 22 ) is produced with the second outer diameter D 2 being greater by at least 100 mm than the first outer diameter D 1 in the single forming step.

Assignees

• Heraeus Quarzglas

Inventors

• Gromann Boris
• Whippey Nigel

Classifications

• C03B23/07

  by blowing, e.g. for making electric bulbs {(C03B23/097 takes precedence)} · CPC title

• C03B23/08

  to exact dimensions, e.g. calibrating · CPC title

• B23K2101/06

  Tubes · CPC title

• B23K26/53

  for modifying or reforming the material inside the workpiece, e.g. for producing break initiation cracks · CPC title

• C03B23/053 Primary

  by centrifuging ({C03B23/094} , C03B37/04 takes precedence) · CPC title