Methane steam reforming, using nickel/alumina nanocomposite catalyst or nickel/silica-alumina hybrid nanocomposite catalyst

Patent metadata

Field	Value
Publication number	US-10280080-B2
Application number	US-201615156741-A
Country	US
Kind code	B2
Filing date	May 17, 2016
Priority date	Jun 30, 2015
Publication date	May 7, 2019
Grant date	May 7, 2019

Abstract

The present invention relates to a method of methane steam reforming using a nickel/alumina nanocomposite catalyst. More specifically, the present invention relates to a method of carrying out methane steam reforming using a nickel/alumina nanocomposite catalyst wherein nickel metal nanoparticles are uniformly loaded in a high amount on a support via a melt infiltration method with an excellent methane conversion even under a relatively severe reaction condition of a high gas hourly space velocity or low steam supply, and to a catalyst for this method. In addition, the present invention prepares a nickel/silica-alumina hybrid nanocatalyst by mixing the catalyst prepared by the melt infiltration method as the first catalyst and the nickel silica yolk-shell catalyst as the second catalyst, and applies it to the steam reforming of methane to provide a still more excellent catalytic activity even under the higher temperature of 700° C. or more with the excellent methane conversion.

First claim

What is claimed is:

1. A method of methane steam reforming with a methane conversion of 50% or more under severe reaction conditions of a high gas hourly space velocity of 100 to 300 NL·g cat −1 ·h −1 and a low steam supply with a molar ratio of steam/methane (H 2 O/CH 4 ) of 2 to 4, which comprises:
i) a step of providing a first catalyst for methane steam reforming, wherein nickel particles having an average particle size of 10 nm or less are uniformly loaded into pores distributed inside a porous gamma-alumina support, thereby preventing an inactivation of catalyst due to carbon deposition under severe reaction conditions of the high gas hourly space velocity of 100 to 300 NL·g cat −1 ·h −1 and the low steam supply with the molar ratio of steam/methane (H 2 O/CH 4 ) of 2 to 4, which is prepared by a first step of grinding and mixing the porous gamma-alumina support and a nickel-containing compound having a melting point lower than the porous gamma-alumina support, and melt-infiltrating the nickel-containing compound into pores of the surface, inside, or both of the porous gamma-alumina support in a closed system at a temperature ranging from the melting point of the nickel-containing compound to +5° C. higher than the melting point; and a second step of thermally treating the melt-infiltrated composite powder at 400 to 600° C. under reducing gas atmosphere to load nickel particles having the average particle size of 10 nm or less in the porous gamma-alumina support; or
a nickel/silica-alumina hybrid catalyst comprising:
the first catalyst; and
a yolk-shell shaped second catalyst for methane steam reforming which includes a hollow shell consisting of porous silica of which inside is accessible to methane; and a core consisting of nickel-containing panicle located inside the hollow shell;

ii) a step of applying the first catalyst with the methane conversion of 50% or more under severe reaction conditions of the high gas hourly space velocity of 200 NL·g cat −1 ·h −1 and low steam supply with a molar ratio of steam/methane (H 2 O/CH 4 ) of 2, or the hybrid catalyst comprising the first catalyst and the yolk-shell shaped second catalyst to a reactor of methane steam reforming;
iii) a step of reducing to activate the first catalyst, or the hybrid catalyst to form an activated catalyst; and
iv) a step of feeding methane-containing gas and steam to the reactor of methane steam reforming and carrying out the methane steam reforming by using the activated catalyst for methane steam reforming under the molar ratio of steam/methane (H 2 O/CH 4 ) of 2 to 4 and the gas hourly space velocity (GHSV) of 100 to 300 NL·g cat −1 ·h −1 , while the carbon deposition on the nickel particles loaded into pores distributed inside the porous gamma-alumina support is prevented, thereby extending an inactivation time of the first catalyst.

2. The method of claim 1 wherein the nickel/silica-alumina hybrid catalyst is used in the methane steam reforming.

3. The method of claim 1 , wherein the porous gamma-alumina support has a pore volume of 0.3 to 0.6 cm 3 /g and a specific surface area of 100 to 300 m 2 /g.

4. The method of claim 1 , wherein the nickel-containing compound is a nickel hydrate salt having a melting point of 30 to 150° C.

5. The method of claim 1 , wherein the nickel-containing compound is Ni(NO 3 ) 2 .6H 2 O, NiSO 4 .6H 2 O, NiCl 2 .6H 2 O, or a mixture thereof.

