Aqueous multi-stage emulsion copolymer compositions for use in joinery applications

Patent metadata

Field	Value
Publication number	US-10190002-B2
Application number	US-201615373609-A
Country	US
Kind code	B2
Filing date	Dec 9, 2016
Priority date	Dec 18, 2015
Publication date	Jan 29, 2019
Grant date	Jan 29, 2019

Abstract

The present invention provides aqueous compositions for use in coating wood joinery, especially for exterior use, comprising (a) one or more dihydrazide compounds in a total amount of from 0.5 to 4 wt. %, based on the total weight of composition solids and (b) of one or more aqueous multistage emulsion copolymers containing, as (i) a first stage, an emulsion copolymer having a glass transition temperature (Tg) via differential scanning calorimetry (DSC) of from −50 to 30° C., and containing, in copolymerized form one or more monoethylenically unsaturated phosphorous acid monomers and, one or more keto group containing amide monomers, and, as (ii) a second stage, an emulsion copolymer having a DSC Tg of at least 50° C. to 125° C., wherein the weight ratio of (i) the first stage to (ii) the second stage, based on copolymer solids, ranging from 50:50 to 90:10.

First claim

We claim:

1. An aqueous composition comprising aqueous multistage emulsion copolymer compositions comprising (a) one or more dihydrazide compounds in a total amount of from 0.5 to 4 wt. %, based on the total weight of composition solids, and (b) of one or more aqueous multistage emulsion copolymers containing, as (i) a first stage, an emulsion copolymer having a glass transition temperature (Tg) via differential scanning calorimetry (DSC) of from −50 to 30° C., and containing, in copolymerized form, from 0.5 to 3.0 wt. % of one or more monoethylenically unsaturated phosphorous acid monomers and, from 0.75 to 5 wt. % of one or more keto group containing amide monomers, and, as (ii) a second stage, an emulsion copolymer having a DSC Tg of from 50° C. to 125° C., wherein the Tg difference between the first stage and the second stage is from 45° C. to 150° C. having a weight ratio of (i) the first stage to (ii) the second stage, based on copolymer solids, ranging from 50:50 to 90:10 or, all monomer wt. % s based on the total weight of monomers used to make the aqueous multistage emulsion copolymer, and, further wherein, the (ii) second stage of the aqueous multistage emulsion copolymer comprises, in copolymerized form, no more than 25 wt. % of the total monoethylenically unsaturated phosphorous acid monomers used to make the aqueous multistage emulsion copolymer, and no more than 50 wt. % of the total keto group containing amide monomers used to make the aqueous multistage emulsion copolymer, and wherein (b) at least one of the one or more aqueous multistage emulsion copolymer comprises, in copolymerized form, at least 90 wt. % of the one or more monoethylenically unsaturated phosphorous acid monomers in the (i) first stage.

2. The aqueous multistage emulsion copolymer composition as claimed in claim 1 , wherein at least one of the (i) first stage emulsions polymer comprises, in copolymerized form, diacetone acrylamide (DAAM) or diacetone methacrylamide.

3. The aqueous multistage emulsion copolymer composition as claimed in claim 1 , wherein at least one of the (ii) second stage emulsion copolymer comprises no more than 25 wt. % of the total keto group containing amide monomers used to make the aqueous multistage emulsion copolymer.

4. The aqueous multistage emulsion copolymer composition as claimed in claim 1 , wherein at least one of the aqueous multistage emulsion copolymers comprises, in the (i) first stage, in copolymerized form, from 0.05 to 1.5 wt. % of one or more ethylenically unsaturated acid monomers, based on the total weight of monomers used to make the first stage.

5. The aqueous multistage emulsion copolymer composition as claimed in claim 1 , wherein (b) the at least one of the one or more aqueous multistage emulsion copolymer comprises, in copolymerized form, ethyl acrylate, butyl acrylate, n-butyl methacrylate, 2-ethylhexyl acrylate, or an admixture of any of those with methyl methacrylate.

6. The aqueous multistage emulsion copolymer composition as claimed in claim 1 , wherein the one or more monoethylenically unsaturated phosphorus acid monomers and salts thereof in the (i) first stage is chosen from dihydrogen phosphate-functional monomers, phosphorus acid containing (meth)acrylic acid esters, monoethylenically unsaturated phosphonate-functional monomers, and 1,2-ethylenically unsaturated (hydroxy)phosphinylalkyl (meth)acrylate monomers.

7. The aqueous multistage emulsion copolymer composition as claimed in claim 1 , wherein (a) the one or more dihydrazide compound is a compound of the formula H2NHN—X—NHNH2, wherein X represents a —CO-A-CO—group, A represents a C1 to C12 alkylene group or a C6 to C12 arylene group and the“—” represents a covalent bond.

