Photochromic glass with sharp cutoff

Patent metadata

Field	Value
Publication number	US-10150692-B2
Application number	US-201615354470-A
Country	US
Kind code	B2
Filing date	Nov 17, 2016
Priority date	Dec 18, 2015
Publication date	Dec 11, 2018
Grant date	Dec 11, 2018

Abstract

A photochromic glass that includes a base glass and a photochromic agent is described. The base glass is a modified boroaluminosilicate glass and the photochromic agent is a nanocrystalline cuprous halide phase. The photochromic glass exhibits a sharp cutoff in the UV or short wavelength visible portion of the spectrum along with an absorption band at longer wavelengths in the visible. The nanocrystalline cuprous halide phase includes Cu2+, which provides states within the bandgap of the cuprous halide that permit the glass to absorb visible light. Absorption of visible light drives a photochromic transition without compromising the sharp cutoff. The nanocrystalline cuprous halide phase may optionally include Ag.

First claim

What is claimed is:

1. A photochromic glass comprising:
a base glass, said base glass including 19 wt %-39 wt % B 2 O 3 , 0.5 wt %-15 wt % Al 2 O 3 , 46 wt %-65 wt % SiO 2 , 3.5 wt %-12.5 wt % alkali metal oxide, and 0.005 wt %-0.40 wt % SnO 2 ; and
0.56 wt %-1.28 wt % copper; and
0.1 wt %-0.7 wt % halide; and
a photochromic agent, said photochromic agent including a nanocrystalline cuprous halide phase within said base glass, said nanocrystalline cuprous halide phase including a copper component and a halide component, said copper component including at least a portion of said copper, said at least portion of said copper including Cu + and Cu 2+ , said halide component including at least a portion of said halide;
wherein said photochromic glass has a cutoff wavelength less than 410 nm.

2. The photochromic glass of claim 1 , wherein said base glass includes 22 wt %-35 wt % B 2 O 3 , 1.0 wt %-11 wt % Al 2 O 3 , 50 wt %-61 wt % SiO 2 , and 4.5 wt %-10.5 wt % alkali metal oxide.

3. The photochromic glass of claim 1 , wherein said base glass includes 24 wt %-33 wt % B 2 O 3 , 1.5 wt %-9 wt % Al 2 O 3 , 52 wt % -59 wt % SiO 2 , and 5.0 wt %-9.5 wt % alkali metal oxide.

4. The photochromic glass of claim 1 , wherein said alkali metal oxide is Na 2 O.

5. The photochromic glass of claim 1 , wherein said glass includes 0.64 wt %-1.12 wt % of said copper.

6. The photochromic glass of claim 1 , wherein said glass includes 0.72 wt %-0.96 wt % of said copper.

7. The photochromic glass of claim 1 , wherein said glass includes 0.01 wt %-1.20 wt % of said halide.

8. The photochromic glass of claim 1 , wherein said glass includes 0.10 wt %-0.60 wt % of said halide.

9. The photochromic glass of claim 1 , wherein said halide is Cl.

10. The photochromic glass of claim 9 , wherein said glass includes 0.01 wt %-0.80 wt % of said halide.

11. The photochromic glass of claim 9 , wherein said glass includes 0.05 wt %-0.50 wt % of said halide.

12. The photochromic glass of claim 1 , wherein said halide is a combination of Cl and Br.

13. The photochromic glass of claim 12 , wherein said glass includes 0.01 wt %-0.60 wt % of said Cl and 0.01 wt %-0.70 wt % of said Br.

14. The photochromic glass of claim 12 , wherein said glass includes 0.01 wt %-0.40 wt % of said Cl and 0.01 wt %-0.50 wt % of said Br.

15. The photochromic glass of claim 1 , wherein said nanocrystalline cuprous halide phase absorbs light over the wavelength range from 400 nm-575 nm.

16. The photochromic glass of claim 1 , wherein said nanocrystalline cuprous halide phase absorbs light over the wavelength range from 450 nm-525 nm.

17. The photochromic glass of claim 1 , wherein said glass exhibits an absorption edge, said absorption edge having a cutoff wavelength less than 420 nm.

18. The photochromic glass of claim 1 , wherein said glass exhibits an absorption edge, said absorption edge having a cutoff wavelength less than 400 nm.

19. The photochromic glass of claim 1 , wherein said glass exhibits an absorption edge, said absorption edge having a cutoff wavelength in the range from 370 nm-420 nm.

