Fluoropolymers

Patent metadata

Field	Value
Publication number	US-10160820-B2
Application number	US-201414772124-A
Country	US
Kind code	B2
Filing date	Mar 7, 2014
Priority date	Mar 15, 2013
Publication date	Dec 25, 2018
Grant date	Dec 25, 2018

Abstract

The invention relates to novel linear, semi-crystalline fluoropolymers containing 0.5 to 25 mole percent of at least one vinyl ester monomer unit. At least 40 mole percent of the vinyl ester monomer units are present in the copolymer as single monomer units (not diads or triads or greater) between two fluoromonomer units. The invention also relates to a process for forming the fluoromonomers/vinyl ester copolymer. The fluoropolymer of the invention may be used in applications benefiting from a functional fluoropolymers including as a binder, or for use in forming hydrophilic membranes and hollow fibers.

First claim

What is claimed is:

1. A random, semi-crystalline copolymer comprising from 80 to 99.95 mole percent of one or more fluoromonomers, wherein said fluoromonomers comprise from 70 to 100 weight percent of vinylidene fluoride, and 0.05 to 20 mole percent of one or more vinyl ester having the formula CH 2 ═CH—O—(CO)—Rn, wherein Rn is a hydrogen atom or a C 1-4 linear or branched hydrocarbon, and wherein at least 40 mole percent of the vinyl ester monomer units are present in the copolymer as single monomer units between two fluoromonomer units.

2. The random copolymer of claim 1 , wherein said fluoromonomers are selected from the group consisting of vinylidene fluoride (VDF), vinyl fluoride (VF), trifluoroethylene, tetrafluoroethylene (TFE), ethylene tetrafluoroethylene, chlorotrifluoroethylene (CTFE) and hexafluoropropylene (HFP), and mixtures thereof.

3. The random copolymer of claim 1 , wherein said copolymer is a hydrophilic copolymer.

4. The random copolymer of claim 1 , wherein said vinyl ester comprises vinyl acetate.

5. The random copolymer of claim 1 , wherein the mole percent of vinyl ester monomer units is from 0.5 to 15 mole percent.

6. The random copolymer of claim 5 , wherein the mole percent of vinyl ester monomer units is from 1 to 10 mole percent.

7. A process for forming the random copolymer of claim 1 , comprising the steps of
a) charging an initial monomer charge that comprising fluoromonomers, and
b) starve-feeding the vinyl ester monomer co-continuously with fluoromonomers to the reactor once polymerization has begun.

8. The process of claim 7 , wherein said initial monomer feed consists of fluoromonomers.

9. The process of claim 7 , wherein only non-fluorinated surfactant is used in the polymerization process.

10. A material comprising the fluoropolymer of claim 1 .

11. The material of claim 10 , wherein said material is selected from a filtration membrane, a hollow fiber filtration device, and a slurry binder for use in forming a non-aqueous solvent type secondary battery or capacitor electrode.

12. The material of claim 11 , wherein said slurry binder is an aqueous-based slurry comprising:
a) from 0.2 to 150 parts fluoropolymer of claim 1 ;
b) from 10 to 500 parts of one or more powdery electrode-forming materials;
c) optionally from 0 to 10 parts of one or more thickeners;
d) optionally, one or more pH adjusting agents;
e) optionally from 0 to 10 parts of one or more additives selected from the group consisting of anti-settling agents and surfactants;
f) optionally from 0 to 5 parts of one or more wetting agents;
g) optionally from 0 to 150 parts of one or more fugitive adhesion promoters;
h) 100 parts water;

all parts being parts by weight based on 100 parts by weight of water, and wherein the composition contains no fluorosurfactant.

13. The material of claim 11 , wherein said slurry binder is a solvent-based slurry, comprising:
a) from 0.1 to 150 parts fluoropolymer of claim 1 ,
b) from 10 to 500 parts of one or more powdery electrode-forming materials;
c) 100 parts of a solvent capable of dissolving said fluoropolymer.

Assignees

• Arkema Inc

Inventors

• Amin-Sanayei Ramin

Classifications

• C08F214/18

  Monomers containing fluorine · CPC title

• C08F14/22

  Vinylidene fluoride · CPC title

• C08F14/28

  Hexafluoropropene · CPC title

• H01M4/623

  fluorinated polymers · CPC title

• C08F214/186

  with non-fluorinated comonomers · CPC title