Micromachined electrolyte sheet

Patent metadata

Field	Value
Publication number	US-10283811-B2
Application number	US-201113249935-A
Country	US
Kind code	B2
Filing date	Sep 30, 2011
Priority date	Sep 30, 2011
Publication date	May 7, 2019
Grant date	May 7, 2019

Abstract

The disclosure relates to ceramic lithium ion electrolyte membranes and processes for forming them. The ceramic lithium electrolyte membrane may comprise at least one ablative edge. Exemplary processes for forming the ceramic lithium ion electrolyte membranes comprise fabricating a lithium ion electrolyte sheet and cutting at least one edge of the fabricated electrolyte sheet with an ablative laser.

First claim

What is claimed:

1. A process for forming a ceramic lithium-ion electrolyte membrane, said process comprising the steps of:
fabricating a fired lithium-ion electrolyte sheet, wherein the step of fabricating a lithium-ion electrolyte sheet comprises the steps of
mixing starting materials,
treating the mixed starting materials to form a lithium metal phosphate powder,
further processing the powder to a particle size of less than about 5.0 μm,
adding phosphoric acid to the powder, wherein adding phosphoric acid to the powder comprises adding to the powder P 2 O 5 in the range of 0.5 to 5 wt % of an inorganic solids content of the powder,
casting the powder to form a tape, and
firing the tape;

and subsequently
cutting at least one edge of the fired tape with an ablative laser to form an ablative edge.

2. The process of claim 1 , wherein the ablative laser comprises an Nd:YVO 4 laser.

3. The process of claim 1 , wherein the ablative laser has a wavelength of less than about 2 μm, a fluence of less than about 250 Joules/cm 2 , repetition rate between about 20 Hz and 100 MHz, and cutting speed over about 10 mm/sec.

4. The process of claim 1 , wherein the ceramic lithium-ion electrolyte membrane is less than about 200 μm thick.

5. The process of claim 1 , wherein the ceramic lithium-ion electrolyte membrane is comprised of grains having an average grain size of less than about 5 μm.

6. The process of claim 1 , wherein the ceramic lithium-ion electrolyte membrane has a relative density greater than about 90%.

7. The process of claim 1 , wherein the ablative edge is an outer edge.

8. The process of claim 1 , wherein the ablative edge is enriched with lithium relative to a bulk of the membrane.

9. The process of claim 1 , wherein the ablative edge comprises a depth of less than about 5 μm.

10. The process of claim 1 , wherein the lithium metal phosphate is LATP.

Assignees

• Badding Michael Edward
• Dutta Indrajit
• Kester Lanrik
• Li Xinghua
• Corning Inc

Inventors

• Badding Michael Edward
• Dutta Indrajit
• Kester Lanrik
• Li Xinghua

Classifications

• H01M10/0562 Primary

  Solid materials · CPC title

• H01M2300/0068

  inorganic · CPC title

• H01M50/406

  Moulding; Embossing; Cutting · CPC title

• H01M2/145

  Electricity · mapped topic

• Y02E60/10

  Energy storage using batteries · CPC title