Bulk nickel-phosphorus-silicon glasses bearing manganese

Patent metadata

Field	Value
Publication number	US-10287663-B2
Application number	US-201514824733-A
Country	US
Kind code	B2
Filing date	Aug 12, 2015
Priority date	Aug 12, 2014
Publication date	May 14, 2019
Grant date	May 14, 2019

Abstract

The disclosure is directed to Ni—P—Si alloys bearing Mn and optionally Cr, Mo, Nb, and Ta that are capable of forming a metallic glass, and more particularly demonstrate critical rod diameters for glass formation greater than 1 mm and as large as 5 mm or larger.

First claim

What is claimed:

1. An alloy capable of forming a metallic glass represented by the following formula (subscripts denote atomic percentages):
Ni (100-a-b-c-d) Mn a X b P c Si d
where:
a is between 0.25 and 12,
b is up to 20,
c is between 14 and 22,
d is between 0.25 and 5,
and where X is selected from Cr, Mo, Nb, Ta, and combinations thereof or by the above formula and wherein:
i) up to 50 atomic percent of Ni is substituted by Co,
ii) up to 30 atomic percent of Ni is substituted by Fe,
iii) up to 10 atomic percent of Ni is substituted by Cu, or
iv) up to 2 atomic percent of Ni is substituted by Ge, V, Sn, W, Ru, Re, Pd, Pt, or a combination thereof.

2. The alloy according to claim 1 , wherein X is selected from Cr and Mo, and combinations thereof, and b is up to 18 percent.

3. The alloy according to claim 1 , wherein X is selected from Nb and Ta, and combinations thereof, and b is up to 6 percent.

4. The alloy according to claim 1 , wherein X is Mo and Nb.

5. The alloy according to claim 4 , wherein the atomic concentration of Mo is between 0.5 and 4 atomic percent, and the critical rod diameter of the alloy is at least 1 mm.

6. The alloy according to claim 4 , wherein the atomic concentration of Nb is between 2.5 and 5 atomic percent, and the critical rod diameter of the alloy is at least 2 mm.

7. The alloy according to claim 1 , wherein X is Cr.

8. The alloy according to claim 7 , wherein a is between 1 and 7, and the critical rod diameter of the alloy is at least 1 mm.

9. The alloy according to claim 7 , wherein b is between 5 and 15, and the critical rod diameter of the alloy is at least 1 mm.

10. The alloy according to claim 7 , wherein c is between 15 and 21, and the critical rod diameter of the alloy is at least 1 mm.

11. The alloy according to claim 7 , wherein d is between 0.25 and 3, and the critical rod diameter of the alloy is at least 1 mm.

12. The alloy according to claim 1 , wherein up to 50 atomic percent of Ni is substituted with Co.

13. The alloy according to claim 1 , wherein up to 30 atomic percent of Ni is substituted by Fe.

14. The alloy according to claim 1 , wherein up to 10 atomic percent of Ni is substituted by Cu.

15. The alloy according to claim 1 , wherein the alloy further comprises Ge, V, Sn, W, Ru, Re, Pd, Pt, or a combination thereof at combined atomic concentration of up to 2 percent.

16. A metallic glass comprising an alloy, wherein a composition of the alloy is represented by the following formula (subscripts denote atomic percentages):
Ni (100-a-b-c-d) Mn a X b P c Si d
where:
a is between 0.25 and 12,
b is up to 20,
c is between 14 and 22,
d is between 0.25 and 5,

and where X is selected from Cr, Mo, Nb, Ta, and combinations thereof.

17. A method of producing a metallic glass comprising:
melting an alloy into a molten state to form an alloy melt; where the alloy has a composition represented by the following formula (subscripts denote atomic percentages):
Ni (100-a-b-c-d) Mn a X b P c Si d

where:
a is between 0.25 and 12,
b is up to 20,
c is between 14 and 22,
d is between 0.25 and 5,

where X is selected from Cr, Mo, Nb, Ta, and combinations thereof; and
quenching the alloy melt at a cooling rate sufficiently rapid to prevent crystallization of the alloy.

18. The method of claim 17 , further comprising fluxing the alloy melt with a reducing agent prior to quenching.

19. The method of claim 17 , wherein the temperature of the alloy melt prior to quenching is at least 1100° C.

20. The method of claim 17 , wherein the temperature of the alloy melt prior to quenching is at least 100° C. above the liquidus temperature of the alloy.

Assignees

• Glassimetal Tech Inc
• Apple Inc

Inventors

• Na Jong Hyun
• Duggins Danielle
• Abarca Oscar
• Launey Maximilien
• Demetriou Marios D
• Johnson William L

Classifications

• C22C19/058

  without Mo and W · CPC title

• C22C1/11

  Making amorphous alloys · CPC title

• C22C45/02

  with iron as the major constituent · CPC title

• C22F1/002

  by rapid cooling or quenching; cooling agents used therefor · CPC title

• C22F1/10 Primary

  of nickel or cobalt or alloys based thereon · CPC title