Proppants with improved strength

Patent metadata

Field	Value
Publication number	US-10087365-B2
Application number	US-201615360696-A
Country	US
Kind code	B2
Filing date	Nov 23, 2016
Priority date	Oct 30, 2013
Publication date	Oct 2, 2018
Grant date	Oct 2, 2018

Abstract

Cements, such as alkali activated binder, may be used as coatings on proppants, such as sand, to improve the strength thereof. The resulting chemically bonded phosphate ceramic (CBPC) coated proppants show increased compressive strength between about 60 to about 130 MPa, as well as produced fines of lower than about 10 wt % at 10,000 psi closure stress.

First claim

What is claimed is:

1. A method of preparing a strengthened proppant comprising:
mixing together (a) a compound selected from the group consisting of an alkali metal phosphate, phosphoric acid, ammonium phosphate, ammonium dihydrogen phosphate, and combinations thereof, and (b) a binder selected from the group consisting of an alkaline earth metal hydroxide, an alkaline earth metal oxide, a metal oxide, a metal hydroxide, an alumino silicate, and combinations thereof in water to form an aqueous solution;
at least partially coating a plurality of proppant cores with the aqueous solution; and
exposing the aqueous solution-coated proppant cores to a temperature to polymerize the (a) compound selected from the group consisting of an alkali metal phosphate, a phosphoric acid, ammonium phosphate, ammonium dihydrogen phosphate, and combinations thereof and (b) binder selected from the group consisting of a metal oxide, a metal hydroxide, an alkaline earth metal hydroxide, an alkaline earth metal oxide, an aluminosilicate, and combinations thereof to form a coating where the coating is selected from the group consisting of magnesium phosphate, calcium phosphate, aluminum phosphate, zirconium aluminum phosphate, zirconium phosphate, zirconium phosphonate, magnesium potassium phosphate, potassium aluminum phosphate, alkali metal transition metal phosphates, carbide materials, tungsten carbide, cements, polymer cements, polyamide-imides, polyether ether ketones (PEEK), and combinations thereof, to give the strengthened proppant having a compressive strength ranging from about 34 to about 130 MPa.

2. The method of claim 1 where (a) the compound is alkali metal phosphate or phosphoric acid, or ammonium phosphate or ammonium dihydrogen phosphate and where the aqueous solution has a mole ratio of (a) compound/(b) binder ranging from about 0.1:1 to about 30:1.

3. The method of claim 1 where the (b) binder is selected from the group consisting of a metal oxide, a metal hydroxide, and combinations thereof, and the (a) compound is selected from the group consisting of alkali metal phosphate or phosphoric acid and mixtures thereof, and where the mole ratio of (b) binder to (a) compound in the aqueous solution ranges from about 0.1:1 to about 6:1.

4. The method of claim 1 where the aqueous solution further comprises fillers selected from the group consisting of silica sand, fly ash, sludges, slags, waste paper, rice husks, saw dust, volcanic aggregates, expanded perlite, pumice, scoria, obsidian, minerals, diatomaceous earth, mica, borosilicates, clays, metal oxides, metal fluorides, plant and animal remains, sea shells, coral, hemp fibers, manufactured fillers, silica, mineral fibers, mineral mats, chopped fiberglass, woven fiberglass, metal wools, turnings, shavings, wollastonite, nanoclays, carbon nanotubes, carbon fibers and nanofibers, graphene oxide, graphite, and combinations thereof.

5. The method of claim 1 where the proppant cores are heated prior to the coating with the aqueous solution.

6. The method of claim 5 where the proppant cores are heated to between about 0 and about 300° C.

7. The method of claim 1 where the proppant cores are selected from the group consisting of sand, ceramic beads, glass beads, bauxite grains, sintered bauxite, sized calcium carbonate, walnut shell fragments, aluminum pellets, silica, nylon pellets, nuts shells, gravel, resinous particles, alumina, minerals, polymeric particles, and combinations thereof.

