Rubber composition manufacturing method and tire manufacturing method

Patent metadata

Field	Value
Publication number	US-10106674-B2
Application number	US-201615218532-A
Country	US
Kind code	B2
Filing date	Jul 25, 2016
Priority date	Aug 27, 2015
Publication date	Oct 23, 2018
Grant date	Oct 23, 2018

Abstract

[PROBLEM] To provide a method for manufacturing a rubber composition that will serve as raw material for vulcanized rubber which excels in tear resistance, wet performance, and ability to achieve reduced heat generation.
[SOLUTION MEANS] Manufacture of a tire or of a rubber composition by means of a method comprising an operation in which (a) a wet master batch comprising a first rubber and a first carbon black, (b) a second rubber comprising styrene-butadiene rubber, and (c) a second carbon black are dry-blended together under specific conditions.

First claim

The invention claimed is:

1. A method for manufacturing a rubber composition comprising:
forming a wet master batch, wherein the wet master batch comprises a first carbon black and a first rubber comprising natural rubber, polyisoprene rubber, or both; and then
kneading the wet master batch, a second rubber and a second carbon black
wherein the second rubber comprises styrene-butadiene rubber, wherein the kneading is performed under conditions satisfying both Formula I and Formula II;
wherein Formula I is 0.40≤A/C≤1.20;
wherein A is an amount of the first carbon black for every 100 parts by mass of the first rubber, and C is an amount of the first carbon black and the second carbon black combined for every 100 parts by mass of the first rubber and the second rubber combined;
wherein Formula II is 0.80≤(B/D)×100/C≤1.30;
wherein B is an amount of the second carbon black for every 100 parts by mass of the first rubber and the second rubber combined, and D is an amount of the second rubber for every 100 parts by mass of the first rubber and the second rubber combined;
wherein, in the kneading, the styrene-butadiene rubber is present in an amount that is not less than 10 parts by mass for every 100 parts by mass of the first rubber and the second rubber combined;
wherein, in the kneading, the first rubber is present in an amount that is not less than 20 parts by mass for every 100 parts by mass of the first rubber and the second rubber combined.

2. The method for manufacturing a rubber composition according to claim 1 , wherein the styrene-butadiene rubber has a glass transition temperature that is −60° C. to 0° C.

3. A rubber composition obtained by the method for manufacturing the rubber composition according to claim 1 .

4. A tire comprising the rubber composition according to claim 3 .

5. The method for manufacturing a rubber composition according to claim 1 , wherein the second carbon black is selected from a group consisting of SAF, ISAF, HAF, FEF, GPF, acetylene black and Ketchen black.

6. The method for manufacturing a rubber composition according to claim 1 , wherein the first carbon black is selected from a group consisting of SAF, ISAF, HAF, FEF, GPF, acetylene black and Ketchen black.

7. A method for manufacturing a tire comprising:
forming a wet master batch, wherein the wet master batch comprises a first carbon black and a first rubber comprising natural rubber, polyisoprene rubber, or both;
kneading the wet master batch, a second rubber and a second carbon black wherein the second rubber comprises styrene-butadiene rubber to manufacture a rubber composition; and making a green tire comprising the rubber composition;
wherein the kneading is performed under conditions satisfying both Formula I and Formula II;
wherein Formula I is 0.40≤A/C≤1.20;
wherein A is an amount of the first carbon black for every 100 parts by mass of the first rubber, and C is an amount of the first carbon black and the second carbon black combined for every 100 parts by mass of the first rubber and the second rubber combined;
wherein Formula II is 0.80≤(B/D)×100/C≤1.30;
wherein B is an amount of the second carbon black for every 100 parts by mass of the first rubber and the second rubber combined, and D is an amount of the second rubber for every 100 parts by mass of the first rubber and the second rubber combined;
wherein, in the kneading, the styrene-butadiene rubber is present in an amount that is not less than 10 parts by mass for every 100 parts by mass of the first rubber and the second rubber combined;
wherein, in the kneading, the first rubber is present in an amount that is not less than 20 parts by mass for every 100 parts by mass of the first rubber and the second rubber combined.

8. The method for manufacturing a rubber composition according to claim 1 , wherein the first rubber comprises natural rubber and polyisoprene.

9. The method for manufacturing a rubber composition according to claim 1 , wherein, in the kneading, the first carbon black is present in an amount that is not less than 10 parts by mass and not more than 80 parts by mass for every 100 parts by mass of the first rubber.

10. The method for manufacturing a rubber composition according to claim 1 , wherein, in the kneading, the styrene-butadiene is present in an amount that is not less than 60 parts by mass for every 100 parts by mass of the second rubber.

11. The method for manufacturing a rubber composition according to claim 1 , wherein, in the kneading, the styrene-butadiene rubber is present in an amount that is not less than 30 parts by mass for every 100 parts by mass of the first rubber and the second rubber combined.

12. The method for manufacturing a rubber composition according to claim 1 , wherein, in the kneading, the styrene-butadiene rubber is present in an amount that is not more than 80 parts by mass for every 100 parts by mass of the first rubber and the second rubber combined.

13. The method for manufacturing a rubber composition according to claim 1 , wherein the kneading further comprises an additive selected from the group consisting of oil, stearic acid, zinc oxide, antioxidant, silica and silane coupling agent.

Assignees

• Toyo Tire & Rubber Co

Inventors

• Nishimura Chiya

Classifications

• C08L9/00 Primary

  Compositions of homopolymers or copolymers of conjugated diene hydrocarbons · CPC title

• C08L7/02

  Latex · CPC title

• C08K3/04

  Carbon · CPC title

• C08L2666/55

  Carbon · CPC title

• C08L9/06

  Copolymers with styrene · CPC title