One-part polyurethane adhesive with high green strength

Patent metadata

Field	Value
Publication number	US-10253227-B2
Application number	US-201615767670-A
Country	US
Kind code	B2
Filing date	Dec 16, 2016
Priority date	Dec 18, 2015
Publication date	Apr 9, 2019
Grant date	Apr 9, 2019

Abstract

A one-part polyurethane composition includes the reaction product of at least one polyether polyol PO, at least one thermoplastic polyester polyol PE, at least one hydrophobic polyol PH, and at least one polyisocyanate PI, preferably methylene diphenyl diisocyanate (MDI), wherein the composition has a remaining isocyanate content of between 0.8 and 3.5 wt.-%, preferably between 1.4 to 1.8 wt.-%, based on the total weight of the isocyanate-functional polymers comprised therein, and wherein said polyether polyol PO includes a bifunctional polyether polyol PO1 and a trifunctional polyether polyol PO2 and wherein said hydrophobic polyol PH is a polyester polyol based on fatty acids. The inventive one-component composition exhibits high green strength and long open time, as well as high storage stability. It is especially suitable as adhesive, in particular for automotive windshields and is preferably applied warm.

First claim

The invention claimed is:

1. One-part polyurethane composition, comprising the reaction product of
A) at least one polyether polyol PO;
B) at least one thermoplastic polyester polyol PE;
C) at least one hydrophobic polyol PH;
D) at least one polyisocyanate PI;
wherein the composition has a remaining isocyanate content of between 0.8 and 3.5 wt.-%, based on the total weight of the isocyanate-functional polymers comprised therein,
wherein said polyether polyol PO comprises a bifunctional polyether polyol PO1 and a trifunctional polyether polyol PO2 and wherein said hydrophobic polyol PH is a polyester polyol based on fatty acids.

2. One-part polyurethane composition according to claim 1 , wherein said polyester polyol PE comprises poly(1,6-hexamethylene adipate).

3. One-part polyurethane composition according to claim 1 , wherein said hydrophobic polyol PH has an OH value of 30 to 75 mg KOH/g.

4. One-part polyurethane composition according to claim 1 , wherein said hydrophobic polyol PH has a viscosity at 25° C. according to ASTM D4878-15 of between 5 Pa s and 150Pa s.

5. One-part polyurethane composition according to claim 1 , wherein the composition further comprises
E) at least one catalyst K for curing isocyanate-functional polyurethanes;
F) at least one filler F;
G) optionally a thixotropy additive TX;
H) optionally at least one plasticizer.

6. One-part polyurethane composition according to claim 5 , wherein said thixotropy additive TX is the reaction product of MDI and N-butylamine, suspended in a plasticizer, and wherein said thixotropy additive TX is essentially free of isocyanate groups.

7. Method of manufacturing a one-part polyurethane composition according to claim 5 , at least comprising the steps of
a) mixing polyester polyol PE, difunctional polyether polyol PO1, and parts of polyisocyanate PI to form an isocyanate-functional prepolymer PR;
b) mixing trifunctional polyether polyol PO2, hydrophobic polyol PH, and the rest of polyisocyanate PI;
c) adding filler and optionally thixotropy additive TH;
d) adding prepolymer PR prepared under step a);
e) adding catalyst for curing isocyanate-functional polyurethanes;
wherein all steps optionally include the addition of plasticizer, heating, cooling, and/or use of vacuum or inert gas.

8. A method comprising applying a one-part polyurethane composition according to claim 1 as an adhesive or sealant.

9. A method according to claim 8 , wherein the one-part polyurethane composition is used as an adhesive for glass, metal, or ceramic frit substrates.

10. A method according to claim 8 , wherein the one-part polyurethane composition is heated to an application temperature of between 30° C. and 120° C.

11. A method according to claim 8 , wherein the one-part polyurethane composition is used to bond a window or windshield to a building or vehicle.

12. Cured one-part polyurethane composition according to claim 1 .

13. Manufacturing product comprising a one-part polyurethane composition according to claim 1 .

Assignees

• Sika Tech Ag

Inventors

• Yao Hong

Classifications

• C08G18/163

  covered by C08G18/18 and C08G18/22 · CPC title

• C08G18/12

  using two or more compounds having active hydrogen in the first polymerisation step · CPC title

• C08G18/2018

  having one nitrogen atom in the ring · CPC title

• C09J175/04 Primary

  Polyurethanes · CPC title

• C08G18/2081

  containing at least two non-condensed heterocyclic rings · CPC title