8. The aqueous multistage emulsion copolymer composition as claimed in claim 1 , used as a coating composition which has a total volatile organic compound (VOC) content of 150 g/L or less.

9. A method of making aqueous multistage emulsion copolymer compositions comprising aqueous emulsion polymerizing by gradual addition in the presence of an initiator or a redox pair from 50 to 90 weight parts, based on 100 parts total monomer solids used to make the multistage emulsion copolymer, of a first monomer mixture containing from 0.5 to 3.0 wt. % of one or more monoethylenically unsaturated phosphorous acid monomers and, from 0.75 to 5 wt. % of one or more keto group containing amide monomers, and the remainder of nonionic monomers including one or more soft monomers to form (i) a first stage aqueous emulsion copolymer having a glass transition temperature (Tg) via differential scanning calorimetry (DSC) of from −50 to 30° C., and,
sequentially preparing a second stage polymer by aqueous emulsion polymerizing by gradual addition in the presence of the (i) first stage aqueous emulsion copolymer and an initiator or a redox pair from 10 to 50 weight parts, based on 100 parts total monomer solids used to make the multistage emulsion copolymer, of a second monomer mixture containing one or more nonionic monomers including each of one or more soft monomers and one or more hard vinyl monomers to form an aqueous multistage emulsion copolymer having (ii) a second stage emulsion copolymer with a DSC Tg of at least 50° C. to 125° C., wherein the Tg difference between the first stage and the second stage is from 10° C. to 125° C., and wherein the weight ratio of (i) the first stage to (ii) the second stage, based on copolymer solids, ranges from 50:50 to 90:10, and,
further wherein, the (ii) second stage of the aqueous multistage emulsion copolymer comprises, in copolymerized form, no more than 25 wt. % of the total monoethylenically unsaturated phosphorous acid monomers used to make the aqueous multistage emulsion copolymer, and less than 50 wt. % the total monoethylenically unsaturated phosphorous acid monomers used to make the aqueous multistage emulsion copolymer, provided that either the amount of monoethylenically unstaturated phosphorous acid in the second stage is no more than 10 wt % of the total monoethylenically unsaturated phosphorous acid monomers used to make the aqueous multistage emulsion copolymer or the amount of keto group in the second stage is less than 25 wt % the total monoethylenically unsaturated phosphorous acid monomers used to make the aqueous multistage emulsion copolymer and, then, formulating the thus formed aqueous multistage emulsion copolymer with one or more dihydrazide compounds in a total amount of from 0.5 to 4 wt. %, based on the total weight of composition solids.

10. An aqueous composition comprising aqueous multistage emulsion copolymer compositions comprising (a) one or more dihydrazide compounds in a total amount of from 0.5 to 4 wt. %, based on the total weight of composition solids, and (b) of one or more aqueous multistage emulsion copolymers containing, as (i) a first stage, an emulsion copolymer having a glass transition temperature (Tg) via differential scanning calorimetry (DSC) of from −50 to 30° C., and containing, in copolymerized form, from 0.5 to 3.0 wt. % of one or more monoethylenically unsaturated phosphorous acid monomers and, from 0.75 to 5 wt. % of one or more keto group containing amide monomers, and, as (ii) a second stage, an emulsion copolymer having a DSC Tg of from 50° C. to 125° C., wherein the Tg difference between the first stage and the second stage is from 45° C. to 150° C. having a weight ratio of (i) the first stage to (ii) the second stage, based on copolymer solids, ranging from 50:50 to 90:10 or, all monomer wt. %s based on the total weight of monomers used to make the aqueous multistage emulsion copolymer, and, further wherein, the (ii) second stage of the aqueous multistage emulsion copolymer comprises, in copolymerized

Assignees

• Rohm & Haas

Inventors

• Bohling James C
• Gruver Jocelyn
• Haase Danniebelle
• Hermes Ann R
• Wang Wenqin

Classifications

• C09D143/02

  Homopolymers or copolymers of monomers containing phosphorus · CPC title

• C09D5/022

  Emulsions, e.g. oil in water · CPC title

• C08F220/1804

  C4-(meth)acrylate, e.g. butyl (meth)acrylate, isobutyl (meth)acrylate or tert-butyl (meth)acrylate · CPC title

• C09D151/003

  grafted on to macromolecular compounds obtained by reactions only involving unsaturated carbon-to-carbon bonds (C09D151/04, C09D151/06 take precedence) · CPC title

• C09D133/08

  Homopolymers or copolymers of acrylic acid esters · CPC title