Thermomechanical rolling of an aluminum plate

Patent metadata

Field	Value
Publication number	US-10131979-B2
Application number	US-201314397084-A
Country	US
Kind code	B2
Filing date	Apr 17, 2013
Priority date	Apr 26, 2012
Publication date	Nov 20, 2018
Grant date	Nov 20, 2018

Abstract

In a rolling process for reverse thermomechanically rolling an aluminum plate involving a plurality of rolling passes, identifying data are determined for thermally guiding the rolling process. Then a value of a state variable, from which a temperature of the aluminum plate can be deduced, is continuously measured and a pass schedule is determined for the rolling process on the basis of the value of the measured state variable and of the identifying data. The pass schedule provides for a rolling pause between at least two successive rolling passes, during which rolling of the aluminum plate is interrupted for cooling purposes.

First claim

The invention claimed is:

1. A method for reversing thermomechanical rolling of an aluminum plate in a rolling process including a plurality of rolling passes, comprising:
specifying characteristic data, including a microstructure of the aluminum plate, a waiting thickness of the aluminum plate assigned to at least one rolling pass and at least one of rolling restart temperatures, a target temperature, a cooling temperature, and a cooling rate, for thermally controlling the rolling process;
continuously determining values of at least one state variable including measured surface temperature profiles of the aluminum plate, from which a temperature of the aluminum plate can be derived;
determining a pass schedule for the rolling process as a function of the characteristic data, including the waiting thickness of the aluminum plate assigned to at least one rolling pass and the at least one of rolling restart temperatures, the target temperature, the cooling temperature, and the cooling rate ,and the values of the at least one state variable obtained by said determining, including measured surface temperature profiles of the aluminum plate, the pass schedule making provision for a rolling pause between at least two successive rolling passes that starts as soon as a measured thickness of the aluminum plate is no longer above the waiting thickness assigned to a completed rolling pass, where during the rolling pause rolling of the aluminum plate is interrupted to allow the aluminum plate to cool down; and
controlling the rolling process in accordance with the pass schedule, based on temperatures measured at different locations on the aluminum plate and the characteristic data, including the waiting thickness of the aluminum plate assigned to at least one rolling pass and the at least one of rolling restart temperatures, the target temperature, the cooling temperature, and the cooling rate.

2. The method as claimed in claim 1 ,
wherein the characteristic data assigns a rolling restart temperature of the aluminum plate to at least one rolling pause, and
wherein the pass schedule makes provision for the rolling pause to terminate as soon as the temperature of the aluminum plate reaches the rolling restart temperature.

3. The method as claimed claim 1 ,
wherein the characteristic data includes a target temperature, and
wherein the pass schedule determines a duration of at least one of the rolling pause and a rolling restart temperature of the aluminum plate after the rolling pause so that the temperature of the aluminum plate after a final rolling pass coincides with the target temperature.

4. The method as claimed claim 1 , wherein the state variable is at least one of a temperature averaged over the measured thickness of the aluminum plate, a surface temperature, a residual hardening, phase fractions, grain sizes, and an enthalpy of the aluminum plate.

5. The method as claimed claim 1 ,
wherein the characteristic data includes a cooling temperature, and
further comprising, after a final rolling pass, supplying the aluminum plate to a cooling unit and cooling to the cooling temperature by the cooling unit.

6. The method as claimed in claim 5 ,
wherein the characteristic data includes a cooling rate, and
wherein in said cooling after the final rolling pass, the aluminum plate is cooled down to the cooling temperature at the cooling rate by the cooling unit.

7. The method as claimed claim 1 , further comprising, performing at least one rolling pass of another aluminum plate during at least one rolling pause.

8. The method as claimed claim 1 ,
further comprising predefining a rolling force threshold value as a function of at least one state variable of the aluminum plate, and
wherein the pass schedule limits a rolling force during the rolling operation to a respective rolling force threshold value as a function of the values of the at least one state variable.

9. The method as claimed in claim 8 , wherein the measured thickness of the aluminum plate is used as a state variable.

10. The method as claimed claim 1 ,
further comprising predefining a thickness reduction threshold value as a function of at least one state variable of the aluminum plate, and
wherein the pass schedule limits a reduction of the measured thickness of the aluminum plate during each rolling pass to a respective thickness reduction threshold value as a function of the values of the at least one state variable.

11. The method as claimed in claim 10 , wherein the measured thickness of the aluminum plate is used as a state variable.

12. The method as claimed claim 1 , further comprising cooling the aluminum plate by a cooling unit during at least one rolling pause.

13. The method as claimed claim 1 ,
further comprising continuously acquiring measured values of at least one measurement variable associated with a temperature of the aluminum plate, and
wherein the values of the at least one state variable are determined based on the measured values by a temperature model evaluating the measured values.

14. The method as claimed claim 1 , further comprising constantly updating the pass schedule.

Assignees

• Siemens Ag
• Primetals Technologies Germany Gmbh

Inventors

• Kurz Matthias
• Schmidt Birger

Classifications

• B21B38/006

  for measuring temperature · CPC title

• C22F1/04 Primary

  of aluminium or alloys based thereon · CPC title

• B21B2201/06

  Thermomechanical rolling · CPC title

• B21B3/00

  Rolling materials of special alloys so far as the composition of the alloy requires or permits special rolling methods or sequences {; Rolling of aluminium, copper, zinc or other non-ferrous metals}(altering special metallurgical properties of alloys, other than structure consolidation or mechanical properties resulting therefrom C21D, C22F) · CPC title

• B21B2003/001

  Aluminium or its alloys · CPC title