Magnetic graphene

Patent metadata

Field	Value
Publication number	US-10134434-B2
Application number	US-201514918328-A
Country	US
Kind code	B2
Filing date	Oct 20, 2015
Priority date	Nov 14, 2014
Publication date	Nov 20, 2018
Grant date	Nov 20, 2018

Abstract

A method of making magnetic graphene comprising transferring or growing a graphene film on a substrate, functionalizing the graphene film, hydrogenating the graphene film and forming fully hydrogenated graphene, manipulating the extent of the hydrogen content, and forming areas of magnetic graphene and non-magnetic graphene. A ferromagnetic graphene film comprising film that has a thickness of less than two atom layers thick.

First claim

What we claim is:

1. A method of making patterned magnetic graphene, comprising:
transferring or growing a graphene film on a substrate;
functionalizing the graphene film;
hydrogenating the graphene film and forming fully hydrogenated graphene;
manipulating the extent of the hydrogen content by using an electron beam from a scanning electron microscope to selectively remove hydrogen, wherein the step of selectively removing hydrogen occurs under a vacuum; and
forming areas of magnetic graphene and non-magnetic graphene.

2. The method of making patterned magnetic graphene of claim 1 , wherein the step of forming areas of magnetic graphene and non-magnetic graphene comprise the steps of forming an area of fully hydrogenated graphene, forming an area of partially hydrogenated graphene, and forming an area of graphene.

3. The method of making patterned magnetic graphene of claim 2 , wherein the area of highly hydrogenated graphene is non-magnetic and the area of graphene is non-magnetic and the area of partially hydrogenated graphene is magnetic.

4. The method of making patterned magnetic graphene of claim 1 wherein the step of hydrogenating the graphene film comprises reacting the graphene film with anhydrous liquid ammonia and lithium.

5. The method of making patterned magnetic graphene of claim 4 wherein the graphene film reacts with the anhydrous liquid ammonia and lithium for about 5 to about 2 minutes.

Assignees

• Us Navy

Inventors

• Lee Woo K
• Whitener Keith E
• Sheehan Paul E

Classifications

• G11B5/84 Primary

  Processes or apparatus specially adapted for manufacturing record carriers · CPC title

• B05D5/00

  Processes for applying liquids or other fluent materials to surfaces to obtain special surface effects, finishes or structures · CPC title

• C01B31/0446

  Chemistry & Metallurgy · mapped topic

• H01F1/42 Primary

  of organic or organo-metallic materials {, e.g. graphene}(H01F1/44 takes precedence) · CPC title

• G11B5/65

  characterised by its composition (G11B5/66 takes precedence) · CPC title