Inner liner for pneumatic tire, method for producing the same, and pneumatic tire

Patent metadata

Field	Value
Publication number	US-10183432-B2
Application number	US-201214122353-A
Country	US
Kind code	B2
Filing date	May 29, 2012
Priority date	May 31, 2011
Publication date	Jan 22, 2019
Grant date	Jan 22, 2019

Abstract

Provided is an inner liner for a pneumatic tire including no less than 8 resin-layers, the resin-layer having a layer A constituted with a resin composition containing a resin having gas barrier properties, and a layer B that is adjacent to the layer A and is constituted with a resin composition containing an elastomer, an extensional viscosity η A of the resin composition of the layer A, and an extensional viscosity η B of the resin composition of the layer B as determined at a predetermined temperature both being no less than 1,000 Pa·s, and an extensional viscosity ratio η A /η B being no less than 0.2 and no greater than 10.

First claim

The invention claimed is:

1. An inner liner for a pneumatic tire, the inner liner comprising a laminate comprising no less than 8 resin-layers,
the no less than 8 resin-layers having a layer A constituted with a resin composition containing a resin having gas barrier properties, and a layer B being adjacent to the layer A and constituted with a resin composition containing an elastomer,
an extensional viscosity η A of the resin composition of the layer A, and an extensional viscosityη B of the resin composition of the layer B as determined under following measurement conditions both being no less than 1,000 Pa·s, and an extensional viscosity ratio η A /η B being no less than 0.3 and no greater than 5,
the measurement conditions including:
a temperature being greater by 25° C. than the higher melting point between a melting point of the resin composition of the layer A and a melting point of the resin composition of the layer B, the melting point corresponding to an outflow-starting temperature for a resin composition not having a melting point; and
a stretching speed being 500 (1/sec),
an average thickness of a single layer of at least one selected from the layer A and the layer B being no less than 0.01 μm and no greater than 10 μm, and the layer A and the layer B being alternately laminated,
a product η A ·T A of the extensional viscosity η A of the resin composition of the layer A and the average thickness T A of the one layer thereof, and a product η B ·T B of the extensional viscosity η B of the resin composition of the layer B and the average thickness T B of the one layer thereof being both no less than 2,000 Pa·s·μm and no greater than 50,000 Pa·s·μm,
the resin composition of the layer A containing, as a sole polymer, the resin having gas barrier properties,
the inner liner for a pneumatic tire further comprising a pair of supporting layers each being adjacently laminated on one of two faces, respectively, of the laminate comprising no less than 8 resin-layers,
one of the pair of supporting layers being an innermost layer and the other one of the pair of supporting layers being an outermost layer, and
the pair of supporting layers each comprising a polyurethane based thermoplastic elastomer; and
wherein the resin having gas barrier properties is an ethylene-vinyl alcohol copolymer.

2. The inner liner according to claim 1 , wherein a ratio (η A ·T A )/ (η B ·T B ) of the product η A ·T A to the product η B T B is no less than 0.01 and no greater than 100.

3. The inner liner according to claim 1 , wherein a thickness of the inner liner being no less than 0.1 μm and no greater than 1,000 μm.

4. The inner liner according to claim 1 , wherein the content of ethylene units of the ethylene-vinyl alcohol copolymer is no less than 3 mol % and no greater than 70 mol %.

5. The inner liner according to claim 1 , wherein the ethylene-vinyl alcohol copolymer has a saponification degree of no less than 80 mol %.

6. The inner liner according to claim 1 , wherein
the ethylene-vinyl alcohol copolymer comprises a structural unit (I), a structural unit (II) or both structural units (I) and (II):

and a content of the structural unit (I) or (II) with respect to all structural units is no less than 0.5 mol % and no greater than 30 mo1%,
wherein,
in the formula (I), R 1 , R 2 and R 3 each independently represent a hydrogen atom, an aliphatic hydrocarbon group having 1 to 10 carbon atoms, an alicyclic hydrocarbon group having 3 to 10 carbon atoms, an aromatic hydrocarbon group having 6 to 10 carbon atoms or a hydroxyl group; with the proviso that two among R 1 , R 2 and R 3 are optionally bound, unless the two both represent a hydrogen atom; and that any of R 1 , R 2 and R 3 that is an aliphatic hydrocarbon group having 1 to 10 carbon atoms, an alicyclic hydrocarbon group having 3 to 10 carbon atoms or an aromatic hydrocarbon group having 6 to 10 carbon atoms optionally has a hydroxyl group, a carboxyl group or a halogen atom; and
in the formula (II), R 4 , R 5 , R 6 and R 7 each independently represent a hydrogen atom, an aliphatic hydrocarbon group having 1 to 10 carbon atoms, an alicyclic hydrocarbon group having 3 to 10 carbon atoms, an aromatic hydrocarbon group having 6 to 10 carbon atoms or a hydroxyl group; with the proviso that R 4 and R 5 or R 6 and R 7 are optionally bound, unless both R 4 and R 5 or both R 6 and R 7 represent a hydrogen atom; and that any of R 4 , R 5 , R 6 and R 7 that is an aliphatic hydrocarbon group having 1 to 10 carbon atoms, an alicyclic hydrocarbon group having 3 to 10 carbon atoms or an aromatic hydrocarbon group having 6 to 10 carbon atoms optionally has a hydroxyl group, an alkoxy group, a carboxyl group or a halogen atom.

7. The inner liner according to claim 1 , wherein the elastomer is a polystyrene based elastomer, a polyolefin based elastomer, a polydiene based elastomer, a polyvinyl chloride based elastomer, a chlorinated polyethylene based elastomer, a polyurethane based elastomer, a polyester based elastomer, a polyamide based elastomer, a fluorine-contained resin based elastomer or a combination thereof.

8. The inner liner according to claim 1 , wherein the layer A and the layer B are obtained through crosslinking by irradiation with an active energy ray.

9. The inner liner according to claim 1 , wherein a binding reaction is involved at an interface between the layer A and the layer B.

10. The inner liner according to claim 1 , wherein the inner liner comprises no less than 15 resin-layers.

11. The inner liner according to claim 1 , wherein a total amount of a resin other than the resin having gas barrier properties, a heat stabilizer, an ultraviolet ray absorbing agent, an antioxidant, a colorant and a filler in the resin composition of the layer A is no greater than 10% by mass.

12. A pneumatic tire comprising the inner liner according to claim 8 .

13. A method for producing an inner liner according to claim 1 , comprising
forming the inner liner by a multilayer coextrusion process using a resin composition comprising a resin having gas barrier properties and a resin composition comprising an elastomer.

Assignees

• Hayashi Nahoto
• Hikasa Masao
• Tanaka Yusuke
• Kitano Hideki
• Tanaka Takatsugu
• Amamoto Tetsuo
• Kuraray Co
• Bridgestone Corp

Inventors

• Hayashi Nahoto
• Hikasa Masao
• Tanaka Yusuke
• Kitano Hideki
• Tanaka Takatsugu
• Amamoto Tetsuo

Classifications

• C08L23/0861

  Saponified copolymers, e.g. ethylene vinyl alcohol copolymers · CPC title

• B60C5/14

  with impervious liner or coating on the inner wall of the tyre · CPC title

• B60C2005/145

  made of laminated layers · CPC title

• C08F2800/10

  as molar percentages · CPC title

• C08F218/08

  Vinyl acetate · CPC title