Copper foil for current collector of lithium secondary battery

Patent metadata

Field	Value
Publication number	US-10205170-B1
Application number	US-201715782494-A
Country	US
Kind code	B1
Filing date	Dec 4, 2017
Priority date	Dec 4, 2017
Publication date	Feb 12, 2019
Grant date	Feb 12, 2019

Abstract

Electrodeposited copper foils having adequate puncture strength to withstand both pressure application during consolidation with negative electrode active materials during manufacture, as well as expansion/contraction during repeated charge/discharging cycles when used in a rechargeable secondary battery are described. These copper foils find specific utility as current collectors in rechargeable secondary batteries, particularly in lithium secondary battery with high capacity. Methods of making the copper foils, methods of producing negative electrode for use in lithium secondary battery and lithium secondary battery of high capacity are also described.

First claim

We claim:

1. An electrodeposited copper foil having an area weight of the electrodeposited copper foil is in the range of 26.7-329.4 g/m 2 , and a puncture strength, Y, the puncture strength Y of the electrodeposited copper foil must lie in a range defined between a maximum value, Y1 (in N), and a minimum value, Y2 (in N), wherein the value Y1 is calculated by the following formula 1:
Y 1=−0.00007* X 2 +0.075* X− 1.3373  formula 1:

and the value Y2 is calculated by the following formula 2:
Y 2=0.00003* X 2 +0.0247* X− 0.6454  formula 2:

wherein X in each of formulas 1 and 2 represents the area weight of the electrodeposited copper foil (g/m 2 ), and Y represents the puncture strength of the electrodeposited copper foil (in N).

2. The electrodeposited copper foil of claim 1 , wherein the copper foil has a deposit side and the surface roughness (Rz) of the deposit side is in the range of 0.4-2.0 μm.

3. The electrodeposited copper foil of claim 2 , wherein the number of voids per μm 2 is less than 5.

4. A rechargeable secondary battery comprising the electrodeposited copper foil of claim 1 .

5. The rechargeable secondary battery of claim 4 , wherein the battery is a lithium containing battery.

6. An electrodeposited copper foil having an area weight of the electrodeposited copper foil is in the range of 26.7-329.4 g/m 2 , and a puncture strength Y, the puncture strength of the electrodeposited copper foil is between a maximum value, Y1 (N), and a minimum value, Y2 (N), wherein the value Y1 is calculated by the following formula 1:
Y 1=−0.00007* X 2 +0.075* X− 1.3373  formula 1:

and the value Y2 is calculated by the following formula 2:
Y 2=0.00003* X 2 +0.0247* X− 0.6454  formula 2:

wherein X in each of formulas 1 and 2 represents the area weight of the electrodeposited copper foil (g/m 2 ), and Y represents the puncture strength of the electrodeposited copper foil (N), wherein the copper foil has a drum side and a deposit side, each of said drum side and said deposit side comprising grains having a grain size, wherein the grain size difference between the drum side and the deposit side is in the range of 0.05-0.55 μm.

Assignees

• Chang Chun Petrochemical Co Ltd

Inventors

• Huang Huei-Fang
• Cheng Kuei-Sen
• Lai Yao-Sheng
• Chou Jui-Chang

Classifications

• H01M4/661 Primary

  Metal or alloys, e.g. alloy coatings (H01M4/669 take precedence) · CPC title

• H01M2004/027

  Negative electrodes · CPC title

• C25D3/38

  of copper · CPC title

• H01M2220/20

  Batteries in motive systems, e.g. vehicle, ship, plane · CPC title

• C25D7/0614

  Strips or foils · CPC title