Powder primer composition and laminate using it

Patent metadata

Field	Value
Publication number	US-10113068-B2
Application number	US-201615096550-A
Country	US
Kind code	B2
Filing date	Apr 12, 2016
Priority date	Dec 11, 2013
Publication date	Oct 30, 2018
Grant date	Oct 30, 2018

Abstract

To provide a powder primer composition excellent in adhesion properties and a laminate obtained by using it. The power primer composition comprises a powder made of a reactive ethylene/tetrafluoroethylene copolymer containing repeating units (A) based on tetrafluoroethylene, repeating units (B) based on ethylene, and repeating units (C) based on a monomer having an acid anhydride residue and a polymerizable unsaturated bond, wherein (C)/((A)+(B)) is from 1/10,000 to 5/100 by molar ratio; and a powder made of an epoxy resin having an epoxy equivalent of from 500 to 2,700 and a softening point of at least 70° C.; wherein the mass ratio of the powder made of a reactive ethylene/tetrafluoroethylene copolymer to the powder made of an epoxy resin is from 99/1 to 80/20.

First claim

What is claimed is:

1. A powder primer composition comprising:
a powder made of a reactive ethylene/tetrafluoroethylene copolymer containing repeating units (A) based on tetrafluoroethylene, repeating units (B) based on ethylene, and repeating units (C) based on a monomer having an acid anhydride residue and a polymerizable unsaturated bond, wherein a ratio (C)/((A)+(B)) is from 1/10,000 to 5/100 by molar ratio; and
a powder made of an epoxy resin having an epoxy equivalent of from 500 to 2,700 and a softening point of at least 70° C.;
wherein a mass ratio of the powder made of a reactive ethylene/tetrafluoroethylene copolymer to the powder made of an epoxy resin is from 99/1 to 80/20,
wherein an average particle size of the powder made of a reactive ethylene/tetrafluoroethylene copolymer is from 1 to 1,000 μm, an average particle size of the powder made of the an epoxy resin is from 1 to 1,000 μm, and a ratio of the average particle size of the powder made of the epoxy resin to the average particle size of the reactive ethylene/tetrafluoroethylene copolymer is from 0.575 to 2.30,
wherein the powder primer composition is prepared by dry blending component powders, and
wherein no formation of nodules is observed in the powder primer composition.

2. The powder primer composition of claim 1 , wherein an average particle size of the powder primer composition is from 1 to 1,000 μm.

3. The powder primer composition of claim 1 , wherein an average particle size of the powder primer composition is from 1 to 300 μm.

4. A laminate comprising a primer layer which is a heat-treated product of the powder primer composition of claim 1 and a top coating layer made of a fluororesin, laminated in this order on a surface of a substrate.

5. The laminate of claim 4 , wherein the peel strength of the top coating layer to the substrate is at least 20 N/cm.

6. The powder primer composition of claim 1 , wherein a bulk density of the primer composition is from 0.4 to 1.2 g/cc.

7. The powder primer composition of claim 1 , wherein an angle of repose of the primer composition is from 20 to 52 degrees.

8. The powder primer composition of claim 1 , wherein the monomer having an acid anhydride residue and a polymerizable unsaturated bond is at least one selected from the group consisting of maleic anhydride, itaconic anhydride, citraconic anhydride, and 5-norbomene-2,3-dicarboxylic anhydride.

9. The powder primer composition of claim 1 , wherein the ration (C)/((A)+(B)) is from 3/1,000 to 3/100.

10. The powder primer composition of claim 1 , wherein a ratio of (A) to (B), (A)/(B), is from 20/80 to 80/20 by mass.

11. The powder primer composition of claim 1 , wherein the reactive ethylene/tetrafluoroethylene copolymer comprises repeating units (D) that are different from the repeating units (A), (B), and (C).

12. The powder primer composition of claim 1 , wherein the softening point of the epoxy resin is from 80 to 140° C.

13. The powder primer composition of claim 1 , wherein the softening point of the epoxy resin is from 90 to 130° C.

14. The powder primer composition of claim 1 , wherein a molecular weight of the epoxy resin is from 1,000 to 3,500.

15. The powder primer composition of claim 1 , wherein the epoxy equivalent of the powder is from 700 to 2,300.

16. The powder primer composition of claim 1 , wherein the epoxy equivalent of the powder is from 900 to 2,000.

17. The powder primer composition of claim 1 , wherein the mass ratio of the powder made of the reactive ethylene/tetrafluoroethylene copolymer to the powder made of the epoxy resin is from 98/2 to 85/15.

18. The powder primer composition of claim 1 , wherein the mass ratio of the powder made of the reactive ethylene/tetrafluoroethylene copolymer to the powder made of the epoxy resin is from 97/3 to 88/1.

Assignees

• Asahi Glass Co Ltd
• Agc Inc

Inventors

• Hoshikawa Jun
• Tate Noriharu
• Susa Hitoshi

Classifications

• C09D5/031

  characterised by particle size or shape · CPC title

• C09D163/00

  Coating compositions based on epoxy resins; Coating compositions based on derivatives of epoxy resins · CPC title

• C09D127/18 Primary

  Homopolymers or copolymers of tetrafluoroethene · CPC title

• C08L27/18

  Homopolymers or copolymers or tetrafluoroethene · CPC title

• C08L63/00

  Compositions of epoxy resins; Compositions of derivatives of epoxy resins · CPC title