Surface-treated fillers for breathable films

Patent metadata

Field	Value
Publication number	US-10287407-B2
Application number	US-201515502537-A
Country	US
Kind code	B2
Filing date	Aug 12, 2015
Priority date	Aug 14, 2014
Publication date	May 14, 2019
Grant date	May 14, 2019

Abstract

The present invention relates to a breathable film comprising at least one thermoplastic polymer and a surface-treated filler material product comprising a treatment layer comprising at least one mono-substituted succinic anhydride and/or at least one mono-substituted succinic acid and/or salty reaction product(s) thereof, a process for producing the same, and the use thereof. Furthermore, the present invention is directed to the use of a surface-treated filler material product comprising a treatment layer comprising at least one mono-substituted succinic anhydride and/or at least one mono-substituted succinic acid and/or salty reaction product(s) thereof in breathable films.

First claim

The invention claimed is:

1. A breathable film comprising at least one thermoplastic polymer and a surface-treated filler material product, wherein the surface-treated filler material product comprises:
A) at least one ground calcium carbonate-comprising filler material having:
a weight median particle size d 50 in the range from 0.1 μm to 7 μm,
a top cut particle size d 98 of less than or equal to 15 μm,
a specific surface area (BET) from 0.5 to 150 m 2 /g, as measured using nitrogen and the BET method according to ISO 9277, and
a residual total moisture content of less than or equal to 1 wt.-%, based on the total dry weight of the at least one ground calcium carbonate-comprising filler material, and

B) a treatment layer on the surface of the at least one ground calcium carbonate-comprising filler material comprising at least one mono-substituted succinic anhydride and/or at least one mono-substituted succinic, acid and/or salty reaction product(s) thereof,
wherein the surface-treated filler material product comprises the treatment layer in an amount of from 0.1 to 3 wt.-%, based on the total dry weight of the at least one ground calcium carbonate-comprising filler material,
wherein the breathable film comprises 2 to 80 wt.-% of the surface-treated filler material product, based on the total weight of the breathable film, and 15 to 70 wt.-% of the at least one thermoplastic polymer, based on the total weight of the breathable film, and
wherein the breathable film has a water vapour transmission rate (WVTR) from 500 to 10,000 g/m 2 ·day), measured according to ASTM 398.

2. The breathable film of claim 1 , wherein the at least one ground calcium carbonate-comprising filler material is a wet ground calcium carbonate-comprising filler material.

3. The breathable film of claim 1 , wherein the at least one thermoplastic polymer is a polyolefin.

4. The breathable film of claim 1 , wherein the at least one thermoplastic polymer is a polyolefin selected from the group consisting of polypropylene, polyethylene, polybutylene, and any mixture thereof.

5. The breathable film of claim 1 , wherein the at least one thermoplastic polymer is selected from the group consisting of high density polyethylene (HDPE), linear low density polyethylene (LLDPE), low density polyethylene (LDPE), ultra-low density polyethylene (ULDPE), very low density polyethylene (VLDPE), and any mixture thereof.

6. The breathable film of claim 1 , wherein the breathable film comprises the surface-treated filler material product in an amount from 5 to 75 wt.-%, based on the total weight of the breathable film.

7. The breathable film of claim 1 , wherein the breathable film comprises the surface-treated filler material product in an amount from 10 to 65 wt.-%, based on the total weight of the breathable film.

8. The breathable film of claim 1 , wherein the at least one ground calcium carbonate-comprising filler material is selected from the group consisting of natural ground calcium carbonate, precipitated calcium carbonate, modified calcium carbonate, surface-treated calcium carbonate, and any mixture thereof.

9. The breathable film of claim 1 , wherein the at least one ground calcium carbonate-comprising filler material has a weight median particle size d 50 from 0.25 μm to 5 μm.

10. The breathable film of claim 1 , wherein the at least one ground calcium carbonate-comprising filler material has a top cut particle size d 98 of less than or equal to 12.5 μm.

