Plasticizers and plasticized polymeric compositions

Patent metadata

Field	Value
Publication number	US-10100172-B2
Application number	US-201314396777-A
Country	US
Kind code	B2
Filing date	May 7, 2013
Priority date	Jun 26, 2012
Publication date	Oct 16, 2018
Grant date	Oct 16, 2018

Abstract

Plasticizers comprising a succinate ester and an epoxidized natural oil and plasticized polymeric compositions comprising such plasticizers. Such plasticized polymeric compositions can be employed in forming various articles of manufacture, such as coated conductors.

First claim

The invention claimed is:

1. A plasticized polymeric vinyl chloride composition consisting of:
(a) a vinyl chloride resin;
(b) a plasticizer consisting of:
(i) from 30 to 50 weight percent of a succinate ester, based on the entire weight of the plasticizer, and
(ii) from 50 to 70 weight percent of an epoxidized natural oil, based on the entire weight of the plasticizer; and

(c) optionally, an additive selected from the group consisting of a metal soap, a lead stabilizer, an epoxide, a salt of monocarboxylic acid, an organic phosphite, a betadiketone, calcium carbonate, clay, silica, antimony trioxide, an antioxidant, and combinations thereof,
wherein said plasticized polymeric vinyl chloride composition has a Shore D hardness of less than 30, as determined by ASTM D2240 when said plasticizer is present in an amount of 52 parts per hundred resin based on 100 parts by weight of the vinyl chloride resin,
wherein said plasticized vinyl chloride polymer composition has a tensile elongation retention of at least 30% when aged at 100° C. for 168 hours, as determined by ASTM D638.

2. The composition of claim 1 , wherein said succinate ester is a dialkyl succinate ester, wherein each alkyl group is independently selected from the group consisting of saturated or unsaturated, branched, straight-chain, or cyclic C 1 to C 13 alkyl groups.

3. The composition of claim 1 , wherein said succinate ester is bis(2-ethylhexyl) succinate.

4. The composition of claim 1 , wherein said plasticizer is present in an amount ranging from 20 to 60 weight percent, based on the entire weight of said plasticized polymeric vinyl chloride composition, wherein said vinyl chloride resin is present in an amount ranging from 40 to 80 weight percent, based on the entire weight of said plasticized polymeric vinyl chloride composition.

5. The composition of claim 1 , wherein said epoxidized natural oil is epoxidized soybean oil.

6. The composition of claim 1 comprising the metal soap, wherein the metal soap is present in an amount ranging from 0.6 to 5 weight percent based on the entire weight of said plasticized polymeric vinyl chloride composition.

7. The composition of claim 6 further comprising the clay.

8. The composition of claim 7 comprising the antimony trioxide.

9. A coated conductor comprising a conductive core and a polymeric layer surrounding at least a portion of said conductive core, wherein said plasticized polymeric vinyl chloride composition of claim 1 constitutes said polymeric layer.

10. The composition of claim 1 , wherein the plasticized vinyl chloride polymer composition has a weight retention of at least 75% when aged at 113° C. for 168 hours when the plasticizer is present in an amount of 52 parts per hundred resin based on 100 parts by weight of the vinyl chloride resin.

11. The composition of claim 1 , wherein the plasticizer consists of:
(i) from 30 to 50 weight percent bis(2-ethylhexyl) succinate, based on the entire weight of the plasticizer, and
(ii) from 50 to 70 weight percent epoxidized soybean oil, based on the entire weight of the plasticizer.

12. The composition of claim 11 , wherein the composition consists of:
(a) from 40 wt % to 80 wt % of the vinyl chloride resin;
(b) from 20 wt % to 60 wt % of the plasticizer; and
(c) from 0.4 wt % to 7 wt % of the metal soap, based on the entire weight of the polymeric composition.

13. The composition of claim 1 wherein the plasticized polymeric vinyl chloride composition has a Shore D hardness from 25 to less than 29, as determined by ASTM D2240 when said plasticizer is present in an amount of 52 parts per hundred resin based on 100 parts by weight of the vinyl chloride resin.

14. The composition of claim 13 comprising the antimony trioxide, the clay, and the antioxidant, and
the plasticized vinyl chloride polymer composition has a tensile elongation retention of at least 70% when aged at 100° C. for 168 hours, as determined by ASTM D638; and a weight retention of at least 80% when aged at 113° C. for 168 hours when the plasticizer is present in an amount of 52 parts per hundred resin based on 100 parts by weight of the vinyl chloride resin.

15. The composition of claim 1 wherein the plasticized polymeric vinyl chloride composition has a Shore A hardness from 82 to less than 95, as determined by ASTM D2240 when said plasticizer is present in an amount of 52 parts per hundred resin based on 100 parts by weight of the vinyl chloride resin.

16. The composition of claim 1 , wherein the plasticized vinyl chloride polymer composition has a tensile strength retention of at least 100% when aged at 113° C. for 168 hours when the plasticizer is present in an amount of 52 parts per hundred resin based on 100 parts by weight of the vinyl chloride resin.

Assignees

• Dow Global Technologies Llc

Inventors

• Chaudhary Bharat I
• Cogen Jeffrey M
• Ries Paul D

Classifications

• C08K5/11

  of acyclic polycarboxylic acids · CPC title

• C08L2203/20

  use in electrical or conductive gadgets · CPC title

• C08K5/1515 Primary

  Three-membered rings · CPC title

• C08K5/0016 Primary

  Plasticisers · CPC title

• Y10T428/2933

  Coated or with bond, impregnation or core · CPC title