Metal plate coated stainless material and method of producing metal plate coated stainless material

Patent metadata

Field	Value
Publication number	US-10294568-B2
Application number	US-201415023323-A
Country	US
Kind code	B2
Filing date	Sep 11, 2014
Priority date	Sep 20, 2013
Publication date	May 21, 2019
Grant date	May 21, 2019

Abstract

There is provided a metal plate coated stainless material (100) which includes a stainless steel sheet (10) having formed thereon a passivation film (11) having a Cr/O value in the range of 0.05 to 0.2 and a Cr/Fe value in the range of 0.5 to 0.8 at the surface as measured by an Auger electron spectroscopy analysis and a metal plated layer (20) formed on the passivation film (11) of the stainless steel sheet (10), in which the metal plated layer (20) is a plated layer formed from any one metal selected from among Ag, Pd, Pt, Rh, Ru, Cu, Sn and Cr, or an alloy of these metals.

First claim

What is claimed is:

1. A metal plate coated stainless material comprising:
a stainless steel sheet coated with a metal plated layer which is deposited on a passivation film present on the surface of the stainless steel sheet, wherein
the passivation film has a surface composition having a Cr/O value comprised within a range from 0.05 to 0.2 and a Cr/Fe value comprised within a range from 0.5 to 0.8, the Cr/0 value and the Cr/Fe value obtained by Auger electron spectroscopy analysis, and
the metal plated layer is formed from any one metal selected from among Ag, Pd, Pt, Rh, Ru, Cu, Sn and Cr, or an alloy composed of at least two or more metals selected from among these metals.

2. The metal plate coated stainless material according to claim 1 , wherein the metal plated layer has a coverage of 95% or more with respect to the passivation film.

3. The metal plate coated stainless material according to claim 1 , wherein the metal plated layer essentially consists of one or more metal selected from a group consisting of Ag, Pd, Pt, Rh, Ru, Cu, Sn and Cr.

4. The metal plate coated stainless material according to claim 1 , wherein the ratio (Fe (metal)/Fe (total)) of an elementary substance of iron (Fe (metal) to the total amount of Fe atoms (Fe (total)) at the surface of the passivation film is 14% or more.

5. The metal plate coated stainless material according to claim 1 , wherein the ratio (Ni (metal)/Ni (total)) of an elementary substance of nickel (Ni (metal) to the total amount of Ni atoms (Ni (total)) at the surface of the passivation film is 18% or more.

6. The metal plate coated stainless material according to claim 1 , wherein an arithmetic average roughness Ra of the passivation film is 0.015 μm to 0.036 μm.

7. The metal plate coated stainless material according to claim 1 , wherein the thickness of the metal plated layer is within 2 to 20 nm.

Assignees

• Toyo Kohan Co Ltd

Inventors

• Mukai Nobuaki
• Yoshida Takahiro

Classifications

• C23C18/38

  Coating with copper · CPC title

• C25D3/46

  of silver · CPC title

• C23C28/34

  including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates · CPC title

• C23C18/42 Primary

  Coating with noble metals · CPC title

• C23C18/31

  Coating with metals · CPC title