Process for hot-rolling metallic hollow bodies and corresponding hot-rolling mill

Patent metadata

Field	Value
Publication number	US-10166583-B2
Application number	US-201113806802-A
Country	US
Kind code	B2
Filing date	Jun 28, 2011
Priority date	Jun 28, 2010
Publication date	Jan 1, 2019
Grant date	Jan 1, 2019

Abstract

In order to optimize the lubrication of a rolling rod in a process for hot-rolling metallic, elongate hollow bodies ( 21 ) by means of the rolling rod ( 2 ), which is arranged in the hollow body and to which lubricant is applied before the hot-rolling operation, the lubricant is applied to the rolling rod in solid form.

First claim

The invention claimed is:

1. A method for hot-rolling a metallic, elongated hollow body, said method comprising:
disposing a rolling rod in the hollow body;
providing a solid lubricant as a lubricant film;
applying the lubricant film in solid form to the rolling rod; and
subsequently hot rolling the hollow body after the lubricant film is applied in solid form to the rolling rod;
wherein a first roller disposed adjacent to the rolling rod presses the lubricant film onto the rolling rod; and
wherein:
a functional agent is provided as a functional agent film or as a functional agent sheet and the functional agent film or the functional agent sheet is applied in solid form to the rolling rod or to the lubricant film before the lubricant film is applied in solid form to the rolling rod.

2. The method according to claim 1 , wherein before the lubricant film is applied in solid form to the rolling rod, the lubricant film is prefabricated.

3. The method according to claim 2 , wherein the lubricant film is prefabricated in a fabrication station and the lubricant film is applied to the rolling rod in a lubricant application station, the lubricant application station being disposed separate from the fabrication station.

4. The method according to claim 1 , wherein the lubricant film is rolled onto the rolling rod via the first roller.

5. The method according to claim 1 , wherein the lubricant film has a varying layer thickness along the rolling rod.

6. The method according to claim 1 , wherein the lubricant film is applied to the rolling rod in multiple layers.

7. The method according to claim 6 , wherein the lubricant layers have different material properties.

8. The method according to claim 1 , wherein the functional agent film or the functional agent sheet is applied to the lubricant film before application of the lubricant film to the rolling rod.

9. The method according to claim 8 , wherein the functional agent comprises an adhesive, a binder, a release agent or an insulation agent.

10. The method according to claim 1 , wherein the functional agent film or the functional agent sheet is applied to the rolling rod before application of the lubricant film to the rolling rod.

11. The method according to claim 1 , wherein the elongated hollow body comprises a shell or a pipe.

12. The method according to claim 1 , wherein the lubricant film comprises graphite.

13. The method according to claim 1 , wherein the lubricant film comprises a support material.

14. The method according to claim 13 , wherein the support material is lost during the rolling process.

15. The method according to claim 1 , wherein the elongated hollow body comprises steel.

16. The method according to claim 1 , wherein a second roller disposed adjacent to the rolling rod presses the lubricant film onto the rolling rod.

17. The method according to claim 1 , wherein the first roller is a half-round roller.

18. A method for hot-rolling a metallic, elongated hollow body, said method comprising:
disposing a rolling rod in the hollow body;
providing a solid lubricant as a graphite lubricant sheet;
applying the graphite lubricant sheet in solid form to the rolling rod; and
subsequently hot rolling the hollow body after the graphite lubricant sheet is applied in solid form to the rolling rod;
wherein a first roller disposed adjacent to the rolling rod presses the graphite lubricant sheet onto the rolling rod; and
wherein:
a functional agent is provided as a functional agent film or as a functional agent sheet and the functional agent film or the functional agent sheet is applied in solid form to the rolling rod or to the graphite lubricant sheet before the graphite lubricant sheet is applied in solid form to the rolling rod.

19. The method according to claim 18 , wherein before the graphite lubricant sheet is applied in solid form to the rolling rod, the graphite lubricant sheet is prefabricated.

20. The method according to claim 19 , wherein the graphite lubricant sheet is prefabricated in a fabrication station and the graphite lubricant sheet is applied to the rolling rod in a lubricant application station, the lubricant application station being disposed separate from the fabrication station.

21. The method according to claim 18 , wherein the graphite lubricant sheet is rolled onto the rolling rod via the first roller.

22. The method according to claim 18 , wherein the graphite lubricant sheet has a varying layer thickness along the rolling rod.

23. The method according to claim 18 , wherein the graphite lubricant sheet is applied to the rolling rod in multiple layers.

24. The method according to claim 23 , wherein the lubricant layers have different material properties.

25. The method according to claim 18 , wherein the functional agent film or the functional agent sheet is applied to the graphite lubricant sheet before application of the graphite lubricant sheet to the rolling rod.

26. The method according to claim 25 , wherein the functional agent comprises an adhesive, a binder, a release agent or an insulation agent.

27. The method according to claim 18 , wherein the functional agent film or the functional agent sheet is applied to the rolling rod before application of the graphite lubricant sheet to the rolling rod.

28. The method according to claim 18 , wherein the elongated hollow body comprises a shell or a pipe.

29. The method according to claim 18 , wherein the graphite lubricant sheet comprises a support material.

30. The method according to claim 29 , wherein the support material is lost during the rolling process.

31. The method according to claim 18 , wherein the elongated hollow body comprises steel.

32. The method according to claim 18 , wherein a second roller disposed adjacent to the rolling rod presses the graphite lubricant sheet onto the rolling rod.

33. The method according to claim 18 , wherein the first roller is a half-round roller.

Assignees

• Pehle Hans Joachim
• Thieven Peter
• Sms Group Gmbh

Inventors

• Pehle Hans-Joachim
• Thieven Peter

Classifications

• B21B25/04 Primary

  Cooling or lubricating mandrels during operation · CPC title

• B21B19/06

  Rolling hollow basic material, {e.g. Assel mills}(B21B19/04 takes precedence; separating work from mandrel B21C45/00) · CPC title

• B21B23/00

  Tube-rolling not restricted to methods provided for in only one of groups B21B17/00, B21B19/00, B21B21/00, e.g. combined processes {planetary tube rolling, auxiliary arrangements, e.g. lubricating, special tube blanks, continuous casting combined with tube rolling}(B21B25/00 takes precedence) · CPC title