Photocatalyst functional film and method for producing the same

Patent metadata

Field	Value
Publication number	US-10220372-B2
Application number	US-201515329785-A
Country	US
Kind code	B2
Filing date	Jul 31, 2015
Priority date	Aug 6, 2014
Publication date	Mar 5, 2019
Grant date	Mar 5, 2019

Abstract

A photocatalytic functional film has a structure of a substrate, a barrier layer and a photocatalytic layer stacked one on another. The barrier layer is an amorphous TiO2 film, the photocatalyst layer comprises an amorphous TiO2 film, and particles of visible light responsive photocatalytic material formed on the surface of the amorphous TiO2 film. A method for producing a photocatalytic functional film includes: adding an alcohol solvent and an acid to a titanium precursor to obtain a TiO2 amorphous sol by dehydration and de-alcoholization reaction; applying and drying the TiO2 amorphous sol on a substrate to form a barrier layer; and applying and drying a composition formed by mixing particles of visible light responsive photocatalyst material with the TiO2 amorphous sol on the barrier layer, to form a photocatalyst layer.

First claim

What is claimed is:

1. A photocatalytic functional film having a structure of a substrate, a barrier layer and a photocatalytic layer stacked one on another,
wherein the barrier layer is an amorphous TiO 2 film,
wherein the photocatalyst layer is an amorphous TiO 2 film comprising particles of visible light responsive photocatalytic material,
wherein the particles of the visible light responsive photocatalyst material are porous metal oxide particles carrying a visible light activating metal in the pores, and
wherein the porous metal oxide particles comprise at least one selected from the group consisting of tungsten oxide, zinc oxide, and niobium oxide.

2. The photocatalytic functional film according to claim 1 , wherein the amorphous TiO 2 films have a porosity of 5% to 50%.

3. The photocatalytic functional film according to claim 1 , wherein the amorphous TiO 2 films have a specific surface area of 5 m 2 /g to 500 m 2 /g.

4. The photocatalytic functional film according to claim 1 , wherein the amorphous TiO 2 films are dried materials of a TiO 2 amorphous sol.

5. The photocatalytic functional film according to claim 1 , wherein the porous metal oxide particles carry the visible light activating metal as a visible light-activating metal or an oxide thereof, wherein the visible light activating metal comprises at least one of tungsten, chromium, vanadium, molybdenum, copper, iron, cobalt, manganese, nickel, platinum, gold, cerium, cadmium, zinc, magnesium, calcium, strontium, barium, or a combination thereof.

6. The photocatalytic functional film according to claim 1 , wherein a weight ratio of the porous metal oxide and a sum of the visible light activating metal and a visible light activating metal oxide in the particles of the visible light responsive photocatalyst material ranges from 99.9:0.1 to 99:1.

7. The photocatalytic functional film according to claim 1 , wherein a thickness of the barrier layer ranges from 20 nm to 500 nm.

8. The photocatalytic functional film according to claim 1 , wherein a thickness of the photocatalytic layer ranges from 50 nm to 500 nm.

9. The photocatalytic functional film according to claim 1 , wherein the substrate is an indoor interior material.

10. A method for producing a photocatalytic functional film, comprising:
adding an alcohol solvent and an acid to a titanium precursor to obtain a TiO 2 amorphous sol by dehydration and de-alcoholization reaction;
applying and drying the TiO 2 amorphous sol on a substrate to form a barrier layer; and
applying and drying a composition formed by mixing particles of visible light responsive photocatalyst material with the TiO 2 amorphous sol on the barrier layer, to form a photocatalyst layer,
wherein the photocatalytic layer is an amorphous TiO 2 film comprising particles of visible light responsive photocatalytic material,
wherein the particles of the visible light responsive photocatalyst material are porous metal oxide particles carrying a visible light activating metal in the pores, and
wherein the porous metal oxide particles comprise at least one selected from the group consisting of tungsten oxide, zinc oxide, and niobium oxide.

11. The method according to claim 10 , wherein the alcohol solvent is at least one selected from a group consisting of isopropyl alcohol, ethanol, methanol, butanol, and a combination thereof.

12. The method according to claim 10 , wherein the composition comprises 20 parts by weight of the TiO 2 amorphous sol with respect to 100 parts by weight of the particles of the visible light responsive photocatalyst material.

Assignees

• Lg Hausys Ltd

Inventors

• Lee Dong-Il
• Seo Joo-Hwan
• Kim Hyun-Jae
• Jang Hye-Youn
• Jung Seong-Moon

Classifications

• B01J37/0244

  Coatings comprising several layers · CPC title

• B01J23/06

  of zinc, cadmium or mercury · CPC title

• B01J23/28

  Molybdenum · CPC title

• B01J23/002

  Mixed oxides other than spinels, e.g. perovskite · CPC title

• B01J23/687

  with tungsten · CPC title