Optical film and method for manufacturing same, polarization plate, and liquid crystal display apparatus

Patent metadata

Field	Value
Publication number	US-10240033-B2
Application number	US-201514642993-A
Country	US
Kind code	B2
Filing date	Mar 10, 2015
Priority date	Sep 28, 2012
Publication date	Mar 26, 2019
Grant date	Mar 26, 2019

Abstract

The optical film of the present invention is an optical film including a thermoplastic resin, in which the optical film has a moisture permeability of 70 g/m2/day or less (in terms of a film thickness of 40 μm), and contains a moisture permeability-reducing compound having a molecular weight of 200 or more and satisfying Formula (1) described below. Formula (1) A/B≤0.9 (A represents a moisture permeability of an optical film in a case in which 10 mass % of the moisture permeability-reducing compound is added to the mass of the thermoplastic resin, and B represents a moisture permeability of an optical film in a case in which the thermoplastic resin is included and the moisture permeability-reducing compound is not added.)

First claim

What is claimed is:

1. An optical film including a thermoplastic resin,
wherein the optical film has a moisture permeability of 70 g/m 2 /day or less, and
contains a moisture permeability-reducing compound having a molecular weight of 200 or more and satisfying Formula (1) described below,
wherein the moisture permeability-reducing compound is a compound represented by General Formula (B) described below, a phenolic resin represented by General Formula (C) described below, a terpene resin, an aromatic hydrocarbon formaldehyde resin, or barbituric acid;
A/B≤ 9  Formula (1)

in Formula (1), A represents a moisture permeability of an optical film in a case in which 10 mass % of the moisture permeability-reducing compound is added to the mass of the thermoplastic resin, B represents a moisture permeability of an optical film in a case in which the thermoplastic resin is included and the moisture permeability-reducing compound is not added,
with the proviso that the moisture permeability is a moisture permeability in terms of a film thickness of 40 μm of the optical film after 24 hours at 40° C. under a relative humidity of 90% using a method of JIS Z-0208,

in General Formula (B), each of R 12 , R 13 , R 14 , R 15 , R 16 , R 21 , R 23 , R 24 , R 25 , R 32 , R 33 , R 34 , R 35 , and R 36 independently represents a hydrogen atom or a substituent, and at least one of R 12 , R 13 , R 14 , R 15 , R 16 , R 21 , R 23 , R 24 , R 25 , R 32 , R 33 , R 34 , R 35 , and R 36 is an amino group, an acylamino group, an alkoxycarbonylamino group, an aryloxycarbonylamino group, a sulfonylamino group, a hydroxyl group, a mercapto group, or a carboxyl group, and

in General Formula (C), n represents 1 to 10, each of ms independently represents an integer of 1 to 4, each of Rs independently represents a hydrogen atom, a —OH group, or an alkyl group having 1 to 10 carbon atoms which may have a substituent, at least one of Rs represents a group having a —OH group, and each of L 1 and L 2 independently represents a methylene group or —CH 2 —O—CH 2 —.

2. The optical film according to claim 1 ,
wherein Formula (2) described below is satisfied,
a/B≤ 0.9  Formula (2)

in Formula (2), a represents a moisture permeability of an optical film in a case in which the thermoplastic resin and the moisture permeability-reducing compound are included, B represents a moisture permeability of an optical film in a case in which the thermoplastic resin is included and the moisture permeability-reducing compound is not added;
the moisture permeability is a moisture permeability in terms of a film thickness of 40 μm of the optical film after 24 hours at 40° C. under a relative humidity of 90% using the method of JIS Z-0208.

3. The optical film according to claim 1 ,
wherein the moisture permeability-reducing compound is a novolac-type phenolic resin, a hydrogenated terpene resin, a xylene resin, or barbituric acid.

4. The optical film according to claim 1 ,
wherein the moisture permeability-reducing compound is a novolac-type phenolic resin, a hydrogenated terpene resin, or a xylene resin.

5. The optical film according to claim 1 ,
wherein the moisture permeability-reducing compound has three or more aromatic rings.

