Adhesion promoters for aqueous coating compositions

Patent metadata

Field	Value
Publication number	US-10208148-B2
Application number	US-201515312415-A
Country	US
Kind code	B2
Filing date	Mar 26, 2015
Priority date	May 20, 2014
Publication date	Feb 19, 2019
Grant date	Feb 19, 2019

Abstract

The present invention relates to a copolymer obtainable by copolymerization of at least three ethylenically unsaturated monomers each different from one another, the copolymer having at least three structural units (S1) and (S2) and (S3) different from one another, to the use of this copolymer as an adhesion-promoting additive in an aqueous coating composition, to an aqueous coating composition comprising at least one polymeric resin (A1), at least one pigment (B), and at least one copolymer of the invention, used as adhesion-promoting additive, as component (C), and also to methods for at least partly coating a substrate with a basecoat and for at least partly coating a substrate with a multicoat paint system.

First claim

What is claimed is:

1. A copolymer obtained by copolymerization of at least three ethylenically unsaturated monomers each different from one another,
wherein
the copolymer has at least three structural units (S1), (S2), and (S3) each different from one another,
each structural unit (S1) has at least one branched alkyl group having at least 11 carbon atoms,
each structural unit (S2) has at least one urea group bonded via a C 1-10 alkylene group, of the formula (I):

wherein:
X is O or S,
A is a C 1-10 alkylene group, and
R 1 , R 2 and R 3 each independently of one another are H or a C 1-10 alkyl radical,
or
R 1 and R 2 together are —(CR 4 R 5 ) n — and R 3 is H or a C 1-10 alkyl radical, where R 4 and R 5 each independently of one another are H or a C 1-6 alkyl radical, and n is an integer from 2 to 5, and

each structural unit (S3) has at least one functional group selected from the group consisting of a carboxyl group, hydroxyl group, thiol group, amino group, epoxide group, and a mixture thereof.

2. The copolymer of claim 1 , wherein the structural units (S1), (S2), and (S3) are introduced into the copolymer by copolymerization of monomers which each independently of one another have at least one (meth)acryloyl group as an ethylenically unsaturated group.

3. The copolymer of claim 1 ,
wherein
each structural unit (S1) has at least one branched alkyl group having at least 13 carbon atoms,
each structural unit (S2) has at least one urea group bonded via a C 1-6 alkylene group, of the formula (I):

wherein:
X is O or S,
A is a C 1-6 alkylene group, and
R 1 and R 2 together are —(CR 4 R 5 ) n — and R 3 is H or a C 1-6 alkyl radical, where R 4 and R 5 each independently of one another are H or a C 1-6 alkyl radical, and n is an integer from 2 to 5, and

each structural unit (S3) has at least one functional group selected from the group consisting of a carboxyl group, hydroxyl group, and a mixture thereof.

4. The copolymer in of claim 1 , wherein the copolymer has at least one further structural unit (S4) different from (S1), (S2), and (S3),
wherein each structural unit (S4) has at least one group selected from the group consisting of a branched and unbranched C 1-10 alkyl group, a C 3-10 cycloalkyl group optionally substituted by at least one C 1-6 alkyl group, an aromatic group optionally substituted by at least one C 1-6 alkyl group, an aromatic group bonded via a C 1-6 alkylene group and optionally substituted by at least one C 1-6 alkyl group, and a C 3-10 cycloalkyl group bonded via a C 1-6 alkylene group and optionally substituted by at least one C 1-6 alkyl group.