11. The breathable film of claim 1 , wherein the at least one ground calcium carbonate-comprising filler material has a specific surface area (BET) of from 0.5 to 50 m 2 /g, as measured using nitrogen and the BET method according to ISO 9277.

12. The breathable film of claim 1 , wherein the at least one ground calcium carbonate-comprising filler material has a residual total moisture content of from 0.01 to 0.2 wt.-%, based on the total dry weight of the at least one ground calcium carbonate-comprising filler material.

13. The breathable film of claim 1 , wherein the at least one ground calcium carbonate-comprising filler material has a residual total moisture content of from 0.04 to 0.15 wt.-%, based on the total dry weight of the at least one ground calcium carbonate-comprising filler material.

14. The breathable film of claim 1 , wherein the at least one mono-substituted succinic anhydride consists of succinic anhydride mono-substituted with a group selected from a linear, branched, aliphatic and cyclic group having a total amount of carbon atoms from C2 to C30 in the substituent.

15. The breathable film of claim 1 , wherein the at least one mono-substituted succinic anhydride consists of succinic anhydride mono-substituted with a group selected from a linear, branched, aliphatic and cyclic group having a total amount of carbon atoms from C4 to C20 in the substituent.

16. The breathable film of claim 1 , wherein the surface-treated filler material product has a moisture pick-up from 0.1 to 1 mg/g, at a temperature of 23° C. (±2° C.).

17. The breathable film of claim 1 , wherein the surface-treated filler material product has a moisture pick-up from 0.2 to 0.8 mg/g, at a temperature of 23° C. (±2° C.).

18. The breathable film of claim 1 , wherein the surface-treated filler material product has a volatile onset temperature of greater than or equal to 250° C.

19. The breathable film of claim 1 , wherein the surface-treated filler material product has a volatile onset temperature of greater than or equal to 270° C.

20. The breathable film of claim 1 , wherein the treatment layer on the surface of the at least one ground calcium carbonate-comprising filler material comprises at least one mono-substituted succinic anhydride and/or at least one mono-substituted succinic acid and/or salty reaction product(s) and at least one polydialkylsiloxane selected from the group consisting of polydimethylsiloxane, polydiethylsiloxane, polymethylphenylsiloxane, and mixtures thereof.

21. The breathable film of claim 1 , wherein the at least one ground calcium carbonate-comprising filler material comprises a treatment layer comprising at least one mono-substituted succinic anhydride and/or at least one mono-substituted succinic acid and/or salty reaction product(s), and an after treatment layer comprising at least one polydialkylsiloxane from the group consisting of polydimethylsiloxane, polydiethylsiloxane, polymethylphenylsiloxane and/or mixtures thereof.

22. A process for producing the breathable film of claim 1 , comprising the steps of:
a) providing a composition comprising at least one thermoplastic polymer and a surface-treated filler material product,
b) forming a film from the composition of step a), and
c) stretching the film obtained in step b) into at least one direction, wherein the surface-treated filler material product comprises:
A) at least one ground calcium carbonate-comprising filler material having
a weight median particle size d 50 in the range from 0.1 μm to 7 μm,
a top cut particle size d 98 of less than or equal to 15 μm,
a specific surface area (BET) from 0.5 to 150 m 2 /g, as measured using nitrogen and the BET method according to ISO 9277, and
a residual total moisture content of less than or equal to 1 wt.-%, based on the total dry weight of the at least one ground calcium carbonate-comprising filler material, and

B) a treatment layer on the surface of the at least one wet ground calcium carbonate-comprising filler material comprising at

Assignees

• Omya Int Ag

Inventors

• Brunner Martin
• Burkhalter René
• Fornera Tazio
• Rentsch Samuel
• Tinkl Michael
• Pullega Francesco
• Moore Monroe

Classifications

• C08J2323/06

  Polyethene · CPC title

• C01P2004/51

  Particles with a specific particle size distribution · CPC title

• C09C1/021

  Calcium carbonates · CPC title

• C01P2006/82

  water content · CPC title

• C08J5/18 Primary

  Manufacture of films or sheets · CPC title