Sizing agent-coated carbon fibers, process for producing sizing agent-coated carbon fibers, prepreg, and carbon fiber reinforced composite material

Patent metadata

Field	Value
Publication number	US-10138593-B2
Application number	US-201214369136-A
Country	US
Kind code	B2
Filing date	Dec 18, 2012
Priority date	Dec 27, 2011
Publication date	Nov 27, 2018
Grant date	Nov 27, 2018

Abstract

Sizing agent-coated carbon fibers includes: a sizing agent including an aliphatic epoxy compound (A) and at least containing an aromatic epoxy compound (B1) as an aromatic compound (B); and carbon fibers coated with the sizing agent, wherein the sizing agent-coated carbon fibers have an (a)/(b) ratio of 0.50 to 0.90 where (a) is a height (cps) of a component at a binding energy (284.6 eV) assigned to CHx, C—C, and C═C and (b) is a height (cps) of a component at a binding energy (286.1 eV) assigned to C—O in a C 1s core spectrum of a surface of the sizing agent applied onto the carbon fibers analyzed by X-ray photoelectron spectroscopy using AlKα 1,2 as an X-ray source at a photoelectron takeoff angle of 15°.

First claim

The invention claimed is:

1. Sizing agent-coated carbon fibers comprising:
a sizing agent coating that includes:
an aliphatic epoxy compound (A) that has three or more epoxy groups and at least one hydroxy group in a molecule,
an aromatic epoxy compound (B1) as a type of aromatic compound (B), and
an aromatic ester compound (C1); and
carbon fibers coated with the sizing agent,

wherein
the sizing agent contains the aliphatic epoxy compound (A) in an amount of 35 to 65% by mass relative to the total amount of the sizing agent exclusive of solvent;
the sizing agent contains the aliphatic epoxy compound (A) and the aromatic epoxy compound (B1) in a mass ratio (A)/(B1) of 52/48 to 80/20;
the sizing agent contains the aromatic ester compound (C1) in an amount of 2 to 35% by mass relative to the total amount of the sizing agent exclusive of solvent;
each of the aliphatic epoxy compound (A) and the aromatic epoxy compound (B1) has a surface tension of 35 to 45 mJ/m 2 at 125° C.;
the sizing agent-coated carbon fibers have an (a)/(b) ratio of 0.50 to 0.90, wherein (a) is a height (cps) of a component at a binding energy (284.6 eV) assigned to CHx, C—C, and C═C and (b) is a height (cps) of a component at a binding energy (286.1 eV) assigned to C—C in a C 1s core spectrum of a surface of the sizing agent applied onto the carbon fibers analyzed by X-ray photoelectron spectroscopy using AlKα 1,2 as an X-ray source at a photoelectron takeoff angle of 15°; and
the carbon fibers have a surface carboxy group concentration COOH/C of 0.003 to 0.015 and a surface hydroxy group concentration COH/C of 0.001 to 0.050 determined by chemical modification X-ray photoelectron spectroscopy.

2. The sizing agent-coated carbon fibers according to claim 1 , wherein when the sizing agent-coated carbon fibers are subjected to ultrasonication in a mixed solvent of acetonitrile and chloroform to extract the applied sizing agent, the aliphatic epoxy compound (A) is extracted in a ratio of 0.3 part by mass or less relative to 100 parts by mass of the sizing agent-coated carbon fibers.

3. The sizing agent-coated carbon fibers according to claim 1 , wherein the sizing agent applied onto the carbon fibers has an epoxy equivalent of 350 to 550 g/eq.

4. The sizing agent-coated carbon fibers according to claim 1 , wherein the sizing agent contains the aromatic compound (B) in an amount of 35 to 60% by mass relative to a total amount of the sizing agent except a solvent.

5. The sizing agent-coated carbon fibers according to claim 1 , wherein the aliphatic epoxy compound (A) is a polyether polyepoxy compound having three or more epoxy groups in a molecule and/or a polyol polyepoxy compound having three or more epoxy groups in a molecule.

6. The sizing agent-coated carbon fibers according to claim 1 , wherein the aromatic epoxy compound (B1) is a bisphenol A epoxy compound or a bisphenol F epoxy compound.

