Polyamide compositions comprising a polyamide 6,6 and a blend of high chain-length polyamides, use thereof, and articles obtained therefrom

Patent metadata

Field	Value
Publication number	US-10301469-B2
Application number	US-201515534171-A
Country	US
Kind code	B2
Filing date	Dec 2, 2015
Priority date	Dec 12, 2014
Publication date	May 28, 2019
Grant date	May 28, 2019

Abstract

The present invention provides polyamide compositions comprising (a) at least one polyamide mixture; (b) at least one reinforcing filler; (c) at least one heat stabilizer; and (d) at least one ionic lubricant, wherein the (a) at least one polyamide mixture is formed from (i) a polyamide 6,6, the amount of AEG being greater than the amount of CEG, and (ii) a blend of a first high chain-length polyamide having viscosity number (VN) of X 1 and a second high chain-length polyamide having VN of X 2 , X 1 being greater than X 2 . The polyamide composition can be advantageously used to produce articles exhibiting enhanced chemical resistance, notably CaCl 2 salt crack resistance, such as radiator end tank in an automobile.

First claim

The invention claimed is:

1. A polyamide composition comprising:
(a) at least one polyamide mixture formed from
(i) a polyamide 6,6, of which the amount of amine end groups is greater than the amount of carboxylic acid end groups; and
(ii) a blend of a first high chain-length polyamide having a viscosity number of X 1 and a second high chain-length polyamide having viscosity number of X 2 ;

(b) at least one reinforcing filler;
(c) at least one heat stabilizer; and
(d) at least one ionic lubricant,
wherein
the first high-chain length polyamide and the second high chain-length polyamide have the same monomer constituents,
X 1 is greater than X 2 , and viscosity number is measured in accordance with the standard ISO 307 in a 0.005 g/mL strength solution of polyamide at 25° C., and
wherein a high chain-length polyamide is a polyamide comprising recurring units (R PAL ), at least 50% moles of said recurring units (R PAL ) complying with any of formula (I) or formula (II):
—NH—R 1 —CO—  formula (I):

—NH—R 2 —NH—CO—R 3 —CO—,  formula (II):

wherein
—R 1 , equal to or different from each other at each occurrence, is a divalent hydrocarbon group having from 6 to 17 atoms
and wherein R 2 and R 3 , equal to or different from each other at each occurrence, are divalent hydrocarbon groups, with the proviso that at least one of following conditions is satisfied:
—R 2 has from 7 to 18 carbon atoms; and
—R 3 has from 5 to 16 carbon atoms,
or
wherein a high chain-length polyamide is a polyamide comprising recurring units (R PAL ) of the polyamide which are obtained through polycondensation reaction of one of pimelic acid [HOOC—(CH 2 ) 5 —COOH], suberic acid [HOOC—(CH 2 ) 6 —COOH], azelaic acid [HOOC—(CH 2 ) 7 —COOH], sebacic acid [HOOC—(CH 2 ) 8 —COOH], undecanedioic acid [HOOC—(CH 2 ) 9 —COOH], dodecandioic acid [HOOC—(CH 2 ) 10 —COOH], tetradecandioic acid [HOOC—(CH 2 ) 12 —COOH], octadecandioic acid [HOOC—(CH 2 ) 16 —COOH] with one of 1,6-diaminohexane, 1,6-diamino-2,5-dimethylhexane, 1,6-diamino-2,4-dimethylhexane, 1,6-diamino-3,3-dimethylhexane, 1,6-diamino-2,2-dimethylhexane, 1,6- diamino-2,2,4-trimethylhexane, 1,6-diamino-2,4,4-trimethylhexane, and 1,6-diamino-2,4-diethylhexane.

2. The polyamide composition according to claim 1 , wherein the amount of amine end groups of the polyamide composition is at least 60 meq/kg, and viscosity number of the polyamide composition is between 110 and 140 ml/g.

3. The polyamide composition according to claim 1 , wherein the amount of amine end groups of the polyamide 6,6 is greater than or equal to 50 meq/kg and the difference between the amount of amine end groups and the amount of carboxylic acid end groups in the polyamide 6,6 is greater than or equal to 5 meq/kg.

4. The polyamide composition according to claim 1 , wherein said first high chain-length polyamide and said second high chain-length polyamide are independently selected from the group consisting of polyamide 11, polyamide 12, polyamide 6,10, polyamide 6,12, polyamide 6,18, polyamide 10,10, polyamide 10,12, polyamide 12,12, and mixtures thereof.

5. The polyamide composition according to claim 1 , wherein X 1 is between 122 and 160 ml/g and X 2 is between 95 and 120 ml/g.

6. The polyamide composition according to claim 1 , wherein an amount of the at least one polyamide mixture is from 40.0 to 95.0 wt % relative to the total weight of the polyamide composition.

