Vinyl-based polymer and method of preparing the same

Patent metadata

Field	Value
Publication number	US-10138311-B2
Application number	US-201615512778-A
Country	US
Kind code	B2
Filing date	Jun 3, 2016
Priority date	Jun 5, 2015
Publication date	Nov 27, 2018
Grant date	Nov 27, 2018

Abstract

Provided are a vinyl chloride-based copolymer, as a secondary particle in which primary particles are assembled, which may exhibit excellent mechanical properties and transparency as well as excellent plasticity by having an average pore diameter of 100 nm or less and a porosity of 40 vol % or less, including 65 wt % to 97 wt % of a vinyl chloride-based monomer-derived repeating unit; and 3 wt % to 35 wt % of cis and trans isomers of an unsaturated fatty acid ester-derived repeating units, and including the repeating units respectively derived from the cis and trans isomers of the unsaturated fatty acid ester in a weight ratio of 60:40 to 99:1, and a method of preparing the same.

First claim

The invention claimed is:

1. A vinyl chloride-based copolymer as a secondary particle in which primary particles are assembled,
wherein the vinyl chloride-based copolymer has an average pore diameter of 100 nm or less and a porosity of 40 vol % or less,
comprises 65 wt % to 97 wt % of a vinyl chloride monomer-derived repeating unit based on 100 wt % of the vinyl chloride-based copolymer; and 3 wt % to 35 wt % of cis and trans isomers of an unsaturated fatty acid ester-derived repeating units based on 100 wt % of the vinyl chloride-based copolymer, and
comprises the repeating units respectively derived from the cis and trans isomers of the unsaturated fatty acid ester in a weight ratio of 60:40 to 99:1.

2. The vinyl chloride-based copolymer of claim 1 , wherein the unsaturated fatty acid ester is an unsaturated dicarboxylic acid ester.

3. The vinyl chloride-based copolymer of claim 1 , wherein the cis isomer of the unsaturated fatty acid ester is a compound of Formula 1, and the trans isomer of the unsaturated fatty acid ester is a compound of Formula 2:

in Formulae 1 and 2,
R 1 to R 4 are each independently selected from the group consisting of an alkyl group having 2 to 16 carbon atoms, a cycloalkyl group having 3 to 16 carbon atoms, and a combination thereof.

4. The vinyl chloride-based copolymer of claim 3 , wherein R 1 to R 4 are each independently a linear or branched alkyl group having 6 to 10 carbon atoms.

5. The vinyl chloride-based copolymer of claim 1 , wherein the vinyl chloride-based copolymer comprises 65 wt % to 80 wt % of the vinyl chloride monomer-derived repeating unit based on 100 wt % of the vinyl chloride-based copolymer; and 20 wt % to 35 wt % of the cis and trans isomers of the unsaturated fatty acid ester-derived repeating units based on 100 wt % of the vinyl chloride-based copolymer.

6. The vinyl chloride-based copolymer of claim 1 , wherein a polydispersity is in a range of 1.5 to 2.5.

7. The vinyl chloride-based copolymer of claim 1 , wherein a weight-average molecular weight is in a range of 70,000 g/mol to 300,000 g/mol, and a number-average molecular weight is in a range of 50,000 g/mol to 150,000 g/mol.

8. The vinyl chloride-based copolymer of claim 1 , wherein the vinyl chloride-based copolymer comprises:
65 wt % to 80 wt % of the vinyl chloride monomer-derived repeating unit based on 100 wt % of the vinyl chloride-based copolymer; and 20 wt % to 35 wt % of the cis and trans isomers of the unsaturated fatty acid ester-derived repeating units based on 100 wt % of the vinyl chloride-based copolymer, and
the repeating units respectively derived from the cis isomer and the trans isomer of the unsaturated fatty acid ester in a weight ratio of 85:15 to 99:1,
wherein the cis isomer of the unsaturated fatty acid ester is a compound of Formula 1, and the trans isomer of the unsaturated fatty acid ester is a compound of Formula 2:

in Formulae 1 and 2, R 1 to R 4 are each independently a linear or branched alkyl group having 6 to 10 carbon atoms.

