Organic binder, granular material, three-dimensional lamination-shaped mold manufacturing apparatus, and three-dimensional lamination-shaped mold manufacturing method

Patent metadata

Field	Value
Publication number	US-10174183-B2
Application number	US-201514908510-A
Country	US
Kind code	B2
Filing date	Mar 9, 2015
Priority date	Mar 9, 2015
Publication date	Jan 8, 2019
Grant date	Jan 8, 2019

Abstract

In order to well perform recoating regardless of the type of granular material and reuse a refractory aggregate in an unprinted portion without any regeneration process in the manufacture of a three-dimensional lamination-shaped mold, this invention provides a granular material for use in shaping a three-dimensional laminated mold, which is coated with an acid as a catalyst which activates and cures an organic binder for binding the granular material. The acid contains at least one of sulfuric acid, phosphoric acid, a sulfonic acid and a carboxylic acid, and is one of a mixture of sulfuric acid and another acid, phosphoric acid only, a mixture of phosphoric acid and another acid, sulfonic acid only, a mixture of sulfonic acid and another acid and a mixture of a carboxylic acid and another acid.

First claim

The invention claimed is:

1. A composition for use in shaping a three-dimensional laminated mold, the composition comprising a granular material coated with a coating layer, the coating layer comprising an acid capable of acting as a catalyst to activate and cure an organic binder for binding the granular material, wherein the coating layer is coated on the granular material by mixing the granular material with a solution comprising the acid and a solvent and volatizing the solvent.

2. The composition according to claim 1 , wherein said acid contains at least one of sulfuric acid, phosphoric acid, a sulfonic acid, and a carboxylic acid.

3. The composition according to claim 2 , wherein said acid is one of a mixture of sulfuric acid and another acid, phosphoric acid only, a mixture of phosphoric acid and another acid, sulfonic acid only, a mixture of sulfonic acid and another acid, and a mixture of a carboxylic acid and another acid.

4. The composition according to claim 2 , wherein the sulfonic acid contains at least one of para toluene sulfonic acid, xylene sulfonic acid, benzene sulfonic acid and methane sulfonic acid, and the carboxylic acid contains at least one of lactic acid, citric acid, malic acid, tartaric acid, malonic acid, maleic acid, oxalic acid and benzoic acid.

5. The composition according to claim 1 , wherein the granular material is heated before mixing with the acid solution and the solvent is volatilized by heat of the heated granular material and stirring of the acid solution.

6. The composition according to claim 1 , wherein the granular material is refractory artificial sand obtained by one of a sintering method, a fusion method and a flame-fusion method.

7. A composition for use in shaping a three-dimensional laminated mold, the composition being formed by applying an organic binder to a granular material that is coated with a coating layer formed on the granular material by mixing the granular material with a solution comprising an acid and a solvent and volatizing the solvent, wherein the acid acts as a catalyst to activate and cure the organic binder to bind the granular material, the organic binder being one of:
furfuryl alcohol only; and
a mixture of furfuryl alcohol and at least one material selected from the group consisting of 2,5-bis(hydroxymethyl)furan, a phenol group, and a bisphenol group.

8. A composition for use in shaping a three-dimensional laminated mold, the composition being formed by applying an organic binder to a granular material that is coated with a coating layer formed on the granular material by mixing the granular material with a solution comprising an acid and a solvent and volatizing the solvent, wherein the acid acts as a catalyst to activate and cure the organic binder to bind the granular material,
the organic binder being one of a condensate and a cocondensate of an aldehyde group and at least one material selected from a phenol group and a bisphenol group.

9. A composition for use in shaping a three-dimensional laminated mold, the composition being formed by applying an organic binder to a granular material that is coated with a coating layer coated on the granular material by mixing the granular material with a solution comprising an acid and a solvent and volatizing the solvent, wherein the acid acts as a catalyst to activate and cure the organic binder to bind the granular material, the organic binder being one of:
a mixture of furfuryl alcohol and one of a condensate and a cocondensate of an aldehyde and at least one material selected from a phenol group and a bisphenol group; and
a mixture of furfuryl alcohol, 2,5-bis(hydroxymethyl)furan, and one of a condensate and a cocondensate of an aldehyde and at least one material selected from a phenol group and a bisphenol group.

10. An organic binder for use in shaping a three-dimensional laminated mold, the composition being formed by applying an organic binder to a granular material that is coated with a coating layer coated on the granular material by mixing the granular material with a solution comprising an acid and a solvent and volatizing the solvent, wherein the acid acts as a catalyst to activate and cure the organic binder to bind the granular material, the organic binder being one of:
a mixture of urea, an aldehyde condensate and furfuryl alcohol; and
a mixture of urea, an aldehyde condensate, furfuryl alcohol and 2,5-bis(hydroxymethyl)furan.

11. A system for manufacturing a three-dimensional lamination-shaped mold, said system comprising:
a granular material coated with a coating layer comprising an acid, wherein the coating layer is coated on the granular material by mixing the granular material with a solution comprising the acid and a solvent and volatizing the solvent;
an organic binder which is activated and cured by the acid in the coating layer when the binder is printed on the coated granular material so that the binder selectively binds said granular material coated with said acid;
means for laminating the granular material on a shaping target to form laminated granular material; and
means for printing the organic binder on the laminated granular material so that the binder is activated and cured by the acid in the coating layer and selectively binds the laminated granular material.

12. A method of manufacturing a three-dimensional lamination-shaped mold, said method comprising the steps of:
(a) coating a granular material with an acid by mixing the granular material with a solution comprising the acid and a solvent and volatizing the solvent, wherein the acid is capable of acting as a catalyst to activate and cure an organic binder;
(b) spreading the granular material coated with the acid into layers;
(c) selectively discharging the organic binder to the granular material spread into layers to activate and cure the organic binder so as to bind the granular material spread into layers and form the three-dimensional laminated mold as an object; and
(d) repeating steps (b) and (c) until the three-dimensional laminated mold as the object is shaped.

13. The method according to claim 12 , wherein the volatizing in step (a) comprises heating the granular material before mixing with the acid solution such that the solvent is volatilized by heat from the heated granular material and stirring of the acid solution.

14. The method according to claim 12 , wherein the granular material is heated to a temperature of about 120° C. in step (a).

Assignees

• Tech Res Association Future Additive Manufacturing

Inventors

• Nagai Yasuhiro
• Takeshita Kosuke
• Ooba Yoshikazu
• Imamura Satoshi
• Okane Toshimitsu

Classifications

• B29C64/165

  using a combination of solid and fluid materials, e.g. a powder selectively bound by a liquid binder, catalyst, inhibitor or energy absorber · CPC title

• B29K2995/0096

  Dimensional stability · CPC title

• B29K2105/16

  Fillers · CPC title

• B22C1/224

  Furan polymers (B22C1/2273 takes precedence) · CPC title

• B22C1/2253

  with phenols · CPC title