Resin additive masterbatch and polyolefin resin composition to which said resin additive masterbatch has been admixed

Patent metadata

Field	Value
Publication number	US-10100173-B2
Application number	US-201414780841-A
Country	US
Kind code	B2
Filing date	Mar 7, 2014
Priority date	Mar 29, 2013
Publication date	Oct 16, 2018
Grant date	Oct 16, 2018

Abstract

The resin additive masterbatch is characterized by comprising, with respect to 100 parts by mass of (A) a polyolefin resin: 50 to 200 parts by mass of (B) a resin additive having a melting point of not higher than 65° C.; and 10 to 20 parts by mass of (C) an inorganic layered compound.

First claim

The invention claimed is:

1. A resin additive masterbatch, characterized by comprising, with respect to 100 parts by mass of (A) a polyolefin resin:
50 to 200 parts by mass of (B) a resin additive comprising at least one hindered amine and having a melting point of not higher than 65° C.; and
10 to 20 parts by mass of (C) at least one inorganic layered compound selected from talc, mica, kaolin or hydrotalcite;
at least one aromatic metal phosphate represented by the following Formula (3):

wherein R 6 represents a hydrogen atom or an alkyl group having 1 to 8 carbon atoms; R 7 represents an alkyl group having 4 to 8 carbon atoms; R 8 represents an alkylidene group having 1 to 4 carbon atoms; and X 1 represents an alkali metal atom, an alkaline earth metal atom or an aluminum atom, with provisos that: when X 1 is an alkali metal atom, n is 1 and m is 0; when X 1 is an alkaline earth metal atom, n is 2 and m is 0; and when X 1 is an aluminum atom, n is 1 or 2 and m is (3−n);
at least one benzotriazole-based ultraviolet absorber represented by the following Formula (4):

wherein, R 9 and R 10 each independently represent a hydrogen atom, a chlorine atom or an alkyl group having 1 to 4 carbon atoms; R 11 and R 12 each independently represent a hydrogen atom or an alkyl group having 1 to 18 carbon atoms; and R 13 and R 14 each independently represent a hydrogen atom or an alkyl group having 1 to 4 carbon atoms;
wherein said (B) resin additive having a melting point of not higher than 65° C. comprises at least one hindered amine compound represented by the following Formula (1) and at least one benzoate compound represented by the following Formula (2), and
the content ratio of said hindered amine compound(s) and said benzoate compound(s) is, in terms of mass ratio, in a range of 1:1 to 4:1:

wherein R 1 represents a hydrogen atom, a hydroxy group, an alkyl, hydroxyalkyl, alkoxy or hydroxyalkoxy group having 1 to 30 carbon atoms, or an oxy radical; and R 2 represents an alkyl group having 7 to 31 carbon atoms or an alkenyl group having 2 to 30 carbon atoms;

wherein, R 3 and R 4 each independently represent a hydrogen atom, an alkyl group having 1 to 12 carbon atoms or an arylalkyl group having 7 to 30 carbon atoms; and R 5 represents an alkyl group having 8 to 30 carbon atoms.

2. The resin additive masterbatch according to claim 1 , wherein said (C) inorganic layered compound is talc.

3. A polyolefin resin composition, characterized by comprising the resin additive masterbatch according to claim 1 in a polyolefin resin.

4. The resin additive masterbatch according to claim 1 , wherein the content ratio of said hindered amine compound(s) and said benzoate compound(s) is, in terms of mass ratio, in a range of 7:3 to 4:1.

5. The resin additive masterbatch according to claim 1 , wherein an amount of the at least one aromatic metal phosphate represented by Formula (3) is 0.3 to 5 parts by mass and an amount of the at least one benzotriazole-based ultraviolet absorber represented by the following Formula (4) is 0.5 to 50 parts by mass.

6. The resin additive masterbatch according to claim 1 , wherein an amount of the at least one aromatic metal phosphate represented by Formula (3) is 0.3 to 5 parts by mass and an amount of the at least one benzotriazole-based ultraviolet absorber represented by the following Formula (4) is 0.5 to 25 parts by mass.

