Rubber composition containing fibrillated aramid fiber micropulp with pre-hydrophobated silica reinforcement and tire with component

Patent metadata

Field	Value
Publication number	US-10144819-B2
Application number	US-201715464435-A
Country	US
Kind code	B2
Filing date	Mar 21, 2017
Priority date	Apr 5, 2016
Publication date	Dec 4, 2018
Grant date	Dec 4, 2018

Abstract

This invention relates to a rubber composition comprised of at least one diene-based elastomer and rubber reinforcement comprised of fibrillated aramid fiber micropulp and reinforcing filler comprised of pre-hydrophobated precipitated silica. Such fibrillated aramid micropulp is comprised of micronized fibrillated aramid fiber pulp. Such pre-hydrophobated precipitated silica is comprised of precipitated silica pre-treated with at least one of bis(3-trialkylsilylalkyl) polysulfide, alkoxyorganomercaptosilane, optionally together with an alkylsilane. The invention further relates to such rubber composition wherein said reinforcing filler is comprised of a combination of said pre-hydrophobated precipitated silica as a precipitated silica pre-treated with an alkoxyorganomercaptosilane and a precipitated silica wherein said pre-hydrophobated precipitated silica and said precipitated silica are both hydrophobated in situ within the rubber composition with a bis(3-trialkoxysilylalkyl) polysulfide. The invention further relates to tires containing at least one component comprised of such rubber composition such as for example a tire tread.

First claim

What it claimed is:

1. A rubber composition is provided comprised of, based on parts by weight per 100 parts by weight rubber (phr):
(A) at least one conjugated diene-based elastomer,
(B) rubber reinforcement comprised of:
(1) about 0.1 to about 20 phr of fibrillated aramid fiber micropulp, and
(2) about 40 to about 120 phr of reinforcing filler comprised of rubber reinforcing carbon black and pre-hydrophobated precipitated silica comprised of from about 3 to about 45 phr of said rubber reinforcing carbon black;
wherein said pre-hydrophobated precipitated silica is precipitated silica pre-reacted with at least one of bis(3-trialkoxysilylalkyl) polysulfide having an average of from 2 to about 4 connecting sulfur atoms in its polysulfidic bridge, and alkoxyorganomercaptosilane and optionally an alkylsilane;
wherein said fibrillated aramid fiber micropulp has a volume average length in a range of from about 0.01 to about 100 mm (micrometers) and an average surface area in a range of from about 15 to about 500 square meter per gram.

2. The rubber composition of claim 1 wherein said bis(3-trialkoxysilylorgano) polysulfide is comprised of bis(3-triethoxysilylpropyl) polysulfide.

3. The rubber composition of claim 1 wherein said reinforcing filler contains up to about 50 percent precipitated silica.

4. The rubber composition of claim 1 wherein said reinforcing filler is comprised of up to about 20 percent of precipitated silica wherein said pre-hydrophobated precipitated silica is precipitated silica pre-treated with said alkoxyorganomercaptosilane and both of said precipitated silica and said pre-hydrophobated precipitated silica are hydrophobated in situ within the rubber composition with said bis(3-trialkoxysilylorgano) polysulfide.

5. The rubber composition of claim 1 wherein said pre-hydrophobated precipitated silica is a precipitated silica pre-treated with an organoalkoxymercaptosilane.

6. The rubber composition of claim 1 wherein said pre-hydrophobated precipitated silica is a precipitated silica pre-treated with at least one of triethoxy mercaptopropyl silane, trimethoxy mercaptopropyl silane, methyl dimethoxy mercaptopropyl silane, methyl diethoxy mercaptopropyl silane, dimethyl methoxy mercaptopropyl silane, triethoxy mercaptoethyl silane, tripropoxy mercaptopropyl silane, ethoxy dimethoxy mercaptopropylsilane, ethoxy diisopropoxy mercaptopropylsilane, ethoxy didodecyloxy mercaptopropylsilane and ethoxy dihexadecyloxy mercaptopropylsilane.

7. The rubber composition of claim 3 wherein said pre-hydrophobated precipitated silica is a precipitated silica pre-treated with an organoalkoxymercaptosilane and said bis(3-trialkoxysilylorgano) polysulfide is a bis(3-trialkoxysilylpropyl) polysulfide having an average of from about 2 to about 4 connecting sulfur atoms in its polysulfidic bridge.

8. The rubber composition of claim 3 wherein said pre-hydrophobated precipitated silica is a precipitated silica pre-treated with at least one of triethoxy mercaptopropyl silane, trimethoxy mercaptopropyl silane, methyl dimethoxy mercaptopropyl silane, methyl diethoxy mercaptopropyl silane, dimethyl methoxy mercaptopropyl silane, triethoxy mercaptoethyl silane, tripropoxy mercaptopropyl silane, ethoxy dimethoxy mercaptopropylsilane, ethoxy diisopropoxy mercaptopropylsilane, ethoxy didodecyloxy mercaptopropylsilane and ethoxy dihexadecyloxy mercaptopropylsilane.

9. A tire having a component comprised of the rubber composition of claim 1 .

10. A tire having a component comprised of the rubber composition of claim 2 .

11. A tire having a component comprised of the rubber composition of claim 3 .

12. A tire having a component comprised of the rubber composition of claim 4 .

13. A tire having a component comprised of the rubber composition of claim 5 .

14. A tire having a component comprised of the rubber composition of claim 6 .

15. A tire having a component comprised of the rubber composition of claim 7 .

16. A tire having a component comprised of the rubber composition of claim 8 .

17. A tire having a tread comprised of the rubber composition of claim 1 .

18. A tire having a tread comprised of the rubber composition of claim 2 .

19. A tire having a tread comprised of the rubber composition of claim 3 .

20. A tire having a tread comprised of the rubber composition of claim 4 .

Assignees

• Goodyear Tire & Rubber

Inventors

• Hahn Bruce Raymond
• Papakonstantopoulos George Jim
• Iverson Benjamin John

Classifications

• C08K9/04

  Ingredients treated with organic substances {(treated with macromolecular compounds C08K9/08)} · CPC title

• C08K5/31

  Guanidine; Derivatives thereof · CPC title

• C08K5/548

  containing sulfur {(C08K5/5477 takes precedence)} · CPC title

• B60C1/0016

  Compositions of the tread · CPC title

• C08L2205/03

  containing three or more polymers in a blend · CPC title