6. The method of claim 1 , wherein the loading amount of nickel in the first catalyst; or in the hybrid catalyst of the first and the second catalysts is 10 to 80% by weight based on the weight of the whole catalyst.

7. The method of claim 1 , wherein the first catalyst for methane steam reforming is prepared by a process further comprising a third step of passivating the first catalyst with an organic solvent after the second step of thermally treating the melt-infiltrated composite powder at 400 to 600° C. under reducing gas atmosphere to load nickel particles having the average particle size of 10 nm or less in the porous gamma-alumina support.

8. The method of claim 1 , wherein the yolk-shell shaped second catalyst is prepared by coating the surface of nickel salt-containing nanoparticles with a pore forming material and a silica precursor, selectively etching the nickel salt-containing nanoparticles by the treatment with an acid to make the yolk-shell shape, and then reducing the nickel salt to nickel metal with removing the pore forming material via a thermal treatment process under reducing atmosphere to form the porous hollow shell.

9. The method of claim 8 , wherein the nickel salt is nickel (II) acetate tetrahydrate (Ni(CH 3 COO) 2 .4H 2 O), nickel (II) acetylacetonate (Ni(C 5 H 7 O 2 ) 2 ), or a mixture thereof.

10. The method of claim 8 , wherein the pore forming material is a compound having a long carbon chain of C 10 ˜C 30 .

11. The method of claim 8 , wherein the silica precursor is tetraethyl ortho silicate (TEOS, Si(OC 2 H 5 ) 4 ), tetramethyl ortho silicate (TMOS, Si(OCH 3 ) 4 ), or a mixture thereof.

12. The method of claim 8 , wherein the acid used for etching is hydrochloric acid, sulfuric acid, nitric acid, or a mixture thereof.

13. The method of claim 8 , wherein the thermal treatment process is carried out for 2 to 10 hours at 500 to 700° C.

14. The method of claim 1 , wherein the methane-containing gas is natural gas.

15. The method of claim 1 , wherein the methane steam reforming of Step iv) is carried out under the reaction temperature of 500 to 900° C. reaction pressure of 1 to 10 bar, the molar ratio of steam/methane (H 2 O/CH 4 ) of 2 to 4, and gas hourly space velocity (GHSV) of 100 to 300 NL·g cat −1 ·h −1 .

16. The method of claim 15 , wherein the steam reforming of methane in Step iv) is carried out at the reaction temperature of 500 to 750° C. when the first catalyst is used as the catalyst for methane steam reforming without the second catalyst.

17. The method of claim 15 , wherein the steam reforming of methane in Step iv) is carried out at the reaction temperature of 700 to 900° C. when the hybrid catalyst of the first and the second catalysts is used as the catalyst for methane steam reforming.

18. A method of preparing hydrogen from methane-containing gas with a methane conversion of 50% or more under severe reaction conditions of a high gas hourly space velocity of 100 to 300 NL·g cat −1 ·h −1 and a low steam supply with a molar ratio of steam/methane (H 2 O/CH 4 ) of 2 to 4, which comprises:
i) a step of providing a first catalyst for methane steam reforming, wherein nickel particles having an average particle size of 10 nm or less are uniformly loaded into pores distributed inside a porous gamma-alumina support, thereby preventing an inactivation of catalyst due to carbon deposition under severe reaction conditions of the high gas hourly space velocity of 100 to 300 NL·g cat −1 ·h −1 and the low steam supply with the molar ratio of steam/methane (H 2 O/CH 4 ) of 2 to 4, which is prepared by a first step of grinding and mixing the porous gamma-alumina support and a nickel-containing compound having a melting point lower than the porous gamma-alumina support, and melt-infiltrating the nickel-containing compound into pores of the surface, inside, or both of the porous gamma-alumina support in a closed system at a temperature ranging from the melting point of the nickel-containing compound to +5° C. higher than the melting point; and a second step of thermally treating the melt-infiltrated composite powder at 400 to 600° C. under reducing gas atmosphere to load

Assignees

• Korea Inst Energy Res

Inventors

• Park Ji Chan
• Yang Jung Il
• Jung Heon
• Lim Tak Hyoung

Classifications

• B01J37/18

  with gases containing free hydrogen · CPC title

• C01B3/382

  Processes with two or more reaction steps, of which at least one is catalytic, e.g. steam reforming and partial oxidation · CPC title

• C01B2203/1082

  Composition of support materials · CPC title

• C01B2203/1058

  Nickel catalysts · CPC title

• C01B2203/142

  At least two reforming, decomposition or partial oxidation steps in series · CPC title