7. The polyamide composition according to claim 1 , wherein the weight ratio of the polyamide 6,6 to the blend of high chain-length polyamides within the polyamide mixture is between about 5:5 and about 3:7, and/or wherein the weight ratio of said first high chain-length polyamide to said second high chain-length polyamide is between about 5:2 and about 3:1.

8. The polyamide composition according to claim 1 , wherein the at least one reinforcing filler is selected from the group consisting of glass fibers, glass beads, calcium carbonate, silicates, talc, kaolin, mica, wood powders, and powders and fibers of other natural products, and synthetic fibers.

9. The polyamide composition according to claim 1 , wherein an amount of the at least one reinforcing filler is from 1.0 to 60.0 wt %, relative to the total weight of the polyamide composition.

10. The polyamide composition according to claim 1 , wherein the at least one heat stabilizer is formed from CuI/KI in a molar ratio of CuI to KI of about 1:5.

11. The polyamide composition according to claim 1 , wherein the at least one heat stabilizer is a combination of a hindered phenol compound and a phosphorous compound.

12. The polyamide composition according to claim 1 , wherein the amount of the at least one heat stabilizer is from 0.05 to 3.0 wt %, relative to the total weight of the polyamide composition.

13. The polyamide composition according to claim 1 , wherein the at least one ionic lubricant is selected from the group consisting of aluminum salts, alkali metal salts, alkaline earth metal salts, or esters or amides of fatty acids having 10 to 44 carbon atoms.

14. The polyamide composition according to claim 1 , wherein the amount of the at least one ionic lubricant is from 0.05 to 1.0 wt %, relative to the total weight of the polyamide composition.

15. The polyamide composition according to claim 1 , further comprising one or more additive selected from the group consisting of antioxidant, UV stabilizer, colorant, dye, chain extender, plasticizer, and any combinations thereof.

16. A method for producing an article exhibiting enhanced chemical resistance, comprising molding a polyamide composition to form the article, wherein the polyamide composition comprises:
(a) at least one polyamide mixture formed from
(i) a polyamide 6,6, of which the amount of amine end groups is greater than the amount of carboxylic acid end groups; and
(ii)a blend of a first high chain-length polyamide having a viscosity number of X 1 and a second high chain-length polyamide having viscosity number of X 2 ;

(b) at least one reinforcing filler;
(c) at least one heat stabilizer; and
(d) at least one ionic lubricant,
wherein
the first high-chain length polyamide and the second high chain-length polyamide have the same monomer constituents,
X 1 is greater than X 2 , and viscosity number is measured in accordance with the standard ISO 307 in a 0.005 g/mL, strength solution of polyamide at 25° C., and
wherein a high chain-length polyamide is a polyamide comprising recurring units (R PAL ), at least 50% moles of said recurring units (R PAL ) complying with any of formula (I) or formula (II):
—NH—R 1 —CO—  formula (I):

—NH—R 2 —NH—CO—R 3 —CO—,  formula (II):

wherein
—R 1 , equal to or different from each other at each occurrence, is a divalent hydrocarbon group having from 6 to 17 atoms
and wherein R 2 and R 3 , equal to or different from each other at each occurrence, are divalent hydrocarbon groups, with the proviso that at least one of the following conditions is satisfied:
—R 2 has from 7 to 18 carbon atoms; and
—R 3 has from 5 to 16 carbon atoms,
or
wherein a high chain-length polyamide is a polyamide comprising recurring units (R PAL ) of the polyamide which are obtained through polycondensation reaction of one of
pimelic acid [HOOC—(CH 2 ) 5 —COOH], suberic acid [HOOC—(CH 2 ) 6 —COOH], azelaic acid [HOOC—(CH 2 ) 7 —COOH], sebacic acid [HOOC—(CH 2 ) 8 —COOH], undecanedioic acid [HOOC—(CH 2 ) 9 —COOH], dodecandioic acid [HOOC—(CH 2 ) 10 —COOH], tetradecandioic acid [HOOC—(CH 2 ) 12 —COOH], octadecandioic acid [HOOC—(CH 2 ) 16 —COOH] with one of 1,6-diam

Assignees

• Rhodia Operations

Inventors

• Jung Jin-Kyung
• Seignobos Elodie
• Yu Yeong-Chool

Classifications

• C10N2010/06

  Groups 3 or 13 · CPC title

• C10N2010/02

  Groups 1 or 11 · CPC title

• C10N2010/04

  Groups 2 or 12 · CPC title

• C08K5/098

  Metal salts of carboxylic acids · CPC title

• C08L77/06 Primary

  Polyamides derived from polyamines and polycarboxylic acids (C08L77/10 takes precedence) · CPC title