Mechanical processing of reactive laminates

Patent metadata

Field	Value
Publication number	US-10207322-B2
Application number	US-201514918272-A
Country	US
Kind code	B2
Filing date	Oct 20, 2015
Priority date	Oct 23, 2009
Publication date	Feb 19, 2019
Grant date	Feb 19, 2019

Abstract

A method of producing a reactive powder includes providing a bulk structure of reactive material comprising a first reactant and a second reactant, the bulk structure having a preselected average spacing between the first and the second reactants; and mechanically processing the bulk structure of reactive material to produce a plurality of particles from the bulk structure such that each of the plurality of particles comprises the first and second reactants having an average spacing that is substantially equal to the preselected average spacing of the bulk structure of reactive material. The first and second materials of the plurality of particles react with each other in an exothermic reaction upon being exposed to a threshold energy to initiate the exothermic reaction and remain substantially stable without reacting with each other prior to being exposed to the threshold energy.

First claim

We claim:

1. A reactive powder produced according to a method comprising:
providing a bulk structure of reactive material comprising a first reactant and a second reactant, said bulk structure having an average spacing between said first and said second reactants less than about 5.0 μm; and
mechanically processing said bulk structure of reactive material to produce a plurality of particles from said bulk structure such that each of said plurality of particles comprises said first and second reactants having an average spacing that is substantially equal to said average spacing of said bulk structure of reactive material,
wherein said first and second reactants of said plurality of particles react with each other in an exothermic reaction upon being exposed to a threshold energy to initiate said exothermic reaction and remain substantially stable without reacting with each other prior to being exposed to said threshold energy, and
wherein the bulk structure of reactive material has at least ten alternating layers of first and second layers, wherein the first layer in the alternating layers comprises the first reactant and the second layer in the alternating layers comprises the second reactant.

2. A reactive material comprising:
a plurality of reactive particles each of which is at least one of fused with or adhered to at least one adjacent reactive particle of said plurality of reactive particles to form a self-supporting structure,
wherein each reactive particle of said plurality of reactive particles comprises a first reactant and a second reactant having corresponding reactant spacing substantially equal to a reactant spacing less than about 5.0 μm, and
wherein said first and second reactants react with each other in an exothermic reaction upon being exposed to a threshold energy to initiate said exothermic reaction and remain substantially stable without reacting with each other prior to being exposed to said threshold energy, and
wherein each reactive particle of said plurality of reactive particles comprises at least ten alternating layers of said first and second reactants.

3. A reactive material according to claim 2 , wherein said preselected reactant spacing is at least 20 nm and less than 1.0 μm.

4. A reactive material according to claim 2 , wherein an ensemble average of a minimum dimension of said plurality of reactive particles is less than about 1 mm.

5. A reactive material according to claim 2 , wherein an ensemble average of a minimum dimension of said plurality of reactive particles is at least 2.0 μm and less than about 1 mm.

6. A reactive material according to claim 2 , wherein an ensemble average of a minimum dimension of said plurality of reactive particles is at least 150 μm and less than about 212 μm.

7. A reactive material according to claim 2 , wherein an ensemble average of a minimum dimension of said plurality of reactive particles is at least 53 μm and less than about 106 μm.

8. A reactive material according to claim 2 , wherein an ensemble average of a minimum dimension of said plurality of reactive particles is at least 38 μm and less than about 43 μm.

9. A reactive material according to claim 2 , further comprising a plurality of particles of a third material each of which is adhered to at least one of said plurality of reactive particles.

10. A reactive material according to claim 9 , wherein said plurality of particles of said third material comprise at least one of a solder, a fuel and a high-density material having a density greater than about 11 g/cm 3.

11. A reactive material according to claim 10 , wherein said high-density material is selected from the group consisting of W, Ta, Pb, Re, Os, Ir, Pt, Hf, Au and combinations thereof.

12. A reactive material according to claim 10 , wherein said fuel is selected from the group consisting of Al, Zr, Ti, Al—Mg, Si, B, C and combinations thereof.

13. A reactive material according to claim 2 , wherein said first reactant is selected from the group consisting of Ti, Zr, and Hf, and said second reactant is B.

14. A reactive material comprising:
a plurality of reactive particles each of which is at least one of fused with or adhered to at least one adjacent reactive particle of said plurality of reactive particles to form a self-supporting structure,
wherein each reactive particle of said plurality of reactive particles comprises a first reactant and a second reactant having corresponding reactant spacing, and
wherein said first and second reactants react with each other in an exothermic reaction upon being exposed to a threshold energy to initiate said exothermic reaction and remain substantially stable without reacting with each other prior to being exposed to said threshold energy,
wherein each reactive particle of said plurality of reactive particles comprises at least ten alternating layers of said first and second reactants.

15. A reactive material according to claim 14 , wherein each reactive particle of said plurality of reactive particles comprises at least one hundred alternating layers of said first and second reactants.

16. A reactive material according to claim 14 , wherein each reactive particle of said plurality of reactive particles comprises at least one thousand alternating layers of said first and second reactants.

17. A reactive material comprising:
a plurality of reactive particles each of which is at least one of fused with or adhered to at least one adjacent reactive particle of said plurality of reactive particles to form a self-supporting structure;
a plurality of particles of a third material each of which is adhered to at least one of said plurality of reactive particles,
wherein each reactive particle of said plurality of reactive particles comprises a first reactant and a second reactant having corresponding reactant spacing, and
wherein said first and second reactants react with each other in an exothermic reaction upon being exposed to a threshold energy to initiate said exothermic reaction and remain substantially stable without reacting with each other prior to being exposed to said threshold energy,
wherein said plurality of particles of said third material comprise at least one of a solder, a fuel and a high-density material having a density greater than about 11 g/cm 3 ,
wherein said solder is an alloy comprising at least one of Pb, Ag, Au, Sn, Cu, In and Sb.

Assignees

• Univ Johns Hopkins

Inventors

• Weihs Timothy P
• Stover Adam

Classifications

• B22F3/23

  involving a self-propagating high-temperature synthesis or reaction sintering step {(making cermets by reaction sintering C22C1/051)} · CPC title

• B23K35/30

  with the principal constituent melting at less than 1550°C · CPC title

• B22F2009/047

  by rolling · CPC title

• B22F3/17

  by forging · CPC title

• Y10T428/2991

  Coated · CPC title