7. The resin additive masterbatch according to claim 1 , wherein an amount of the at least one aromatic metal phosphate represented by Formula (3) is 0.3 to 5 parts by mass and an amount of the at least one benzotriazole-based ultraviolet absorber represented by the following Formula (4) is 0.5 to 10 parts by mass.

8. The resin additive masterbatch according to claim 1 , wherein an amount of the (C) at least one inorganic layered compound is 10 to 15 parts by mass, an amount of the at least one aromatic metal phosphate represented by Formula (3) is 1 to 3 parts by mass and an amount of the at least one benzotriazole-based ultraviolet absorber represented by the following Formula (4) is 1 to 10 parts by mass.

9. A resin additive masterbatch, characterized by comprising, with respect to 100 parts by mass of (A) a polyolefin resin:
50 to 200 parts by mass of (B) a resin additive comprising at least one hindered amine and having a melting point of not higher than 65° C.; and
10 to 20 parts by mass of (C) at least one inorganic layered compound selected from talc, mica, kaolin or hydrotalcite;
at least one aromatic metal phosphate represented by the following Formula (3):

wherein R 6 represents a hydrogen atom or an alkyl group having 1 to 8 carbon atoms; R 7 represents an alkyl group having 4 to 8 carbon atoms; R 8 represents an alkylidene group having 1 to 4 carbon atoms; and X 1 represents an alkali metal atom, an alkaline earth metal atom or an aluminum atom, with provisos that: when X 1 is an alkali metal atom, n is 1 and m is 0; when X 1 is an alkaline earth metal atom, n is 2 and m is 0; and when X 1 is an aluminum atom, n is 1 or 2 and m is (3−n);
at least one benzotriazole-based ultraviolet absorber represented by the following Formula (4):

wherein, R 9 and R 10 each independently represent a hydrogen atom, a chlorine atom or an alkyl group having 1 to 4 carbon atoms; R 11 and R 12 each independently represent a hydrogen atom or an alkyl group having 1 to 18 carbon atoms; and R 13 and R 14 each independently represent a hydrogen atom or an alkyl group having 1 to 4 carbon atoms;
wherein said (B) resin additive having a melting point of not higher than 65° C. comprises at least one hindered amine compound represented by the following Formula (1):

wherein R 1 represents a hydrogen atom, a hydroxy group, an alkyl, hydroxyalkyl, alkoxy or hydroxyalkoxy group having 1 to 30 carbon atoms, or an oxy radical; and R 2 represents an alkyl group having 7 to 31 carbon atoms or an alkenyl group having 2 to 30 carbon atoms.

10. The resin additive masterbatch according to claim 9 , wherein an amount of the at least one aromatic metal phosphate represented by Formula (3) is 0.3 to 5 parts by mass and an amount of the at least one benzotriazole-based ultraviolet absorber represented by the following Formula (4) is 0.5 to 50 parts by mass.

11. The resin additive masterbatch according to claim 9 , wherein an amount of the at least one aromatic metal phosphate represented by Formula (3) is 0.3 to 5 parts by mass and an amount of the at least one benzotriazole-based ultraviolet absorber represented by the following Formula (4) is 0.5 to 25 parts by mass.

12. The resin additive masterbatch according to claim 9 , wherein an amount of the at least one aromatic metal phosphate represented by Formula (3) is 0.3 to 5 parts by mass and an amount of the at least one benzotriazole-based ultraviolet absorber represented by the fol

Assignees

• Adeka Corp

Inventors

• Ayabe Takashi
• Yamashita Kenji

Classifications

• C08K5/3435 Primary

  Piperidines · CPC title

• C08J3/226

  using a polymer as a carrier · CPC title

• C08J2423/02

  not modified by chemical after treatment · CPC title

• C08K3/346

  Clay · CPC title

• C08K5/523

  with hydroxyaryl compounds · CPC title