High performance water-based tackified acrylic pressure sensitive adhesives

Patent metadata

Field	Value
Publication number	US-10160891-B2
Application number	US-201313750844-A
Country	US
Kind code	B2
Filing date	Jan 25, 2013
Priority date	Feb 8, 2012
Publication date	Dec 25, 2018
Grant date	Dec 25, 2018

Abstract

A pressure-sensitive adhesion composition comprising: a first polymer that is acrylate polymer or copolymer comprising polymerized monomers selected from the group consisting of acrylic acid, butyl acrylate, 2-ethylhexyl acrylate, methyl methacrylate, octyl acrylate, styrene, vinyl acetate and combinations thereof; and b) a second polymer selected from the group consisting of ethylene-acrylic acid copolymer, oxidized polyethylene, oxidized ethylene-vinyl acetate copolymer, maleated polyolefin and combinations thereof; wherein the composition is water-based and adapted for pressure-sensitive adhesion to substrates. The adhesion composition may also comprise a tackifier resin selected from the group consisting of rosin ester resin, rosin acid resin, synthetic hydrocarbon resin, synthetic terpenic resin and combinations thereof. An article of manufacture comprising a support member and a pressure-sensitive adhesion layer attached thereto that comprises said pressure-sensitive adhesion composition. A process of forming a pressure-sensitive adhesive article of manufacture.

First claim

What is claimed is:

1. A pressure-sensitive adhesion composition comprising: a) about 59 weight % to about 98.5 weight %, based on the total weight of the adhesive of a first polymer that comprises a majority component of either 2-ethylhexylacrylate or butyl acrylate copolymerized with a minority component of either methyl methacrylate, vinyl acetate, or styrene; b) about 1 weight % to about 17.5 weight % based on the total weight of the adhesive of a second polymer consisting of an ethylene-acrylic acid copolymer having a number average molecular weight between 1500 and 3000 in combination with an oxidized polyethylene having a number average molecular weight between 800 and 6000; and c) about 0.5 weight % to about 40 weight % based on the total weight of the adhesive of a tackifier resin having a number average molecular weight between about 270 and about 1400, selected from the group consisting of rosin ester resin, rosin acid resin, synthetic hydrocarbon resin, synthetic terpenic resin and combinations of two or more thereof;
wherein the composition is water-based and adapted for pressure-sensitive adhesion to substrates.

2. The composition of claim 1 , wherein the ethylene-acrylic acid copolymer has an acid number of between about 40 mg KOH/g and about 200 mg KOH/g determined according to method ASTM D-1386, a hardness at 25° C. of less than about 20 dmm determined according to method ASTM D-5, and a viscosity at 140° C. of between about 200 cps and about 800 cps determined with a Brookfield rotational viscometer; and
wherein the oxidized polyethylene has an acid number of between about 10 mg KOH/g and about 21 mg KOH/g determined according to method ASTM D-1386, a hardness at 25° C. of between about 0.5 dmm and about 13 dmm determined according to method ASTM D-5, and a viscosity at 140° C. of between about 100 cps and about 500 cps determined with a Brookfield rotational viscometer.

3. The composition of claim 1 , wherein the second polymer b) is present in an amount of about 1% to about 4% by weight based on the total weight of the adhesive.

4. The composition of claim 1 , wherein the tackifier resin c) is present in an amount of up to about 10% by weight based on the total weight of the adhesive while being present at least about 0.5%.

5. The composition of claim 1 , wherein second polymer b) is present at 10% by weight, and wherein a weight ratio of the ethylene-acrylic acid copolymer to the oxidized polyethylene is 25:75.

6. A process of forming a pressure-sensitive adhesive article of manufacture comprising a step of applying the pressure-sensitive adhesion composition of one of claim 1 or 2 to a support member.

7. An article of manufacture comprising: a support member and a pressure-sensitive adhesion layer attached thereto comprising a) about 59 weight % to about 98.5 weight %, based on the total weight of the adhesive of a first polymer that comprises a majority component of either 2-ethylhexylacrylate or butyl acrylate copolymerized with a minority component of either methyl methacrylate, vinyl acetate, or styrene, wherein the main component is present in the copolymer in relative proportion greater than the minor component; b) about 1 weight % to about 17.5 weight % based on the total weight of the adhesive of a second polymer consisting of an ethylene-acrylic acid copolymer having a number average molecular weight between 1500 and 3000 in combination with an oxidized polyethylene having a number average molecular weight between 800 and 6000; and c) about 0.5 weight % to about 40 weight % based on the total weight of the adhesive of a tackifier resin having a number average molecular weight between about 270 and about 1400, selected from the group consisting of rosin ester resin, rosin acid resin, synthetic hydrocarbon resin, synthetic terpenic resin and combinations of two or more thereof;
wherein the adhesion layer is water-based and adapted for pressure-sensitive adhesion to substrates.

8. The article of manufacture of claim 7 , wherein the ethylene-acrylic acid copolymer has an acid number of between about 40 mg KOH/g and about 200 mg KOH/g determined according to method ASTM D-1386, a hardness at 25° C. of less than about 20 dmm determined according to method ASTM D-5, and a viscosity at 140° C. of between about 200 cps and about 800 cps determined with a Brookfield rotational viscometer; and
wherein the oxidized polyethylene has an acid number of between about 10 mg KOH/g and about 21 mg KOH/g determined according to method ASTM D-1386, a hardness at 25° C. of between about 0.5 dmm and about 13 dmm determined according to method ASTM D-5, and a viscosity at 140° C. of between about 100 cps and about 500 cps determined with a Brookfield rotational viscometer.

9. The article of manufacture of claim 7 , wherein the second polymer b) is present in an amount of about 1% to about 4% by weight based on the total weight of the adhesive.

10. The article of manufacture of claim 7 , wherein the tackifier resin c) is present in an amount of up to about 10% by weight based on the total weight of the adhesive while being present at least about 0.5%.

Assignees

• Honeywell Int Inc

Inventors

• Dodge Robert G
• Severyns Kurt

Classifications

• C09J2433/00

  Presence of (meth)acrylic polymer · CPC title

• C09J133/08 Primary

  Homopolymers or copolymers of acrylic acid esters · CPC title

• C09J123/0869

  Acids or derivatives thereof · CPC title

• C08L33/12

  Homopolymers or copolymers of methyl methacrylate · CPC title

• C09J7/385

  Acrylic polymers · CPC title