High block, tack and scrub resistant polymer

Patent metadata

Field	Value
Publication number	US-10301501-B2
Application number	US-201715437879-A
Country	US
Kind code	B2
Filing date	Feb 21, 2017
Priority date	Dec 15, 2011
Publication date	May 28, 2019
Grant date	May 28, 2019

Abstract

The present invention is directed to a coating composition or paint comprising a multistage latex with at least first and second stages, wherein the composition or paint is substantially free of volatile organic compounds (VOC) and capable of film formation even in the absence of coalescent agents. The base paint formulation is capable of being tinted at a point-of-sale (i.e. in-store) using a colorant composition of a type and quantity required to produce a paint of desired color and finish. The paints, including deeply colored paints, show improved block resistance, scrub resistance and tack resistance.

First claim

What is claimed is:

1. A method of making a multistage latex polymer, the method comprising:
preparing a first mixture of monomers for a first stage, the first mixture comprising about 94 to 98 wt % methyl methacrylate, 1 to 3 wt % methacrylic acid, about 1 to 3 wt % ureido-functional monomer, and optionally, about 1 to 3 wt % acetoacetoxy ethyl methacrylate, based on the total weight of the monomers in the first mixture;
preparing a second mixture of monomers for a second stage, the second mixture comprising about 30 to 40 wt % methyl methacrylate, about 50 to 60 wt % butyl acrylate, about 1 to 3% methacrylic acid, about 1 to 5 wt % acetoacetoxy ethyl methacrylate, and about 1 to 3 wt % ureido-functional monomers, based on the total weight of the monomers in the second mixture;
feeding the first mixture into a reactor vessel;
initiating a free radical polymerization of at least the first mixture; and
feeding the second mixture into the reactor vessel,

wherein the multistage latex has at least two distinct theoretical Tg values.

2. The method of claim 1 , wherein the multistage latex is capable of forming a film at a temperature of 4° C. or less.

3. The method of claim 1 , wherein the multistage latex is capable of forming a film at a temperature of 10° C. or less, in the absence of a separate coalescing agent.

4. The method of claim 1 , further comprising forming a composition that includes the multistage latex polymer and up to about 2 wt % coalescing agent, and is capable of forming a film at a temperature of 20° C. or less.

5. The method of claim 1 , wherein the difference in Tg of the first and second stage monomers is at least about 65° C.

6. The method of claim 1 , further comprising forming a coating composition that includes the multi-stage latex polymer, wherein the composition exhibits block resistance rating of at least 6.

7. The method of claim 1 , further comprising forming a coating composition that includes the multi-stage latex polymer, wherein the composition exhibits tack resistance of up to about 3 s.

8. The method of claim 1 , further comprising forming a coating composition that includes the multi-stage latex polymer, wherein the composition is capable of forming a film at temperature of less than about 15° C.

9. The method of claim 1 , further comprising forming a coating composition that includes the multi-stage latex polymer and a colorant, wherein the colorant comprises:
a colorant component;
a surfactant package comprising at least one latex-compatible surfactant; and
a carrier,

wherein the colorant has less than about 20 g/L VOC.

10. The method of claim 1 , further comprising forming a coating composition that includes the multi-stage latex polymer, wherein the composition comprises about 0.1 to 0.3 wt % fluorosurfactant, based on the total weight of the composition.

Assignees

• Valspar Sourcing Inc
• Sherwin Williams Co

Inventors

• Hibben Mary Jane
• Rebel Nicholas
• Hallberg Steven

Classifications

• C09D121/02

  Latex · CPC title

• C09D5/00

  Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced {(electrically insulating plastics, resins or waxes H01B3/30)}; Filling pastes · CPC title

• C09D133/08

  Homopolymers or copolymers of acrylic acid esters · CPC title

• C09D133/12 Primary

  Homopolymers or copolymers of methyl methacrylate · CPC title

• C09D7/80 Primary

  Processes for incorporating ingredients · CPC title