6. The optical film according to claim 1 ,
wherein the moisture permeability-reducing compound is represented by General Formula (C) described below,

in General Formula (C), n represents 1 to 10, each of ms independently represents an integer of 1 to 4, each of Rs independently represents a hydrogen atom, a —OH group, or an alkyl group having 1 to 10 carbon atoms which may have a substituent, at least one of Rs represents a group having a —OH group, and each of L 1 and L 2 independently represents a methylene group or —CH 2 —O—CH 2 —.

7. The optical film according to claim 1 ,
wherein the moisture permeability-reducing compound is a novolac-type phenolic resin or a xylene resin.

8. The optical film according to claim 1 , comprising:
1 mass % or more of the moisture permeability-reducing compound with respect to the mass of the thermoplastic resin.

9. The optical film according to claim 1 ,
wherein the film thickness is 60 μm or less.

10. The optical film according to claim 1 ,
wherein Re and Rth defined by Formula (I) described below and Formula (II) described below satisfy Formula (III) described below and Formula (IV) described below at a wavelength of 590 nm,
Re =( nx−ny )× d   Formula (I)

Rth ={( nx+ny )/2 −nz}×d   Formula (II)

| Re|≤ 50 nm  Formula (III)

| Rth|≤ 300 nm  Formula (IV)

in Formulae (I) to (IV), nx is a refractive index in an in-plane slow axis direction of the optical film, ny is a refractive index in an in-plane fast axis direction of the optical film, nz is a refractive index in a thickness direction of the optical film, and d is a thickness, of which unit is nm, of the optical film.

11. The optical film according to claim 1 ,
wherein the optical film is manufactured by casting a macromolecular solution including the thermoplastic resin, the moisture permeability-reducing compound, and a solvent on a support.

12. The optical film according to claim 1 ,
wherein a functional layer having a film thickness in a range of 0.1 μm to 20 μm is present on at least one surface of the optical film.

13. The optical film according to claim 12 ,
wherein a moisture permeability (C) of the optical film in a case in which the functional layer is laminated and a moisture permeability (D) of just the optical film in a case in which the functional layer is not laminated satisfy C/D≤0.9.

14. A polarization plate comprising:
at least one of the optical film according to claim 1 as a protective film for a polarizer.

15. A liquid crystal display apparatus comprising:
a liquid crystal cell; and
the polarization plate according to claim 14 disposed in at least one side of the liquid crystal cell,
wherein the optical film is disposed so as to serve as an outermost layer.

16. The optical film according to claim 1 ,
wherein the phenolic resin is a novolac-type phenolic resin represented by General Formula (1) described below,

in General Formula (1), n represents 1 to 10 on the average, and each of Rs independently represents a hydrogen atom or an alkyl group having 1 to 10 carbon atoms.

17. The optical film according to claim 1 ,
wherein the moisture permeability-reducing compound is the compound represented by General Formula (B), a terpene resin, an aromatic hydrocarbon formaldehyde resin, or barbituric acid.

18. The optical film according to claim 1 ,
wherein the moisture permeability-reducing compound is the compound represented by General Formula (B), the phenolic resin represented by General Formula (C), a hydrogenated terpene resin, an aromatic hydrocarbon formaldehyde resin, or barbituric acid.

19. The optical film according to claim 1 ,
wherein the moisture permeability-reducing compound is the compound represented by General Formula (B), a hydrogenated terpene resin, an aromatic hydrocarbon formaldehyde resin, or barbituric acid.

Assignees

• Fujifilm Corp

Inventors

• Nimura Shigeaki
• Kamo Makoto
• Arita Shusuke
• Nozoe Yutaka
• Sasata Katsumi

Classifications

• C08K5/3462

  Six-membered rings · CPC title

• C08K5/13

  Phenols; Phenolates · CPC title

• Y10T428/1036

  Cross-Sectional Technologies · mapped topic

• B29D11/00644

  polarizing · CPC title

• B29K2995/0018

  having particular optical properties, e.g. fluorescent or phosphorescent · CPC title