20. The photochromic glass of claim 1 , wherein said glass exhibits an absorption edge, said absorption edge having a cutoff wavelength in the range from 390 nm-405 nm.

21. The photochromic glass of claim 1 , wherein said glass exhibits an absorption edge, said absorption edge having a slope of at least 0.20 cm −1 /nm.

22. The photochromic glass of claim 21 , wherein said slope occurs at a wavelength in the range from 370 nm-420 nm.

23. The photochromic glass of claim 1 , wherein said glass exhibits an absorption edge, said absorption edge having a slope of at least 0.40 cm −1 /nm.

24. The photochromic glass of claim 23 , wherein said slope occurs at a wavelength in the range from 370 nm-420 nm.

25. The photochromic glass of claim 1 , wherein said glass further comprises silver, said nanocrystalline cuprous halide phase further including at least a portion of said silver.

26. The photochromic glass of claim 25 , wherein said nanocrystalline cuprous halide phase exhibits an absorption band having a peak wavelength in the range from 440 nm-540 nm.

27. The photochromic glass of claim 1 , wherein said glass has a cutoff wavelength less than or equal to 405 nm.

28. The photochromic glass of claim 1 , wherein said glass has a cutoff wavelength less than or equal to 400 nm.

29. The photochromic glass of claim 1 , wherein said glass has a cutoff wavelength less than or equal to 395 nm.

30. The photochromic glass of claim 1 , wherein said glass is uncolored.

31. The photochromic glass of claim 1 , wherein a sample of said glass having a thickness of 2 mm has a transmittance of 99% or greater for a wavelength range extending from said cutoff wavelength to a wavelength 25 nm above said cutoff wavelength.

32. The photochromic glass of claim 31 , wherein said sample has a transmittance of 1% or less for a wavelength range extending from said cutoff wavelength to a wavelength 25 nm below said cutoff wavelength.

33. The photochromic glass of claim 1 , wherein a sample of said glass having a thickness of 2 mm has a transmittance of 99% or greater for a wavelength range extending from said cutoff wavelength to a wavelength 50 nm above said cutoff wavelength.

34. The photochromic glass of claim 33 , wherein said sample has a transmittance of 1% or less for a wavelength range extending from said cutoff wavelength to a wavelength 50 nm below said cutoff wavelength.

35. The photochromic glass of claim 1 , wherein a sample of said glass having a thickness of 2 mm has a transmittance of 99% or greater for a wavelength range extending from said cutoff wavelength to a wavelength 100 nm above said cutoff wavelength.

36. The photochromic glass of claim 35 , wherein said sample has a transmittance of 1% or less for a wavelength range extending from said cutoff wavelength to a wavelength 75 nm below said cutoff wavelength.

37. The photochromic glass of claim 1 , wherein a sample of said glass having a thickness of 2 mm has a transmittance of 99% or greater for a wavelength range extending from said cutoff wavelength to a wavelength 200 nm above said cutoff wavelength.

38. The photochromic glass of claim 37 , wherein said sample has a transmittance of 1% or less for a wavelength range extending from said cutoff wavelength to a wavelength 25 nm below said cutoff wavelength.

39. The photochromic glass of claim 1 , further comprising WO 3 .

40. The photochromic glass of claim 39 , wherein said photochromic glass comprises 0.01 wt %-0.50 wt % WO 3 .

41. The photochromic glass of claim 39 , further comprising MoO 3 .

42. The photochromic glass of claim 39 , wherein said photochromic glass comprises 0.01 wt %-0.50 wt % MoO 3 .

43. The photochromic glass of claim 1 , further comprising MoO 3 .

44. The photochromic glass of claim 43 , wherein said photochromic glass comprises 0.01 wt %-0.50 wt % MoO 3 .

45. A photochromic glass comprising:
a base glass, said base glass including 19 wt %-39 wt % B 2 O 3 , 0.5 wt %-15 wt % Al

Assignees

• Corning Inc

Inventors

• Araujo Roger Jerome
• Borrelli Nicholas Francis
• Lönnroth Nadja Teresia
• Morse David Lathrop
• Seward Iii Thomas Philip

Classifications

• C03C2204/00

  Glasses, glazes or enamels with special properties · CPC title

• C03C4/065 Primary

  for silver-halide free photochromic glass · CPC title

• C03C3/11 Primary

  containing halogen or nitrogen · CPC title

• C03C14/006 Primary

  the non-glass component being in the form of microcrystallites, e.g. of optically or electrically active material · CPC title

• C03C4/085

  for ultraviolet absorbing glass · CPC title