7. The sizing agent-coated carbon fibers according to claim 1 , wherein relation (III):
0.50≤( I )≤0.90 and 0.6<( II )/( I )<1.0  (III)

is satisfied where (I) is a value of (a)/(b) of a surface of the sizing agent-coated carbon fibers before ultrasonication, (II) is the value of (a)/(b) of the surface of the sizing agent-coated carbon fibers of which an adhesion amount of the sizing agent is reduced to 0.09 to 0.20% by mass by ultrasonic cleaning of the sizing agent-coated carbon fibers in an acetone solvent, (a) is the height (cps) of a component at a binding energy (284.6 eV) assigned to CHx, C—C, and C═C, and (b) is the height (cps) of a component at a binding energy (286.1 eV) assigned to C—O in a C 1s core spectrum of the sizing agent-coated carbon fibers analyzed by X-ray photoelectron spectroscopy using an X-ray at 400 eV at a photoelectron takeoff angle of 55°.

8. The sizing agent-coated carbon fibers according to claim 1 , wherein the aliphatic epoxy compound (A) adheres onto the carbon fibers in an amount of 0.2 to 2.0% by mass relative to the sizing agent-coated carbon fibers.

9. Sizing agent-coated carbon fibers comprising:
a sizing agent that includes:
an aliphatic epoxy compound (A) that has three or more epoxy groups and at least one hydroxy group in a molecule,
an aromatic epoxy compound (B1) as a type of aromatic compound (B), and
an aromatic ester compound (C1) having no epoxy group in a molecule as a type of aromatic compound (B); and

carbon fibers coated with the sizing agent,

wherein
the sizing agent contains the aliphatic epoxy compound (A) in an amount of 35 to 65% by mass relative to the total amount of the sizing agent exclusive of solvent;
the sizing agent contains the aliphatic epoxy compound (A) and the aromatic epoxy compound (B1) in a mass ratio (A)/(B1) of 52/48 to 80/20;
the sizing agent contains the aromatic ester compound (C1) in an amount of 2 to 35% by mass relative to the total amount of the sizing agent exclusive of solvent;
each of the aliphatic epoxy compound (A) and the aromatic epoxy compound (B1) has a surface tension of 35 to 45 mJ/m 2 at 125° C.;
the aromatic ester compound (C1) is a condensate of an unsaturated dibasic acid and an alkylene oxide adduct of a bisphenol; and
the sizing agent-coated carbon fibers have an (a)/(b) ratio of 0.50 to 0.90, wherein (a) is a height (cps) of a component at a binding energy (284.6 eV) assigned to CHx, C—C, and C═C and (b) is a height (cps) of a component at a binding energy (286.1 eV) assigned to C—C in a C 1 core spectrum of a surface of the sizing agent applied onto the carbon fibers analyzed by X-ray photoelectron spectroscopy using ALKα 1,2 as an X-ray source at a photoelectron takeoff angle of 15°.

10. The sizing agent-coated carbon fibers according to claim 1 , wherein the aromatic ester compound (C1) is a condensate of maleic acid, sebacic acid, and an ethylene oxide adduct of bisphenol A.

11. The sizing agent-coated carbon fibers according to claim 9 , wherein the aromatic ester compound (C1) is a condensate of maleic acid, sebacic acid, and an ethylene oxide adduct of bisphenol A.

12. The sizing agent-coated carbon fibers according to claim 1 , wherein the sizing agent coating includes an innermost region adjacent to the carbon fiber and an outermost region away from the carbon fiber, and the aliphatic epoxy compound (A) is present in a larger amount in the innermost region, while the aromatic compound (B1) is present in a larger amount in the outermost region.

13. The sizing agent-coated carbon fibers according to claim 9 , wherein the sizing agent coating includes an innermost region adjacent to the carbon fiber and an outermost region away from the carbon fiber, and the aliphatic epoxy compound (A) is present in a larger amount in the innermost region, while the aromatic compound (B1) is present in a larger amount in the outermost region.

14. The sizing agent-coated carbon fibers according to claim 1 , wherein the aliphatic epoxy compound (A) and the aromatic epoxy compound (B1) have surface tensions which differ by 3 mJ/m 2 at 125° C. or less.

15. The sizing agent-coated carbon fibers according to claim 9 , wherein the aliphatic epoxy compound (A) and the aromatic epoxy compound (B1) have surface tensions which differ by 3 mJ/m 2 at 125° C. or less.

Assignees

• Toray Industries

Inventors

• Ichikawa Tomoko
• Endo Makoto
• Taiko Hiroshi
• Kobayashi Masanobu
• Arai Nobuyuki
• Misumi Jun

Classifications

• Y10T428/249944

  Fiber is precoated · CPC title

• D01F11/14

  with organic compounds, e.g. macromolecular compounds · CPC title

• D06M13/11

  Compounds containing epoxy groups or precursors thereof · CPC title

• C08J2363/00

  Characterised by the use of epoxy resins; Derivatives of epoxy resins · CPC title

• Y10T428/2918

  including free carbon or carbide or therewith [not as steel] · CPC title