9. The vinyl chloride-based copolymer of claim 1 , wherein the vinyl chloride-based copolymer further comprises a vinyl-based monomer-derived repeating unit, and
wherein the vinyl-based monomer is an olefin-based compound, vinyl esters, unsaturated nitriles, vinyl alkyl ethers, unsaturated fatty acids, or anhydrides of the unsaturated fatty acids, or a mixture of two or more thereof.

10. A method of preparing the vinyl chloride-based copolymer of claim 1 , the method comprising a polymerization of a vinyl chloride monomer with a cis isomer and a trans isomer of an unsaturated fatty acid ester in the presence of a polymerization initiator,
wherein the vinyl chloride monomer and the cis and trans isomers of the unsaturated fatty acid ester are used in amounts to provide 65 wt % to 97 wt % of a vinyl chloride monomer-derived repeating unit based on 100 wt % of the vinyl chloride-based copolymer and 3 wt % to 35 wt % of cis and trans isomers of the unsaturated fatty acid ester-derived repeating units based on 100 wt % of the vinyl chloride-based copolymer in the prepared vinyl chloride-based copolymer, and
the cis isomer and the trans isomer of the unsaturated fatty acid ester are used in a weight ratio of 60:40 to 99:1.

11. The method of claim 10 , wherein the vinyl chloride monomer and the cis and trans isomers of the unsaturated fatty acid ester are used in amounts to provide 65 wt % to 80 wt % of the vinyl chloride monomer-derived repeating unit based on 100 wt % of the vinyl chloride-based copolymer and 20 wt % to 35 wt % of the cis and trans isomers of the unsaturated fatty acid ester-derived repeating units based on 100 wt % of the vinyl chloride-based copolymer in the prepared vinyl chloride-based copolymer.

12. The method of claim 10 , wherein the cis isomer of the unsaturated fatty acid ester is a compound of Formula 1, and the trans isomer of the unsaturated fatty acid ester is a compound of Formula 2:

in Formulae 1 and 2,
R 1 to R 4 are each independently selected from the group consisting of an alkyl group having 2 to 16 carbon atoms, a cycloalkyl group having 3 to 16 carbon atoms, and a combination thereof.

13. The method of claim 10 , wherein the polymerization is performed in a temperature range of 52° C. to 58° C.

14. The method of claim 10 , wherein the polymerization is performed by suspension polymerization of the vinyl chloride monomer with the cis isomer and the trans isomer of the unsaturated fatty acid ester in a solvent in the presence of the polymerization initiator and a protective colloid auxiliary.

15. The method of claim 14 , wherein the protective colloid auxiliary comprises one selected from the group consisting of a vinyl alcohol-based resin, cellulose, and an unsaturated organic acid polymer, or a mixture of two or more thereof.

16. The method of claim 14 , wherein the protective colloid auxiliary comprises a mixture in which a vinyl alcohol-based resin and cellulose are mixed in a mixing ratio of 5:1 to 7:7, and
the vinyl alcohol-based resin comprises a mixture in which a first polyvinyl alcohol having a degree of hydration of greater than 50 wt % and equal to or less than 90 wt % and a second polyvinyl alcohol having a degree of hydration of 30 wt % to 50 wt % are mixed in a weight ratio of 2:1 to 1:2.

17. The method of claim 10 , wherein the polymerization is performed by emulsion polymerization of the vinyl chloride monomer with the cis isomer and the trans isomer of the unsaturated fatty acid ester in a solvent in the presence of the polymerization initiator and an emulsifier.

18. The method of claim 10 , wherein the polymerization is performed by solution polymerization of the vinyl chloride monomer with the cis isomer and the trans isomer of the unsaturated fatty acid ester in an inert organic solvent in the presence of the polymerization initiator.

19. The method of claim 10 , wherein the polymerization is performed by bulk polymerization of the vinyl chloride monomer with the cis isomer and the trans isomer of the unsaturated fatty acid ester in the presence of the polymerization initiator.

20. The method of claim 10 , wherein a vinyl-based monomer is furt

Assignees

• Lg Chemical Ltd

Inventors

• Ahn Seong Yong
• Kim Kun Ji
• Lee Se Woong

Classifications

• C08F14/06

  Vinyl chloride · CPC title

• C08F18/16

  with alcohols containing three or more carbon atoms · CPC title

• C08F214/06 Primary

  Vinyl chloride · CPC title

• C08F222/10 Primary

  Esters · CPC title

• C08F2/02

  Polymerisation in bulk · CPC title