Magnesium alloy with adjustable degradation rate

Patent metadata

Field	Value
Publication number	US-10196715-B2
Application number	US-201715442013-A
Country	US
Kind code	B2
Filing date	Feb 24, 2017
Priority date	Mar 14, 2013
Publication date	Feb 5, 2019
Grant date	Feb 5, 2019

Abstract

An alloy and an implant having a three-dimensional structure based on such alloy. The alloy comprises a MgZnCa alloy containing nanosized precipitates being less noble than the Mg matrix alloy and having a Zn content ranging 0.1 wt. % Zn to 2 wt. % Zn and a calcium content ranging from 0.2 wt. % to 0.5 wt. %, and having less than 0.04 wt. % of one or more other elements with the remainder being Mg. For these micro-alloys, any second phase generated during the solidification process can be completely dissolved by a solution heat treatment. Finely dispersed nanosized precipitates can then be generated by a subsequent aging heat treatment step. These precipitates are used to “pin” the grain boundaries and to prevent the coarsening of the grain structure during further processing to achieve grain sizes below 5 μm.

First claim

What is claimed:

1. A composition comprising:
a MgZnCa alloy containing nanosized precipitates, the alloy having a Zn content ranging from 0.1 wt. % Zn to 2.0 wt. % Zn and a calcium content ranging from 0.2 wt. % Ca to 0.5 wt. % Ca, less than 0.04 wt. % of one or more other elements and with the remainder of the alloy being Mg, wherein the Mg has a purity of at least 99.96 wt. %, and wherein the nanosized precipitates are less noble than the remainder Mg.

2. The composition of claim 1 , wherein the one or more other elements are located in a secondary phase.

3. The composition of claim 2 , wherein the one or more other elements comprise Fe, Cu, Ni, Co, Si, Mn, Al, Zr, P, or any combination thereof.

4. The composition of claim 1 , wherein the alloy is substantially free of microgalvanic elements.

5. The composition of claim 1 , wherein the nanosized precipitates that are less noble than the remainder Mg comprise (Mg,Zn) 2 Ca.

6. The composition of claim 1 , further comprising nanosized precipitates that are more noble than the Mg remainder wherein said precipitates comprise Mg 6 Zn 3 Ca 2.

7. The composition of claim 1 , wherein the alloy has a grain size of less than 5μm.

8. The composition of claim 1 , wherein the alloy has a yield strength of at least 180 MPa.

9. The composition of claim 1 , wherein the alloy has an ultimate tensile strength of at least 240 MPa.

10. The composition of claim 1 , wherein the alloy has at least 10% elongation at break.

11. An implant comprising the composition of claim 1 .

12. The implant of claim 11 , wherein the implant has an in vitro degradation rate of less than 0.5 mg/cm 2 day as measured in a simulated body fluid.

13. The implant of claim 11 , wherein the implant is an orthopedic implant.

14. The implant of claim 13 , wherein the orthopedic implant comprises a nail, a screw, a staple, a plate, a rod, a tack, a bolt, a bolt to lock and IM nail, an anchor, a dowel, a plug, a peg, a sleeve, a mesh, a transconnector, a nut, a shaped body, a spinal cage, a wire, a K-wire, a woven structure, a clamp, a splint, a scaffold, a foam, a honeycomb structure, or any combination thereof.

15. The implant of claim 11 , wherein the implant is a non-orthopedic implant.

16. The implant of claim 15 , wherein the non-orthopedic implant comprises a cardiovascular stent, a neuro stent, or a vertebroplasty stent.

17. The implant of claim 11 , wherein the implant has a lower degradation rate compared to implants made from a magnesium alloy containing microgalvanic elements.

18. The composition of claim 1 , wherein the one or more other elements do not include rare earth elements.

19. A composition comprising:
a MgZnCa alloy containing nanosized precipitates, the alloy having a Zn content ranging from 0.1 wt. % Zn to 2.0 wt. % Zn and a calcium content ranging from 0.2 wt. % Ca to 0.5 wt. % Ca, less than 0.04 wt. % of one or more other elements and with the remainder of the alloy being Mg, wherein the one or more other elements do not include rare earth elements, and wherein the nanosized precipitates are less noble than the remainder Mg.

Assignees

• Depuy Synthes Products Inc

Inventors

• Imwinkelried Thomas
• Beck Stefan
• Uggowitzer Peter
• Loeffler Joerg

Classifications

• A61L31/148

  Materials at least partially resorbable by the body · CPC title

• C22C23/02

  with aluminium as the next major constituent · CPC title

• C22C23/04 Primary

  with zinc or cadmium as the next major constituent · CPC title

• C22F1/06

  of magnesium or alloys based thereon · CPC title

• A61L2400/12

  Nanosized materials, e.g. nanofibres, nanoparticles, nanowires, nanotubes; Nanostructured surfaces · CPC title