Titanium dioxide pigment and method for manufacturing same, and composition in which same is blended

Patent metadata

Field	Value
Publication number	US-10087329-B2
Application number	US-201515319307-A
Country	US
Kind code	B2
Filing date	Jun 12, 2015
Priority date	Jun 17, 2014
Publication date	Oct 2, 2018
Grant date	Oct 2, 2018

Abstract

Provided is a titanium dioxide pigment having minimal yellow color and minimal yellowing due to exposure, i.e., good yellowing resistance and high pigment performance such as brightness. Also provided is a titanium dioxide pigment which has a reduced amount of volatile moisture and which does not readily decompose when blended with a resin or the like. In the present invention, a compound including 0.05-20% by mass of phosphorus and an alkaline earth metal is present on surfaces of titanium dioxide particles having an average particle diameter of 0.15-1.0 μm. The titanium dioxide pigment is manufactured by mixing an alkaline earth metal compound, a phosphate compound, and titanium dioxide particles having an average particle diameter of 0.15-1.0 μm, and bonding the compound including phosphorus and an alkaline earth metal to the titanium dioxide particles.

First claim

The invention claimed is:

1. A titanium dioxide pigment comprising titanium dioxide particles having an average particle diameter of 0.15 to 1.0 μm, wherein 0.05 to 20 mass % of a compound including phosphorus and calcium is present on surfaces of the titanium dioxide particles, wherein a value of (a BET diameter of the titanium dioxide pigment)/(a median diameter of the titanium dioxide pigment) is 0.04 or more.

2. The titanium dioxide pigment according to claim 1 wherein a value of (a difference (ppm) between a Karl Fischer moisture of the titanium dioxide pigment at 300° C. and a Karl Fischer moisture of the titanium dioxide pigment at 100° C.)/(a total amount (mass %) of an inorganic compound(s) present on a surface of the titanium dioxide pigment, the amount being used to treat the surface) is 3500 or less.

3. The titanium dioxide pigment according to claim 1 , wherein a color difference Δb of a difference between a b-value of a powder color in a Hunter color system of the titanium dioxide pigment in which the compound including phosphorus and calcium is present and a b-value of a powder color in the color system of the titanium dioxide pigment before the compound including phosphorus and calcium is present is −0.1 or less.

4. The titanium dioxide pigment according to claim 1 , wherein a compound including at least one element selected from the group consisting of silicon, aluminum, titanium, tin, zirconium, and antimony and the compound including phosphorus and calcium are present on the surfaces of the titanium dioxide particles.

5. The titanium dioxide pigment according to claim 4 , wherein the compound including at least one element selected from the group consisting of silicon, aluminum, titanium, tin, zirconium and antimony is present on the surfaces of the titanium dioxide particles, and the compound including phosphorus and calcium is present on an outside thereof.

6. The titanium dioxide pigment according to claim 4 , wherein the compound including phosphorus and calcium is present on the surfaces of the titanium dioxide particles, and the compound including at least one element selected from the group consisting of silicon, aluminum, titanium, tin, zirconium and antimony is present on an outside thereof.

7. The titanium dioxide pigment according to claim 4 , wherein the compound including at least one element selected from the group consisting of silicon, aluminum, titanium, tin, zirconium and antimony is at least one selected from the group consisting of an oxide thereof, a hydroxide thereof, and a hydrous oxide thereof.

8. The titanium dioxide pigment according to claim 1 , further comprising an organic compound, wherein the organic compound is attached to a surface of the titanium dioxide pigment.

9. The titanium dioxide pigment according to claim 8 , wherein the organic compound is at least one organic compound selected from the group consisting of organosilicon compounds and polyols.

10. A method for manufacturing a titanium dioxide pigment according to claim 1 comprising:
mixing titanium dioxide particles having an average particle diameter of 0.15 to 1.0 μm, a phosphoric acid compound, and a calcium compound; and
attaching a compound including the phosphorus and the calcium to the titanium dioxide particles.

11. The method according to claim 10 , comprising:
preparing an aqueous slurry including the titanium dioxide particles having an average particle diameter of 0.15 to 1.0 μm, the phosphoric acid compound, and the calcium compound; and
adjusting a pH of the aqueous slurry, thereby attaching the compound including the phosphorus and the calcium to the titanium dioxide particles.

12. A method for manufacturing the titanium dioxide pigment according to claim 1 comprising attaching a compound including phosphorus and calcium and a compound including at least one element selected from the group consisting of silicon, aluminum, titanium, tin, zirconium, and antimony to titanium dioxide particles having an average particle diameter of 0.15 to 1.0 μm.

13. The according to claim 12 , comprising:
mixing the titanium dioxide particles and the compound including at least one element selected from the group consisting of silicon, aluminum, titanium, tin, zirconium and antimony, thereby attaching the compound including the at least one element to the titanium dioxide particles; and
subsequently mixing a phosphoric acid compound and a calcium compound, thereby attaching the compound including phosphorus and calcium to the titanium dioxide particles.

14. The method according to claim 12 , comprising:
mixing the titanium dioxide particles, a phosphoric acid compound, and a calcium compound, thereby attaching the compound including phosphorus and calcium are attached to the titanium dioxide particles; and
subsequently mixing the titanium dioxide particles and the compound including at least one element selected from the group consisting of silicon, aluminum, titanium, tin, zirconium and antimony, thereby attaching the compound including the at least one element to the titanium dioxide particles.

15. The according to claim 12 , wherein the compound including at least one element selected from the group consisting of silicon, aluminum, titanium, tin, zirconium and antimony is attached to the titanium dioxide particles and is at least one selected from the group consisting of an oxide thereof, a hydroxide thereof, and a hydrous oxide thereof.

16. A method for manufacturing a titanium dioxide pigment comprising further firing the titanium dioxide pigment manufactured by the method according to claim 10 .

17. A method for manufacturing a titanium dioxide pigment comprising further attaching an organic compound to the titanium dioxide pigment manufactured by the method according to claim 10 .

18. The method according to claim 17 , wherein the organic compound is at least one organic compound selected from the group consisting of organosilicon compounds and polyols.

19. A composition comprising the titanium dioxide pigment according to claim 1 .

20. A method for manufacturing a titanium dioxide pigment comprising further firing the titanium dioxide pigment manufactured by the method according to claim 12 .

21. A method for manufacturing a titanium dioxide pigment comprising further attaching an organic compound to the titanium dioxide pigment manufactured by the method according to claim 12 .

22. The method for manufacturing a titanium dioxide pigment according to claim 21 , wherein the organic compound is at least one organic compound selected from the group consisting of organosilicon compounds and polyols.

Assignees

• Ishihara Sangyo Kaisha
• Ishihara Sangyo Kaisha

Inventors

• Isobe Kaoru
• Sanefuji Norihiko
• Tanida Yasutsune
• OHSAKI Kensuke

Classifications

• C09C1/3661 Primary

  Coating · CPC title

• C09C1/3623

  Grinding · CPC title

• C09C1/3607 Primary

  Titanium dioxide · CPC title

• C01P2006/82

  water content · CPC title

• C01P2006/64

  b* (yellow-blue axis) · CPC title