Liquid (meth)acrylic syrup for impregnating a fibrous substrate, method of impregnating a fibrous substrate, composite material obtained following polymerisation of the pre-impregnated substrate

Patent metadata

Field	Value
Publication number	US-10131768-B2
Application number	US-201414774186-A
Country	US
Kind code	B2
Filing date	Mar 10, 2014
Priority date	Mar 11, 2013
Publication date	Nov 20, 2018
Grant date	Nov 20, 2018

Abstract

The present invention relates to a liquid (meth)acrylic syrup for impregnating a fibrous substrate. The present invention relates in particular to a viscous liquid syrup mainly containing methacrylic or acrylic components. The invention also relates to a process for manufacturing such a syrup. The invention also relates to a process for impregnating a fibrous substrate or long fibers with said viscous liquid syrup. The invention also relates to a fibrous substrate preimpregnated with said syrup, which is useful for manufacturing mechanical or structured parts or products.
The present invention also relates to a manufacturing process for manufacturing mechanical or structured parts or articles and to three-dimensional mechanical or structured parts obtained by this process.
The invention applies to the preparation of mechanical parts or structural elements made of fire-resistant thermoplastic composite material.

First claim

The invention claimed is:

1. A liquid (meth)acrylic syrup for impregnating a fibrous substrate, said fibrous substrate consisting of long fibers having a diameter of from 1 to 50 micron and an aspect ratio of at least 10000, wherein said syrup comprises:
a) a (meth)acrylic polymer, having a weight-average molecular weight of greater than 50,000 g/mol.
b) a (meth)acrylic monomer,
c) at least one flame-retardant substance selected from the group consisting of
phosphorus-based additives selected from phosphinates, diphosphinates, phosphonates, phosphates, red phosphorus, ammonium polyphosphates with a number of units n of at least 1000, and
hydrated mineral fillers,

the overall content of flame-retardant substance in said liquid (meth)acrylic syrup being from 5% to less than 50% by weight, said liquid (meth)acrylic syrup having a dynamic viscosity of between 10 mPa·s and 10 000 mPa·s,
wherein the flame-retardant substance(s) are in the form of particles with a mean diameter D 50 of between 0.5 and 10 μm.

2. The liquid (meth)acrylic syrup as claimed in claim 1 , wherein the phosphorus-based additives are chosen from phosphinates or diphosphinates of formula (I) or (II):

in which:
R 1 and R 2 denote a linear or branched C 1 -C 6 alkyl and/or aryl group;
R 3 denotes a linear or branched C 1 -C 10 alkylene, C 6 -C 10 arylene, alkylarylene or arylalkylene group;
M denotes Mg, Ca, Al, Sb, Sn, Ge, Ti, Zn, Fe, Zr, Ce, Bi, Sr, Mn, Li, Na or K;
m is an integer between 1 and 4;
n is an integer between 1 and 4;
x is an integer between 1 and 4.

3. The liquid (meth)acrylic syrup as claimed in claim 2 , wherein R 1 and R 2 are methyl, ethyl, n-propyl, isopropyl, n-butyl, tert-butyl, n-pentyl and/or phenyl groups.

4. The liquid (meth)acrylic syrup as claimed in claim 2 , wherein R 3 is a methylene, ethylene, n-propylene, isopropylene, n-butylene, tert-butylene, n-pentylene, n-octylene or n-dodecylene group; or a phenylene, methylphenylene, ethylphenylene, tert-butylphenylene, methylnaphthylene, phenylmethylene, phenylethylene, phenylpropylene or naphthalene group.

5. The liquid (meth)acrylic syrup as claimed in claim 2 , wherein the phosphorus-based additive is of formula (I) and M denotes Al and R 1 and R 2 both denote a C 1 -C 6 alkyl group.

6. The liquid (meth)acrylic syrup as claimed in claim 5 , wherein the flame-retardant additive has the formula (III) or (IV):

7. The liquid (meth)acrylic syrup as claimed in claim 2 , wherein said flame-retardant additive of formula (I) or (II) represents from 10% to 30% by weight of the (meth)acrylic syrup.

8. The liquid (meth)acrylic syrup as claimed in claim 1 , wherein the hydrated mineral fillers consist of aluminum trihydrate or magnesium hydroxide.

9. The liquid (meth)acrylic syrup as claimed in claim 8 , wherein the hydrated mineral fillers consist of aluminum trihydrate.

10. The liquid (meth)acrylic syrup as claimed in claim 8 , wherein the hydrated mineral fillers represent from 10% to 30% by weight of the (meth)acrylic syrup.

11. The liquid (meth)acrylic syrup as claimed in claim 1 , wherein said syrup comprises one or more additives selected from the group consisting of fumed silica, clays/bentonites; inorganic fillers, magnesium carbonate, calcium carbonate, magnesium oxide, calcium oxide, hydrotalcite, dihydrotalcite, calcium hydroxide, talc (dihydroxylated magnesium silicate), metal oxides, zinc oxide, aluminum oxide, titanium oxides, antimony trioxide, and antimony tartrate, which reinforce the efficacy of the flame-retardant substance.

