Pressure-sensitive adhesive composition for optical film, pressure-sensitive adhesive layer for optical film, pressure-sensitive adhesive optical film, and image display device

Patent metadata

Field	Value
Publication number	US-10266629-B2
Application number	US-201113641904-A
Country	US
Kind code	B2
Filing date	May 16, 2011
Priority date	May 18, 2010
Publication date	Apr 23, 2019
Grant date	Apr 23, 2019

Abstract

An aqueous dispersion-type pressure-sensitive adhesive composition for an optical film includes a emulsion particles of a core-shell structure, wherein the emulsion particles include a (meth)acryl-based copolymer (A) having a glass transition temperature of −55° C. to 0° C. and a (meth)acryl-based copolymer (B) having a glass transition temperature of 0° C. to 180° C., in a single emulsion particle, one of the copolymers (A) and (B) forms a core layer, and another forms a shell layer, at least one of the copolymers (A) and (B) contains a carboxyl group-containing monomer, a difference of the glass transition temperatures between the copolymers (A) and (B) is 50° C. or more, and a ratio (A)/(B) (by weight) is in the range of 50/50 to 90/10.

First claim

The invention claimed is:

1. An aqueous dispersion-type pressure-sensitive adhesive composition for an optical film, comprising emulsion particles of a core-shell structure, wherein
the emulsion particles comprise:
a (meth)acryl-based copolymer (A) containing an alkyl (meth)acrylate as a monomer unit and having a glass transition temperature of −55° C. to 0° C.; and a (meth)acryl-based copolymer (B) containing an alkyl (meth)acrylate as a monomer unit and having a glass transition temperature of 70° C. to 180° C.;
wherein the glass transition temperature is calculated based on monofunctional monomers for monomer units,
in a single emulsion particle, one of the (meth)acryl-based copolymers (A) and (B) forms a core layer, and another of the copolymers (A) and (B) forms a shell layer,
at least one of the (meth)acryl-based copolymers (A) and (B) contains a carboxyl group-containing monomer as a monomer unit,
a difference of the glass transition temperatures between the (meth)acryl-based copolymers (A) and (B) is 50° C. or more,
a ratio (A)/(B) by weight of the (meth)acryl-based copolymers (A) and (B) is in the range of 50/50 to 90/10, and
the (meth) acryl-based copolymers (B) contains a alkyl methacrylate as a monomer unit and the content of the alkyl methacrylate is 60 to 99.9% by weight of all monomer units in the (meth) acryl-based copolymer (B).

2. The aqueous dispersion-type pressure-sensitive adhesive composition for an optical film according to claim 1 , wherein the (meth)acryl-based copolymer (B) forms the core layer, and the (meth)acryl-based copolymer (A) forms the shell layer.

3. The aqueous dispersion-type pressure-sensitive adhesive composition for an optical film according to claim 1 ,
wherein at least one of the (meth)acryl-based copolymers (A) and (B) contains an alkoxysilyl group-containing monomer as a monomer unit and
wherein the alkoxysilyl group-containing monomer is excluded from the monofunctional monomers for calculation of the glass transition temperature, and
wherein a content of the alkoxysilyl group-containing monomer is 0.001 to 1% by weight of all monomer units in the (meth)acryl-based copolymer (A) or (B).

4. The aqueous dispersion-type pressure-sensitive adhesive composition for an optical film according to claim 1 , wherein at least one of the (meth)acryl-based copolymers (A) and (B) contains a phosphate group-containing monomer as a monomer unit.

5. The aqueous dispersion-type pressure-sensitive adhesive composition for an optical film according to claim 4 , wherein a content of the phosphate group-containing monomer is 0.1 to 20% by weight of all monomer units in the (meth)acryl-based copolymer (A) or (B).

6. The aqueous dispersion-type pressure-sensitive adhesive composition for an optical film according to claim 1 , wherein the emulsion particles of a core-shell structure are obtained by a process comprising performing emulsion polymerization of monomers for monomer units of the copolymer for the core layer to form the copolymer for the core layer and then performing emulsion polymerization of monomers for monomer units of the copolymer for the shell layer to form the copolymer for the shell layer.

7. A pressure-sensitive adhesive layer for an optical film obtained by a process comprising applying the aqueous dispersion-type pressure-sensitive adhesive composition for an optical film according to claim 1 to a substrate and then drying the composition.

