Phase difference film layered body having layer with specified ratio of polyphenylene ether to polystyrene-based polymer and method for producing the same

Patent metadata

Field	Value
Publication number	US-10175402-B2
Application number	US-201314385197-A
Country	US
Kind code	B2
Filing date	Feb 26, 2013
Priority date	Mar 15, 2012
Publication date	Jan 8, 2019
Grant date	Jan 8, 2019

Abstract

A phase difference film layered body is obtained by stretching a film before stretching, the film before stretching including: a P1 layer formed of a resin p1 containing polyphenylene ether having a positive intrinsic birefringence value and a polystyrene-based polymer having a negative intrinsic birefringence value and having a syndiotactic structure; and a P2 layer disposed in contact with the P1 layer and formed of a resin p2 containing an acrylic resin or an alicyclic structure-containing polymer. In the resin p1, the weight ratio of (the content of the polyphenylene ether)/(the content of the polystyrene-based polymer) is 35/65 to 45/55. A method for producing the phase difference film layered body and a method for producing a phase difference film using the phase difference film layered body are also provided.

First claim

The invention claimed is:

1. A phase difference film layered body obtained by stretching a pre-stretch film, the pre-stretch film including: a P1 layer consisting of a resin p1 containing polyphenylene ether having a positive intrinsic birefringence value and a polystyrene-based polymer having a negative intrinsic birefringence value and having a syndiotactic structure; and a P2 layer disposed in contact with the P1 layer and consisting of a resin p2 containing an acrylic resin or an alicyclic structure-containing polymer, wherein
in the resin p1, a weight ratio of (a content of the polyphenylene ether)/(a content of the polystyrene-based polymer) is 35/65 to 45/55,
in a layer portion of the phase difference film layered body excluding the P2 layer, an in-plane direction retardation Re 450 of light having a wavelength of 450 nm, an in-plane direction retardation Re 550 of light having a wavelength of 550 nm, and an in-plane direction retardation Re 650 of light having a wavelength of 650 nm satisfy a relationship of Re 450 <Re 550 <Re 650 ,
a weight average molecular weight of the polyphenylene ether is 15,000 to 100,000, and
a weight average molecular weight of the polystyrene-based polymer is 130,000 to 300,000.

2. The phase difference film layered body according to claim 1 , wherein the phase difference film layered body is a long-length film and has a slow axis in a diagonal direction with respect to a lengthwise direction of the phase difference film layered body.

3. The phase difference film layered body according to claim 2 , wherein the phase difference film layered body has the slow axis in a direction inclined at an angle of 40° or more and 50° or less with respect to the lengthwise direction.

4. A method for producing the phase difference film layered body according to claim 1 , the method comprising the steps of:
obtaining a pre-stretch film by co-extruding a resin p1 and a resin p2, the resin p1 containing polyphenylene ether having a positive intrinsic birefringence value and a polystyrene-based polymer having a negative intrinsic birefringence value and having a syndiotactic structure, a weight ratio of (a content of the polyphenylene ether)/(a content of the polystyrene-based polymer) being 35/65 to 45/55, the resin p2 containing an acrylic resin or an alicyclic structure-containing polymer; and
stretching the pre-stretch film.

5. The method according to claim 4 , wherein the stretching is performed at a film temperature of Tg −20° C. to Tg+20° C. where Tg is a glass transition temperature of the resin p1.

6. The method according to claim 4 , wherein
the pre-stretch film obtained in the step of obtaining the pre-stretch film is a long-length film, and
in the stretching step, the pre-stretch film is stretched in a diagonal direction with respect to the lengthwise direction of the pre-stretch film.

7. The method according to claim 6 , wherein, in the step of stretching, the pre-stretch film is stretched in a direction inclined at an angle of 40° or more and 50° or less with respect to the lengthwise direction of the pre-stretch film.

8. A method for producing a phase difference film, the method comprising removing the P2 layer from the phase difference film layered body according to claim 1 .

9. The phase difference film layered body according to claim 1 , wherein the polyphenylene ether is a polymer containing a phenylene ether unit represented by formula (I)

wherein each Q 1 independently represents a halogen atom, an alkyl group having 7 or less carbon atoms, a phenyl group, a haloalkyl group, an aminoalkyl group, a hydrocarbon oxy group, or a halohydrocarbon oxy group provided that a halogen atom and an oxygen atom are separated by at least two carbon atoms, and
each Q 2 independently represents a hydrogen atom, a halogen atom, an alkyl group having 7 or less carbon atoms, a phenyl group, a haloalkyl group, a hydrocarbon oxy group, or a halohydrocarbon oxy group provided that a halogen atom and an oxygen atom are separated by at least two carbon atoms.

10. The phase difference film layered body according to claim 1 , wherein the polystyrene-based polymer is selected from the group consisting of polystyrene, poly(alkylstyrene), poly(halogenated styrene), poly(halogenated alkylstyrene), poly(alkoxystyrene), poly(vinylbenzoic acid ester), hydrogenated polymers thereof, and copolymers thereof.

11. The phase difference film layered body according to claim 1 , wherein a thickness of the P2 layer is 50 μm to 300 μm.

Assignees

• Zeon Corp

Inventors

• Morita Takashi
• Fujii Kohei
• Kinohira Tomokazu
• Yamanaka Shunsuke
• Hatano Taku

Classifications

• B29D11/0073

  Optical laminates · CPC title

• B29C48/08

  flexible, e.g. films · CPC title

• B29C55/045

  in a direction which is not parallel or transverse to the direction of feed, e.g. oblique · CPC title

• B29C55/023

  using multilayered plates or sheets · CPC title

• B29C48/0018

  combined with shaping by orienting, stretching or shrinking, e.g. film blowing (B29C48/0017 takes precedence) · CPC title