8. The method of claim 1 where
the (a) compound is an alkali metal phosphate, and the (b) binder is selected from the group consisting of an alkaline earth metal hydroxide, an alkaline earth metal oxide, and combinations thereof, the alkali metal is selected from the group consisting of sodium, potassium and mixtures thereof and the alkaline earth metal is selected from the group consisting of calcium, magnesium and mixtures thereof, and
the coating is selected from the group consisting of magnesium phosphate, aluminum phosphate, zirconium aluminum phosphate, zirconium phosphate, zirconium phosphonate, magnesium potassium phosphate, and combinations thereof.

9. The method of claim 1 where the strengthened proppant has
a density ranging from about 2 to about 2.63 g/cm 3 .

10. A method of preparing a strengthened proppant comprising:
mixing together (a) a compound selected from the group consisting of an alkali metal phosphate, phosphoric acid, ammonium phosphate, ammonium di-hydrogen phosphate, and combinations thereof, and (b) a binder selected from the group consisting of an alkaline earth metal hydroxide, an alkaline earth metal oxide, a metal oxide, a metal hydroxide, an aluminosilicate, and combinations thereof, in water to form an aqueous solution, and where the aqueous solution has a mole ratio of (a) compound/(b) binder ranging from about 0.1:1 to about 30:1;
at least partially coating a plurality of proppant cores with the aqueous solution, where the proppant cores are selected from the group consisting of sand, ceramic beads, glass beads, bauxite grains, sintered bauxite, sized calcium carbonate, walnut shell fragments, aluminum pellets, silica, nylon pellets, nuts shells, gravel, resinous particles, alumina, minerals, polymeric particles, and combinations thereof; and
exposing the aqueous solution-coated proppant cores to a temperature to polymerize the (a) compound selected from the group consisting of an alkali metal phosphate, a phosphoric acid, ammonium phosphate, ammonium dihydrogen phosphate, and combinations thereof and (b) binder selected from the group consisting of an alkaline earth metal hydroxide, an alkaline earth metal oxide, a metal oxide, a metal hydroxide, an aluminosilicate in water, and combinations thereof to form a coating where the coating is selected from the group consisting of magnesium phosphate, calcium phosphate, aluminum phosphate, zirconium aluminum phosphate, zirconium phosphate, zirconium phosphonate, magnesium potassium phosphate, potassium aluminum phosphate, alkali metal transition metal phosphates, carbide materials, tungsten carbide, cements, polymer cements, polyamide-imides, polyether ether ketones (PEEK), and combinations thereof, to give the strengthened proppant having a compressive strength ranging from about 34 to about 130 MPa.

11. The method of claim 10 where the aqueous solution further comprises fillers selected from the group consisting of silica sand, fly ash, sludges, slags, waste paper, rice husks, saw dust, volcanic aggregates, expanded perlite, pumice, scoria, obsidian, minerals, diatomaceous earth, mica, borosilicates, clays, metal oxides, metal fluorides, plant and animal remains, sea shells, coral, hemp fibers, manufactured fillers, silica, mineral fibers, mineral mats, chopped fiberglass, woven fiberglass, metal wools, turnings, shavings, wollastonite, nanoclays, carbon nanotubes, carbon fibers and nanofibers, graphene oxide, graphite, and combinations thereof.

12. The method of claim 10 where the proppant cores are heated prior to the coating with the aqueous solution.

13. The method of claim 12 where the proppant cores are heated to between about 0 and about 300° C.

14. The method of claim 10 where
in the (a) compound is selected from the group consisting of an alkali metal phosphate, phosphoric acid, ammonium phosphate, ammonium dihydrogen phosphate, and combinations thereof, and the (b) binder is an alkaline earth metal hydroxide, an alkaline earth metal oxide, and combinations thereof, the alkali metal is selected from the group consisting of sodium, potassium and mixtures thereof and the alkaline earth metal is selected from the group consis

Assignees

• Baker Hughes Inc
• Baker Hughes A Ge Co Llc

Inventors

• Bestaoui-Spurr Naima
• Qu Qi
• Stephenson Christopher J

Classifications

• B05D3/0254

  After-treatment · CPC title

• C09K2208/08

  Fiber-containing well treatment fluids · CPC title

• B05D3/0218

  Pretreatment, e.g. heating the substrate · CPC title

• C09K8/805 Primary

  Coated proppants · CPC title

• C09K8/62

  Compositions for forming crevices or fractures · CPC title