12. The liquid (meth)acrylic syrup as claimed in claim 1 , wherein the (meth)acrylic polymer is a homo- or copolymer of methyl methacrylate (MMA) or a mixture thereof.

13. The liquid (meth)acrylic syrup as claimed in claim 12 , wherein the copolymer of methyl methacrylate (MMA) comprises at least 70%, by weight of methyl methacrylate (MMA).

14. The liquid (meth)acrylic syrup as claimed in claim 12 , wherein the copolymer of methyl methacrylate (MMA) comprises from 70% to 99.7% by weight of methyl methacrylate and from 0.3 to 30% by weight of at least one monomer bearing at least one ethylenic unsaturation that can copolymerize with methyl methacrylate.

15. The liquid (meth)acrylic syrup as claimed in claim 12 , wherein the (meth)acrylic polymer comprises a comonomer, said comonomer being an alkyl acrylate containing an alkyl group of 1 to 12 carbon atoms.

16. The liquid (meth)acrylic syrup as claimed in claim 15 , wherein the comonomer is chosen from methyl acrylate, ethyl acrylate, and a mixture thereof.

17. The liquid (meth)acrylic syrup as claimed in claim 1 , wherein the (meth)acrylic monomer is chosen from acrylic acid, methacrylic acid, alkyl acrylic monomers, alkyl methacrylic monomers, and mixtures thereof, wherein said alkyl group in said alkyl acrylate or alkyl methacrylate containing from 1 to 22 linear, branched or cyclic carbons.

18. The liquid (meth)acrylic syrup as claimed in claim 17 , wherein the (meth)acrylic monomer selected from the group consisting of methyl methacrylate, ethyl methacrylate, methyl acrylate, ethyl acrylate, methacrylic acid, acrylic acid, n-butyl acrylate, isobutyl acrylate, n-butyl methacrylate, isobutyl methacrylate, cyclohexyl acrylate, cyclohexyl methacrylate, isobornyl acrylate and isobornyl methacrylate, and mixtures thereof.

19. The liquid (meth)acrylic syrup as claimed claim 17 , wherein the (meth)acrylic monomer is chosen from methyl methacrylate, isobornyl acrylate, acrylic acid, and mixtures thereof.

20. The liquid (meth)acrylic syrup as claimed in claim 17 , wherein 50% by weight of the (meth)acrylic monomer is methyl methacrylate.

21. The liquid (meth)acrylic syrup as claimed in claim 1 , wherein the (meth)acrylic polymer in the liquid (meth)acrylic syrup is present in a content of at least 1% by weight of the total liquid (meth)acrylic syrup.

22. The liquid (meth)acrylic syrup as claimed in claim 1 , wherein the (meth)acrylic polymer in the liquid (meth)acrylic syrup is present in a content of not more than 50% by weight of the total liquid (meth)acrylic syrup.

23. The liquid (meth)acrylic syrup as claimed in claim 1 , wherein the (meth)acrylic monomer in the liquid (meth)acrylic syrup is present in proportions of between 40% and 80% by weight of the total liquid (meth)acrylic syrup.

24. The liquid (meth)acrylic syrup as claimed in claim 2 , wherein the liquid (meth)acrylic syrup comprises:
a) from 5% by weight to 20% by weight of a (meth)acrylic polymer,
b) from 40% by weight to 80% by weight of a (meth)acrylic monomer,
c) from 10% by weight to 30% by weight of a phosphorus-based additives of formula (I) or (II), and/or
d) from 15% by weight to 50% by weight of aluminum trihydrate.

25. An impregnation process for impregnating a fibrous substrate, said fibrous substrate consisting of long fibers and said process comprising a step of impregnating said fibrous substrate with said (meth)acrylic syrup as claimed in claim 1 .

26. The impregnation process as claimed in claim 25 , wherein the step of impregnating said fibrous substrate is performed in a closed mold.

27. A polymeric composite material comprising a

Assignees

• Arkema France
• Pole De Plasturgie De Lest
• Univ De Lorraine

Inventors

• Gerard Pierre
• Glotin Michel
• Cauchois Jean-Pierre
• Quinten Claire
• Mihaluta Marius
• Lin Qing
• Ferriol Michel
• Cochez Marianne

Classifications

• C08L33/12

  Homopolymers or copolymers of methyl methacrylate · CPC title

• B29L2031/30

  Vehicles, e.g. ships or aircraft, or body parts thereof {(vanes or blades B29L2031/08, air bags B29L2022/027)} · CPC title

• C08J5/24

  Impregnating materials with prepolymers which can be polymerised in situ, e.g. manufacture of prepregs · CPC title

• B29K2505/02

  Aluminium · CPC title

• B29C70/021 Primary

  Combinations of fibrous reinforcement and non-fibrous material · CPC title