Two-component coating compositions and coatings produced therefrom for improving erosion resistance

Patent metadata

Field	Value
Publication number	US-10214660-B2
Application number	US-201615548612-A
Country	US
Kind code	B2
Filing date	Jan 14, 2016
Priority date	Feb 10, 2015
Publication date	Feb 26, 2019
Grant date	Feb 26, 2019

Abstract

A two-component coating composition contains (1) a paint base component comprising (A) at least one polycarbonate diol, (B) at least one hydroxyl-containing acrylate resin, polyester resin and/or polyester acrylate resin having a hydroxyl number of 75 to 500 mg KOH/g, and (C) at least one filler modified with at least one organosilane, and (2) a hardener component comprising (D) at least one organic polyisocyanate, where the coating composition has a viscosity of 50 to 2000 mPa·s at a shear stress of 1000 l/s and a temperature of 23° C. and a proportion of organic solvents of 100 to 350 g/L.

First claim

The invention claimed is:

1. A solvent-based two-component coating composition, comprising
(1) a paint base component comprising
(A) at least one polycarbonate diol,
(B) at least one hydroxyl-containing acrylate resin, polyester resin and/or polyester acrylate resin having a hydroxyl number of 75 to 500 mg KOH/g, and
(C) at least one filler modified with at least one organosilane, and

(2) a hardener component comprising
(D) at least one organic polyisocyanate,

wherein the coating composition has a viscosity of 50 to 2000 mPa·s at a shear stress of 1000 l/s and a temperature of 23° C. and a proportion of organic solvents of 100 to 350 g/L.

2. The two-component coating composition as claimed in claim 1 , wherein said at least one polycarbonate diol (A) has a hydroxyl number of 50 to 500 mg KOH/g.

3. The two-component coating composition as claimed in claim 1 , wherein said at least one polycarbonate diol (A) is an aliphatic and linear polycarbonate diol.

4. The two-component coating composition as claimed in claim 1 , wherein said at least one acrylate resin, polyester resin and/or polyester acrylate resin (B) has a hydroxyl number of 175 to 400 mg KOH/g.

5. The two-component coating composition as claimed in claim 1 , wherein said at least one filler (C) modified with at least one organosilane is selected from the group consisting of the silicates modified with at least one organosilane.

6. The two-component coating composition as claimed in claim 1 , wherein said filler (C) modified with at least one organosilane is preparable by modification of an inorganic filler with organosilanes of the formula (I)
X 4−n−m Si—R n (-A-B) m   (I)

wherein
X=OH, halogen, alkoxy, aryloxy,
R=alkyl, phenyl or H,
A=divalent organic radical,
B=amino, hydroxyl, epoxy, epoxypropyloxy, hydroxyalkyl, acetoxy, isocyanate, acryloyloxy, methacryloyloxy, imidazole, ureido, vinyl group, and
n, m=0, 1, 2, 3, with n+m≤3.

7. The two-component coating composition as claimed in claim 1 , wherein said at least one organic polyisocyanate has an isocyanate content of 16% to 24%.

8. The two-component coating composition as claimed in claim 1 , wherein said at least one organic polyisocyanate is an isocyanurate of hexamethylene diisocyanate.

9. The two-component coating composition as claimed in claim 1 , which has a proportion of organic solvents of 150 to 300 g/L.

10. The two-component coating composition as claimed in claim 1 , which has a viscosity of 1000 to 10 000 mPa·s at a shear stress of 1 l/s and a temperature of 23° C., with the proviso that the viscosity at 1 l/s, 23° C. is a factor of 4 to 20 higher than the viscosity of the coating composition at a shear stress of 1000 l/s, 23° C.

11. A method for producing a coating on a substrate, comprising:
spraying applying of a coating composition as claimed in claim 1 to a substrate.

12. The method as claimed in claim 11 , wherein the coating produced by application is cured at a temperature of not more than 80° C.

13. A coating obtained by a method as claimed in claim 11 .

14. A multicoat coating which comprises as topcoat a coating as claimed in claim 13 .

15. A method for improving the erosion resistance of a substrate, said method comprising:
spray applying of a coating composition as claimed in claim 1 to the substrate, to obtain a coated substrate;
wherein the erosion resistance of the coated substrate is improved compared to the same substrate having no coating.

Assignees

• Basf Coatings Gmbh

Inventors

• Seeger Dirk
• Mueller Harald
• MEYERJUERGENS Andreas
• Kaune Martin

Classifications

• B05D1/02

  performed by spraying · CPC title

• C09D175/06 Primary

  from polyesters · CPC title

• C08G18/4063

  Mixtures of compounds of group C08G18/62 with other macromolecular compounds · CPC title

• F05B2260/95

  Preventing corrosion · CPC title

• F05B2230/90

  Coating; Surface treatment · CPC title