8. The pressure-sensitive adhesive layer for an optical film according to claim 7 , which has a haze (H20) of 0 to 1% when having a thickness of 20 μm.

9. The pressure-sensitive adhesive layer for an optical film according to claim 8 , which has a ratio of a haze (H200) to the haze (H20) of 2 or less, wherein the haze (H200) is a haze of the pressure-sensitive adhesive layer with a thickness of 200 μm.

10. A pressure-sensitive adhesive optical film, comprising an optical film and the pressure-sensitive adhesive layer for an optical film according to claim 7 placed on at least one side of the optical film.

11. The pressure-sensitive adhesive optical film according to claim 10 , wherein the optical film is a polarizing plate comprising a polarizer and a transparent protective film or films provided on one or both sides of the polarizer.

12. The pressure-sensitive adhesive optical film according to claim 11 , wherein the polarizer has a thickness of 10 μm or less.

13. An image display device comprising at least one piece of the pressure-sensitive adhesive optical film according to claim 10 .

14. The aqueous dispersion-type pressure-sensitive adhesive composition for an optical film according to claim 1 , wherein the difference of the glass transition temperatures between the (meth) acryl-based copolymers (A) and (B) is 100° C. or more.

15. The aqueous dispersion-type pressure-sensitive adhesive composition for an optical film according to claim 1 , wherein the alkyl (meth)acrylate is selected from a group consisting of methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, n-butyl (meth) acrylate, tert-butyl (meth) acrylate, n-hexyl (meth) acrylate, cyclohexyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, n-octyl (meth) acrylate, lauryl (meth) acrylate, tridecyl (meth) acrylate and stearyl (meth) acrylate.

16. A method of producing the aqueous dispersion-type pressure-sensitive adhesive composition for an optical film according to claim 1 , comprising the steps of:
performing emulsion polymerization of monomers for monomer units of a copolymer for a core layer to form the copolymer for the core layer; and
then performing emulsion polymerization of monomers for monomer units of a copolymer for a shell layer to form the copolymer for the shell layer, so that emulsion particles of a core-shell structure are produced in such a manner that a single emulsion particle includes the copolymer for the core layer and the copolymer for the shell layer, wherein
one of the copolymers for the core layer and the shell layer is a (meth)acryl-based copolymer (A) containing an alkyl (meth)acrylate as a monomer unit and having a glass transition temperature of −55° C. to 0° C. (wherein the glass transition temperature is calculated based on monofunctional monomers for monomer units),
another of the copolymers for the core layer and the shell layer is a (meth)acryl-based copolymer (B) containing an alkyl (meth)acrylate as a monomer unit and having a glass transition temperature of 0° C. to 180° C. (wherein the glass transition temperature is calculated based on monofunctional monomers for monomer units),
at least one of the (meth)acryl-based copolymers (A) and (B) contains a carboxyl group-containing monomer as a monomer unit,
a difference of the glass transition temperatures between the (meth)acryl-based copolymers (A) and (B) is 50° C. or more, and
a ratio (A)/(B) (by weight) of the (meth)acryl-based copolymers (A) and (B) is in the range of 50/50 to 90/10.

Assignees

• Inui Kunihiro
• Hosokawa Toshitsugu
• Ishii Takaaki
• Satake Masayuki
• Okada Kenichi
• Takahashi Toshitaka
• Makihata Yousuke
• Shimokuri Taiki
• Goto Shusaku
• Kitagawa Takeharu
• Miyatake Minoru
• Mori Tomohiro
• Kamijo Takashi
• Nitto Denko Corp

Inventors

• Inui Kunihiro
• Hosokawa Toshitsugu
• Ishii Takaaki
• Satake Masayuki
• Okada Kenichi
• Takahashi Toshitaka
• Makihata Yousuke
• Shimokuri Taiki
• Goto Shusaku
• Kitagawa Takeharu
• Miyatake Minoru
• Mori Tomohiro
• Kamijo Takashi

Classifications

• G02F2202/28

  Adhesive materials or arrangements · CPC title

• Y10T428/265

  1 mil or less · CPC title

• Y10T428/2891

  including addition polymer from alpha-beta unsaturated carboxylic acid [e.g., acrylic acid, methacrylic acid, etc.] Or derivative thereof · CPC title

• C09J151/06 Primary

  grafted on to homopolymers or copolymers of aliphatic hydrocarbons containing only one carbon-to-carbon double bond · CPC title

• Y10T428/2848

  Three or more layers · CPC title