Manufacturing method of honeycomb structure

Patent metadata

Field	Value
Publication number	US-10195597-B2
Application number	US-201715467117-A
Country	US
Kind code	B2
Filing date	Mar 23, 2017
Priority date	Mar 31, 2016
Publication date	Feb 5, 2019
Grant date	Feb 5, 2019

Abstract

The manufacturing method includes a step of mixing a coarse particle zeolite, a fine particle zeolite, and a raw material of an inorganic bonding material to prepare a zeolite raw material; a step of forming the prepared zeolite raw material into a honeycomb shape to prepare a honeycomb formed body; and a step of firing the prepared honeycomb formed body to prepare the honeycomb structure. In the step of preparing the zeolite raw material, as the coarse particle zeolite, a chabazite type zeolite having a specific average particle diameter, the fine particle zeolite having a specific average particle diameter, the raw material of the inorganic bonding material which includes at least basic aluminum lactate is used.

First claim

What is claimed is:

1. A manufacturing method of a honeycomb structure, comprising:
a step of mixing a coarse particle zeolite having a large average particle diameter, a fine particle zeolite having an average particle diameter smaller than that of the coarse particle zeolite, and a raw material of an inorganic bonding material to prepare a zeolite raw material;
a step of forming the prepared zeolite raw material into a honeycomb shape to prepare a honeycomb formed body; and
a step of firing the prepared honeycomb formed body to prepare the honeycomb structure,
wherein in the step of preparing the zeolite raw material,
as the coarse particle zeolite, a chabazite type zeolite is used in which an average particle diameter is 2 μm or more and 6 μm or less,
the fine particle zeolite is used in which an average particle diameter is 0.02 μm or more and smaller than 2 μm,
the raw material of the inorganic bonding material which includes at least basic aluminum lactate is used, and
10 to 35 parts by mass of the basic aluminum lactate as the raw material of the inorganic bonding material is added to 100 parts by mass of a total mass of the coarse particle zeolite and the fine particle zeolite, to prepare the zeolite raw material.

2. The manufacturing method of the honeycomb structure according to claim 1 ,
wherein in the raw material of the inorganic bonding material, a mass ratio of the basic aluminum lactate is from 65 to 100 mass %.

3. The manufacturing method of the honeycomb structure according to claim 1 ,
wherein as the raw material of the inorganic bonding material, boehmite is further used in addition to the basic aluminum lactate.

4. The manufacturing method of the honeycomb structure according to claim 3 ,
wherein in the raw material of the inorganic bonding material, a mass ratio of the basic aluminum lactate is from 65 to 90 mass % and a mass ratio of the boehmite is from 10 to 35 mass %.

5. The manufacturing method of the honeycomb structure according to claim 1 ,
wherein 10 to 50 parts by mass of the raw material of the inorganic bonding material is added to 100 parts by mass of the total mass of the coarse particle zeolite and the fine particle zeolite, to prepare the zeolite raw material.

6. The manufacturing method of the honeycomb structure according to claim 1 ,
wherein as the coarse particle zeolite, at least one selected from the group consisting of chabazite, SAPO-34 and SSZ-13 is used.

7. The manufacturing method of the honeycomb structure according to claim 1 ,
wherein as the fine particle zeolite, at least one selected from the group consisting of a Φ-type zeolite, a Y-type zeolite, a ZSM-5 type zeolite and the chabazite type zeolite is used.

8. The manufacturing method of the honeycomb structure according to claim 1 ,
wherein the basic aluminum lactate as the raw material of the inorganic bonding material is dissolved in water, and the basic aluminum lactate dissolved in water is mixed with the coarse particle zeolite and the fine particle zeolite, to prepare the zeolite raw material.

9. The manufacturing method of the honeycomb structure according to claim 8 ,
wherein the basic aluminum lactate as the raw material of the inorganic bonding material is dissolved in an amount of water which corresponds to twice or more as much as the mass of the basic aluminum lactate.

10. The manufacturing method of the honeycomb structure according to claim 1 , further comprising:
a step of performing ion exchange of the coarse particle zeolite and the fine particle zeolite with copper ions.

11. The manufacturing method of the honeycomb structure according to claim 10 ,
wherein the step of performing the ion exchange is performed prior to the step of preparing the zeolite raw material.

12. The manufacturing method of the honeycomb structure according to claim 1 ,
wherein at least one inorganic fiber selected from the group consisting of alumina fiber, silica alumina fiber and glass fiber is further added to prepare the zeolite raw material.

13. The manufacturing method of the honeycomb structure according to claim 12 ,
wherein 5 to 20 parts by mass of the inorganic fiber is added to 100 parts by mass of the total mass of the coarse particle zeolite and the fine particle zeolite, to prepare the zeolite raw material.

Assignees

• Ngk Insulators Ltd

Inventors

• Yamazaki Satoshi
• Hayase Toru
• Morimoto Kenji

Classifications

• B01J29/7015

  CHA-type, e.g. Chabazite, LZ-218 · CPC title

• B28B11/243

  Setting, e.g. drying, dehydrating or firing ceramic articles (B28B11/242 takes precedence) · CPC title

• B01J29/80

  Mixtures of different zeolites · CPC title

• B01D2257/702

  Hydrocarbons · CPC title

• B01J29/7007

  Zeolite Beta · CPC title