Sintered alloy and production method therefor

Patent metadata

Field	Value
Publication number	US-10094009-B2
Application number	US-201514954035-A
Country	US
Kind code	B2
Filing date	Nov 30, 2015
Priority date	Mar 30, 2015
Publication date	Oct 9, 2018
Grant date	Oct 9, 2018

Abstract

A sintered alloy having superior heat resistance and superior wear resistance and also having corrosion resistance against salt damage that may occur in cold-weather regions, and a production method therefor, are provided. The sintered alloy consists of, by mass %, 32.4 to 48.4% of Cr, 2.9 to 10.0% of Mo, 0.9 to 2.9% of Si, 0.3 to 1.8% of P, 0.7 to 3.9% of C, and the balance of Fe and inevitable impurities, and it has a density ratio of not less than 90% and includes carbides that are dispersed in a matrix of a metallic structure thereof.

First claim

What is claimed is:

1. A sintered alloy consisting of, by mass %, 32.4 to 48.4% of Cr, more than 3.0% and not more than 10.0% of Mo, 0.9 to 2.9% of Si, 0.3 to 1.8% of P, 0.7 to 3.9% of C, and the balance of Fe and inevitable impurities, having a density ratio of not less than 90%, and including carbides that are dispersed in a matrix of a metallic structure thereof,
wherein the carbides are dispersed in the metallic structure, except for pores, at 35 to 70% by area ratio.

2. The sintered alloy according to claim 1 , wherein the carbides are dispersed in the metallic structure, except for pores, in a condition in which the carbides are continuously connected so as to surround portions of the matrix, thereby dividing the matrix into a plurality of the portions.

3. The sintered alloy according to claim 1 , wherein Mo is present in an amount of ≥4.7 mass %.

4. A production method for the sintered alloy of claim 1 , the method comprising:
preparing an iron alloy powder consisting of, by mass %, 35.0 to 50.0% of Cr, 3.0 to 10.3% of Mo, 1.0 to 3.0% of Si, 0.5 to 2.5% of C, and the balance of Fe and inevitable impurities, an iron-phosphorous alloy powder including P at 10 to 30 mass %, and a graphite powder; mixing 3.0 to 6.0 mass % of the iron-phosphorous alloy powder and 0.2 to 1.5 mass % of the graphite powder with the iron alloy powder so as to obtain a mixed powder; compacting the mixed powder into a green compact; and sintering the green compact.

Assignees

• Hitachi Chemical Co Ltd

Inventors

• Fukae Daisuke
• Kawata Hideaki

Classifications

• C22C30/00

  Alloys containing less than 50% by weight of each constituent · CPC title

• C22C38/34

  with more than 1.5% by weight of silicon · CPC title

• C22C38/02

  containing silicon · CPC title

• C22C33/0207

  Using a mixture of pre-alloyed powders or a master alloy · CPC title

• C22C1/08

  Alloys with open or closed pores · CPC title