In-situ compatibilization of silicone rubber/polyolefin elastomer blends by forming ionomers for cold shrink splice and preparation method thereof

Patent metadata

Field	Value
Publication number	US-10150867-B2
Application number	US-201415322293-A
Country	US
Kind code	B2
Filing date	Jun 27, 2014
Priority date	Jun 27, 2014
Publication date	Dec 11, 2018
Grant date	Dec 11, 2018

Abstract

A cold shrink article made from a composition comprising (A) a silicone rubber; (B) an ethylene/α-olefin interpolymer; (C) a filler; and (D) an α,β-unsaturated carboxylic acid. The composition may optionally include additives selected from the group consisting of plasticizer, peroxide curing agent, antioxidant, process additives, flame retardant and combinations thereof.

First claim

The invention claimed is:

1. A composition comprising:
a resin blend comprising
(A) 60-80 parts of a silicone rubber per 100 parts of the resin blend (phr), and
(B) 20-40 phr of an ethylene/α-olefin interpolymer;
(C) 10-30 phr of a filler; and
(D) 0.5-3 phr of an α,β-unsaturated carboxylic acid.

2. A cold shrink article made from the composition of claim 1 .

3. The cold shrink article of claim 2 , the composition having an ACBD strength of greater than 20 kV/mm and a tear resistance of greater than or equal to 40 N/mm.

4. The cold shrink article of claim 2 , the composition comprising:
(A) 60-80 phr vinyl-terminated silicone rubber;
(B) 20-40 phr EPDM;
(C) 10-30 phr MgO;
(D) 0.5-3 phr MAA;
(E) 1-10 phr plasticizer;
(F) 0.1-5 phr peroxide curing agent;
(G) 0-10 phr antioxidant;
(H) 0-10 phr processing aid; and
(1) 0-50 phr flame retardant.

5. The cold shrink article of claim 2 having at least one of (a) tensile set of less than 20%, (b) an ACBD strength of greater than 25 kV/mm, and (c) a tear resistance of greater than 44 N/mm.

6. A cold shrink article comprising a shaped, stretched and cured composition comprising the composition of claim 1 .

7. A cable having an external layer and comprising a cold shrink splice, the splice shrunk about and in contact with the external layer of the cable and comprising a shaped and cured crosslinked composition, the composition comprising the composition of claim 1 .

8. A composition comprising:
a resin blend comprising
(A) 60-80 parts of a silicone rubber per 100 parts of the resin blend (phr), and
(B) 20-40 phr of an ethylene/α-olefin interpolymer;
(C) 10-30 phr of a filler; and
(D) 0.5-3 phr of an α,β-unsaturated carboxylic acid; and
having an ACBE strength of greater than 20 kV/mm and a tear resistance of greater than or equal to 40 N/mm.

9. The composition of claim 8 wherein the silicone rubber comprises a vinyl-terminated silicone rubber.

10. The composition of claim 8 wherein the ethylene/α-olefin interpolymer comprises EPDM.

11. The composition of claim 8 wherein the filler comprises a metal oxide or metal hydroxide.

12. The composition of claim 8 wherein the α,β-unsaturated carboxylic acid comprises methyl acrylic acid.

13. The composition of claim 8 having a Shore A hardness of from 30 to 70 and further comprising:
(E) 1-10 phr plasticizer;
(F) 0.1-5 phr peroxide curing agent;
(G) 0-10 phr antioxidant;
(H) 0-10 phr processing aid; and
(I) 0-50 phr flame retardant.

14. The composition of claim 13 comprising:
(A) 60-80 phr vinyl-terminated silicone rubber;
(B) 20-40 phr EPDM;
(C) 10-30 phr MgO;
(D) 0.5-3 phr MAA;
(E) 1-10 phr plasticizer;
(F) 0.1-5 phr peroxide curing agent;
(G) 0-10 phr antioxidant;
(H) 0-10 phr processing aid; and
(I) 0-50 phr flame retardant.

15. A method of splicing a cable comprising:
(1) providing a cold shrink article comprising a flexible sleeve made from a composition comprising (A) a silicone rubber; (B) an ethylene/α-olefin interpolymer; (C) a filler; and (D) an α,β-unsaturated carboxylic acid, wherein the flexible sleeve is held in radially expanded condition on a support core;
(2) inserting at least a portion of a cable inside the support core;
(3) removing the support core from the cold shrink article; and
(4) allowing the cold shrink article to contract onto the at least a portion of the cable.

Assignees

• Dow Global Technologies Llc
• Yu Haiyang
• Huo Yanli

Inventors

• Yu Haiyang
• Huo Yanli
• Esseghir Mohamed
• Sengupta Saurav
• Cogen Jeffrey

Classifications

• C08K3/22

  of metals · CPC title

• C08L83/04 Primary

  Polysiloxanes · CPC title

• C08L23/16

  Ethylene-propylene or ethylene-propylene-diene copolymers · CPC title

• C08K5/09

  Carboxylic acids; Metal salts thereof; Anhydrides thereof · CPC title

• C08L2203/202

  use in electrical wires or wirecoating · CPC title