Polyester resin composition and method for producing the same

Patent metadata

Field	Value
Publication number	US-10179849-B2
Application number	US-201515500989-A
Country	US
Kind code	B2
Filing date	Oct 29, 2015
Priority date	Oct 31, 2014
Publication date	Jan 15, 2019
Grant date	Jan 15, 2019

Abstract

A polyester resin composition having excellent hydrolysis resistance and excellent transparency and a method of producing the same are provided. There is provided a polyester resin composition comprising a polyester resin that is obtained from a dicarboxylic acid or an ester-forming derivative thereof and a diol as main raw material; and a copper-containing compound and a chelate ligand compound having a nitrogen-containing heterocyclic structure or a tertiary amine structure that are mixed with the polyester resin.

First claim

The invention clamed is:

1. A polyester resin composition, comprising:
a polyester resin that is obtained by polycondensation from a dicarboxylic acid or an ester-forming derivative thereof and a diol as main raw material; and
a copper-containing compound and a nitrogen-containing chelate ligand having a nitrogen-containing heterocyclic structure or a tertiary amine structure that are mixed with the polyester resin;
wherein
0.001 to 0.3 mmol of the copper-containing compound is mixed on a copper atom basis relative to 100 g of the polyester resin, and
a polyester solution obtained by dissolving 2 g of the polyester resin composition in 20 ml of a 3/2 (volume ratio) mixed solution oh phenol/ 1,1,2,2-tetrachloroethane has a haze of not higher than 2.3% that is measured by using a cell having an optical path of 20 mm.

2. The polyester resin composition according to claim 1 ,
wherein 0.001 to 10 mmol of the nitrogen-containing chelate ligand is mixed relative to 100 g of the polyester resin.

3. The polyester resin composition according to claim 1 ,
wherein the nitrogen-containing chelate ligand is mixed with copper atom of the copper-containing compound at a molar ratio (the nitrogen-containing chelate ligand/ copper atom of the copper-containing compound) of 0.001 to 4.

4. The polyester resin composition according to claim 1 ,
wherein the copper-containing compound is at least one selected from the group consisting of an organic copper salt, an inorganic copper salt, a copper halide, a copper oxide and a copper hydroxide.

5. The polyester resin composition according to claim 1 ,
wherein the nitrogen-containing chelate ligand is any of a compound having a partial structure of 2,2′-bipyridyl, a compound having a partial structure of 1,10-phenanthroline and a compound having a partial structure of N,N,N′,N′-tetramethylethylenediamine.

6. The polyester resin composition according to claim 5 ,
wherein the nitrogen-containing chelate ligand is either of 2,2′-bipyridyl and 1,10-phenanthrorine.

7. The polyester resin composition according to claim 1 ,
wherein the polyester resin is at least one selected from the group consisting of polyethylene terephthalate, polypropylene terephthalate, polybutylene terephthalate and polyethylene naphthalate.

8. The polyester resin composition according to claim 1 ,
wherein the polyester resin has a number-average molecular weight of 5000 to 100000.

9. The polyester resin composition according to claim 1 ,
wherein the polyester resin has an acid value of not higher than 13 eq/t.

10. A method of producing the polyester resin composition according to claim 1 , the method comprising:
in a process of producing a polyester resin by performing esterification or transesterification of a dicarboxylic acid or an ester-forming derivative thereof and a diol, and subsequently performing polycondensation,
mixing a copper-containing compound and a nitrogen-containing chelate ligand having a nitrogen-containing heterocyclic structure or a tertiary amine structure in any of the esterification, the transesterification or the polycondensation.

11. The method of producing the polyester resin composition according to claim 10 ,
the method mixing 0.001 to 0.3 mmol of the copper-containing compound on a copper atom basis relative to 100 g of the obtained polyester resin.

12. The method of producing the polyester resin composition according to claim 10 ,
wherein 0.001 to 10 mmol of the nitrogen-containing chelate ligand is mixed relative to 100 g of the obtained polyester resin.

13. The method of producing the polyester resin composition according to claim 10 ,
wherein the nitrogen-containing chelate ligand is mixed with the copper-containing compound at a molar ratio of 0.001 to 4 with respect to the nitrogen-containing ligand and the copper atom of the copper-containing compound.

14. A polyester resin composition, comprising:
a polyester resin formed by polycondensation from a dicarboxylic acid and/or an ester-forming derivative thereof and a diol as main raw material;
a copper-containing compound; and
a nitrogen-containing chelate ligand having at least one of a nitrogen-containing heterocyclic structure and a tertiary amine structure;
wherein
0.001 to 0.3 mmol of the copper-containing compound is mixed on a copper atom basis relative to 100 g of the polyester resin, and
a polyester solution obtained by dissolving 2 g of the polyester resin composition in 20 ml of a 3/2 (volume ratio) mixed solution of phenol/ 1,1,2,2-tetrachloroethane has a haze of not higher than 2.3% that is measured by using a cell having an optical path of 20 mm.

Assignees

• Toray Industries

Inventors

• Akahira Masato
• Sudo Ken
• Yasutake Eri
• Kato Koya

Classifications

• C08G63/183

  Terephthalic acids · CPC title

• C08K5/098

  Metal salts of carboxylic acids · CPC title

• C08K5/3437 Primary

  condensed with carbocyclic rings · CPC title

• C08K5/17

  Amines; Quaternary ammonium compounds · CPC title

• C08K5/34

  Heterocyclic compounds having nitrogen in the ring · CPC title