Cementitious tile adhesive compositions containing crosslinked cellulose ethers for mortars with enhanced gel-strength

Patent metadata

Field	Value
Publication number	US-10150704-B2
Application number	US-201615567210-A
Country	US
Kind code	B2
Filing date	Jun 29, 2016
Priority date	Jun 30, 2015
Publication date	Dec 11, 2018
Grant date	Dec 11, 2018

Abstract

The present invention provides cementitious tile adhesives comprising ordinary Portland cement, sand or another inorganic filler, and from 0.12 to 0.6 wt. % of total solids of one or more polyether group containing crosslinked cellulose ethers. The present invention also provides methods of making the polyether group containing crosslinked cellulose ethers comprising crosslinking a cellulose ether at 90° C. or less, in an inert atmosphere, e.g. nitrogen, in the presence of a polyether group containing crosslinking agent and in the presence of alkali; the process may comprise part of a stepwise addition process of making of a cellulose ether itself in which the crosslinking of the cellulose ethers precedes at least one addition of alkyl halide or alkylene oxide to form, respectively, alkyl or hydroxyalkyl groups on the cellulose.

First claim

We claim:

1. A dry mix composition for use in making cementitious tile adhesives or mortars comprising from 20 to 35 wt. % of ordinary portland cement, from 64.7 to 79.9 wt. % of sand or an inorganic filler, and one or more crosslinked cellulose ethers containing polyether groups in the amount of from 0.12 to 0.6 wt. % of total solids.

2. The dry mix composition as claimed in claim 1 , wherein at least one of the one or more crosslinked cellulose ethers is a mixed cellulose ether that contains hydroxyalkyl groups and alkyl ether groups.

3. The dry mix composition as claimed in claim 2 , wherein the one or more crosslinked cellulose ethers is chosen from hydroxyethyl methylcellulose (NEMC), hydroxypropyl methylcellulose (HPMC), methyl hydroxyethyl hydroxypropylcellulose (MHEHPC), and ethylhydroxyethyl cellulose (EHEC).

4. The dry mix composition as claimed in claim 1 , wherein the polyether group in the crosslinked cellulose ethers is a polyoxyalkylene which has from 2 to 100 oxyalkylene groups.

5. The dry mix composition as claimed in claim 1 , wherein the polyether group in the crosslinked cellulose ethers is a polyoxyalkylene chosen from a polyoxyethylene, a polyoxypropylene and combinations thereof.

6. The dry mix composition as claimed in claim 1 , wherein the crosslinked cellulose ether is a polyoxypropylene group containing hydroxyethyl methylcellulose.

7. A method of using the dry mix compositions as claimed in claim 1 , comprising combining the dry mix composition with water or aqueous liquid to make a mortar, applying the mortar to an unfinished side or backside of one or more tiles, placing the mortar containing backside of the one or more tiles on a substrate, and letting the mortar set.

8. A method of making polyether group containing crosslinked cellulose ethers comprising crosslinking at 90° C. or less, in an inert atmosphere, a cellulose ether in the presence of a polyether group containing crosslinking agent in an amount of from 0.0001 to 0.05 eq to form a crosslinked polyether group containing cellulose ether, wherein the unit “eq” represents the molar ratio of moles of the respective crosslinking agent relative to the number of moles of anhydroglucose units (AGU) in the cellulose ether; and, granulating and drying the resulting crosslinked polyether group containing cellulose ether.

9. The method as claimed in claim 8 , wherein the polyether group containing crosslinking agent having two or more crosslinking groups chosen from halogen groups, glycidyl groups, epoxy groups, and ethylenically unsaturated groups that form ether bonds with the cellulose ether in crosslinking the cellulose ether.

10. The method as claimed in claim 8 , wherein the crosslinking of the cellulose ethers takes place in the reactor in which the cellulose ether itself is made and in the presence of caustic or alkali.

11. The method as claimed in claim 8 , wherein the crosslinking of the cellulose ethers precedes one or more addition of alkyl halide in the presence of alkali to form alkyl ethers of the cellulose.

Assignees

• Dow Global Technologies Llc

Inventors

• Hild Alexandra
• Neubauer Joerg
• Breckwoldt Joern

Classifications

• C04B24/386

  containing polyether side chains · CPC title

• C04B2111/00646

  Masonry mortars · CPC title

• C04B2111/00689

  of the setting type · CPC title

• C04B28/04 Primary

  Portland cements · CPC title

• C08B11/08

  with hydroxylated hydrocarbon radicals; Esters, ethers, or acetals thereof · CPC title