5. The copolymer of claim 4 , wherein the copolymer is obtained by radical copolymerization of
(s1) at least one ethylenically unsaturated monomer capable of forming the structural unit (S1), in an amount in a range from 0.5 to 15 mol %, based on the total amount in mol % of all monomers used for preparing the copolymer,
(s2) at least one ethylenically unsaturated monomer capable of forming the structural unit (S2), in an amount in a range from 0.5 to 15 mol %, based on the total amount in mol % of all monomers used for preparing the copolymer,
(s3) at least one ethylenically unsaturated monomer capable of forming the structural unit (S3), in an amount in a range from 5 to 50 mol %, based on the total amount in mol % of all monomers used for preparing the copolymer, and
(s4) at least one ethylenically unsaturated monomer capable of forming the structural unit (S4), in an amount in a range from 20 to 90 mol %, based on the total amount in mol % of all monomers used for preparing the copolymer,
with the total amount of all monomers (s1), (s2), (s3), and (s4) used for preparing the copolymer adding up in total to 100 mol %.

6. An aqueous coating composition for at least partly coating a substrate with a basecoat, the aqueous coating composition comprising:
at least one polymeric resin (A1) and optionally at least one crosslinking agent (A2),
at least one pigment (B), and
as a component (C), at least one copolymer as in claim 1 , said copolymer is different from the polymeric resin (A1) and is used as adhesion-promoting additive.

7. The aqueous coating composition of claim 6 , wherein the coating composition comprises from 0.5 to 15 wt % of the copolymer (C), based on the total solids fraction of the coating composition.

8. The aqueous coating composition of claim 6 , wherein
the polymeric resin (A1) is selected from the group consisting of a polyurethane, polyester, epoxy resin, poly(meth)acrylate, each having at least one functional hydroxyl group, and a mixture thereof, and
the optionally present crosslinking agent (A2) comprises at least one optionally alkylated melamine-formaldehyde condensation product and/or at least one blocked polyisocyanate.

9. The aqueous coating composition of claim 6 , wherein the coating composition comprises:
from 7.5 to 30 wt % of the at least one polymeric resin (A1), based on the total weight of the coating composition,
from 2.5 to 15 wt % of the at least one crosslinking agent (A2), based on the total weight of the coating composition, and
from 0.5 to 20 wt % of the at least one pigment (B), based on the total weight of the coating composition, and
wherein an amount of water, (A1), (A2), (B), and (C) components present in the coating composition, and of optionally present at least one of an additive (D) and an organic solvent add up in total to 100 wt %.

10. A method for at least partly coating a substrate with a basecoat, the method comprising:
at least partly contacting the substrate with the aqueous coating composition of claim 6 .

11. A basecoat present at least partly on a substrate, obtained by the method of claim 10 .

12. A substrate coated at least partly with an aqueous coating composition, obtained by the method of claim 10 .

13. A method for at least partly coating a substrate with a multicoat paint system, the method comprising:
(1) at least partly contacting the substrate with the aqueous coating composition of claim 6 for at least partly forming a basecoat on the substrate, and
(2) applying a clearcoat to the basecoat formed in (1).

14. A multicoat paint system present at least partly on a substrate, obtained by the method of claim 13 .

15. A substrate coated at least partly with a multicoat paint system, obtained by the method of claim 13 .

16. A substrate coated at least partly with the aqueous coating composition of claim 6 .

17. The method as claimed in claim 10 , wherein the substrate comprises at least one plastic.

18. The substrate as claimed in claim 12 , which comprises at least one plastic.

19. The method as claimed in claim 13 , wherein the substrate comprises at least one plastic.

20. The substrate as claimed in claim 15 , which comprises at least one plastic.

Assignees

• Basf Coatings Gmbh

Inventors

• Corten Cathrin
• Andersen Audree
• Saedler Markus
• Boshe-Plois Stefanie
• Foelling Frederik
• Misske Andrea

Classifications

• C08F212/08

  Styrene · CPC title

• C08F220/1804

  C4-(meth)acrylate, e.g. butyl (meth)acrylate, isobutyl (meth)acrylate or tert-butyl (meth)acrylate · CPC title

• C08F2800/20

  as weight or mass percentages · CPC title

• C09D17/001

  in aqueous medium (C09D17/003, C09D17/004 take precedence) · CPC title

• C09D175/04

  Polyurethanes · CPC title